Cu10sn + ZrO2 + CNT hibrit nanokompozitlerin toz metalurjisi yöntemiyle üretimi ve mikroyapı - mekanik özelliklerinin araştırılması
Fabrication of Cu10sn + ZrO2 + CNT hybrid nanocomposites by powder metallurgy and investigation of microstructural and mechanical properties
- Tez No: 847186
- Danışmanlar: DR. ÖĞR. ÜYESİ HAKAN ADA
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Kastamonu Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 107
Özet
Saf malzemelerle karşılaştırıldığında mükemmel mekanik ve elektriksel özellikleri nedeniyle, son zamanlarda nanokompozit malzemeler araştırmacıların dikkatini çekmiştir. Bronz malzemeler iyi elektriksel ve termal iletkenliklere sahiptir. Bununla birlikte, düşük mukavemet, sertlik ve aşınma direnci nedeniyle endüstriyel uygulamalarda zaman zaman problemler yaşanmaktadır. Bu sorunu çözmek için bilim adamları, yüksek mukavemet ve sertlik ve aşınma direncine sahip bronz esaslı kompozit üretmeyi başarmıştır. Bu çalışmada, bronz matrisli hibrit nanokompozitler toz metalurjisi metodu ile üretilmiştir. Çalışmada matris malzemesi olarak ön alaşımlı Cu10Sn tozları ile takviye malzemeleri olarak karbon nanotüp (CNT) ve Zirkonya (ZrO2) kullanılmıştır. Üretilen hibrit nanokompozitlerin mikroyapısal – mekanik özellikleri araştırılmıştır. Çalışma sonucunda sertlik ve aşınma davranışı özelinde takviye oranlarına göre Zirkonya takviyesinin olumlu etkileri olduğu tespit edilirken, CNT takviyesinin olumsuz etkileri olduğu görülmüş, hibrit kompozitlerde ise her iki takviye özelliklerinin ortalaması mekanik özellikler gözlemlenmiştir
Özet (Çeviri)
Due to their excellent mechanical and electrical properties compared to pure materials, nanocomposite materials have recently attracted the attention of researchers. Bronze materials have good electrical and thermal conductivities. However, due to their low strength, hardness and wear resistance, industrial applications sometimes have problems. To solve this problem, scientists have succeeded in producing bronze-based composites with high strength, hardness and wear resistance. In this study, bronze matrix hybrid nanocomposites were produced by the powder metallurgy method. Pre-alloyed Cu10Sn powders were used as matrix material and carbon nanotubes (CNT) and Zirconia (ZrO2) were used as reinforcement materials. The microstructural and mechanical properties of the hybrid nanocomposites were investigated. As a result of the study, it was found that Zirconia reinforcement had positive effects on hardness and wear behaviour according to reinforcement ratios, while CNT reinforcement had negative effects, and hybrid composites exhibited properties that were the average of both reinforcement properties.
Benzer Tezler
- Toz metalurjisi yöntemi ile üretilen Cu10Sn/B4C kompozitlerin difüzyon kaynağı ile birleştirilebilirliğinin araştırılması
Investigation of the combinability of Cu10Sn/B4C composites produced by powder metallurgy method with diffusion welding
SERKAN ÖZSOY
Yüksek Lisans
Türkçe
2023
Makine MühendisliğiKastamonu ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ HAKAN ADA
- T/M yöntemiyle üretilen karbür katkılı cu alaşımlarının aşınma dayanımlarının incelenmesi
Investigation of wear resistance of carbide added cu alloys produced by P/M method
MEVLAN YÜREK
Yüksek Lisans
Türkçe
2022
Makine MühendisliğiBitlis Eren ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. SERKAN ÖZEL