Manufacturing duplex steel by using induction furnaces and characterization
Dubleks çeliklerin indüksiyon ocağı ile üretilmesi ve karakterizasyonu
- Tez No: 851238
- Danışmanlar: PROF. DR. GÜL YILMAZ ATAY
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Dubleks çelik, indüksiyon ocakları, ısıl işlem, Elektromanyetik indüksiyon, Çift fazlı çelik, Duplex steel, induction furnaces, heat treatment, Electromagnetic induction, Dual phase steel
- Yıl: 2024
- Dil: İngilizce
- Üniversite: İzmir Katip Çelebi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Dubleks çelikleri yapısında ferrit ve östenit fazları bulunduran, korozyona karşı yüksek dayanıma sahip, ve bunun yanında gelişmiş mekanik değerler gösteren malzemelerdir. Yapısındaki östenit genel korozyon dayanımı ve süneklik sağlarken, ferrit sayesinde ise gerilmeli korozyon çatlağına karşı dayanım ve mekanik dayanım elde edilmektedir. Dubleks çelikleri gemicilik ve petrokimya başta olmak üzere yaygın bir kullanımına sahiptir. Geniş kullanım alanı ile talep gören dubleks çeliklerinin mevcut üretim yöntemi genellikle argon oksijen dekarbürizasyon ocaklarıdır (AOD). Kimyasal komposizyonunda kritik değerlere sahip elementler barındıran dupleks çeliklerinin üretim yönteminin yanı sıra ısıl işlem prosesi de önemli bir yer tutar. Yapısında bulunan ferrit ve östenit fazlarının %50 değerlerinde olması bekleni ki bu şekilde korozyon direnci ve süneklik sağlanırken istenen mekanik dayanım da elde edilebilmektedir. Bu çalışmada mevcut üretim yöntemi argon oksijen dekarbürizasyonu ocakları olan dubleks çeliklerinin indüksiyon ocakları ile üretiminin gerçekleşmesi sağlanmıştır. Buna bağlı olarak yeni pazar sağlanması, mevcut maliyetlerin azaltılması ve karbon emisyonunun düşürülmesi hedeflenmiştir. Dubleks çeliklerinin üretiminin indüksiyon ocağında yapılmasının ardından üretimi yapılan parçalara ısıl işlem uygulanmıştır. Elde edilen parçalar yapısal ve morfolojik olarak incelenmiş, yapıda ferrit ve östenit fazları %50 oranlarında tespit edilmiştir. Ayrıca indüksiyon ocağında üretilen dubleks çeliklerinin mekanik özellikleri değerlendirilmiştir.
Özet (Çeviri)
Duplex steels are materials that contain ferrite and austenite phases in their structure, have high resistance to corrosion, and also show improved mechanical values. While the austenite in its structure provides general corrosion resistance and ductility, ferrite provides resistance to stress corrosion cracking and mechanical strength. Duplex steels have widespread use, especially in shipping and petrochemistry. The current production method of duplex steels, which are in demand with a wide usage area, is generally argon oxygen decarburization furnaces (AOD). In addition to the production method of duplex steels, which contain elements with critical values in their chemical composition, the heat treatment process also has an important place. The ferrite and austenite phases in its structure are expected to be at 50% values, so that the desired mechanical strength can be achieved while providing corrosion resistance and ductility. In this study, the production of duplex steels, whose current production method is argon oxygen decarburization furnaces, was achieved using induction furnaces. Accordingly, it is aimed to provide new markets, reduce existing costs and reduce carbon emissions. After the duplex steels were produced in the induction furnace, heat treatment was applied to the produced parts. The obtained parts were examined structurally and morphologically, and ferrite and austenite phases were detected at a rate of 50% in the structure. Additionally, the mechanical properties of duplex steels produced in the induction furnace were evaluated.
Benzer Tezler
- A study on the wire arc additive manufacturing of duplex stainless steel plates: Optimization of process parameters and investigation of mechanical properties
Tel ark eklemeli imalat yöntemiyle dubleks paslanmaz çelik plaka üretiminde proses parametrelerinin optimizasyonu ve plaka mekanik özelliklerinin incelenmesi
HASSAN A.H. SAADAWI
Doktora
İngilizce
2022
Mühendislik BilimleriAtılım ÜniversitesiMühendislik Sistemlerinin Modellenmesi ve Tasarımı Ana Bilim Dalı
DOÇ. DR. ERKAN KONCA
DR. ÖĞR. ÜYESİ KAZIM TUR
- Dubleks paslanmaz çelik (1.4462) malzemenin farklı iletim hızlarında erozif aşınma davranışı üzerine bir çalışma
A study on the erosive wear behavior of duplex stainless steel (1.4462) at different transmission rates
MEHMET ALİ KAHRAMAN
Yüksek Lisans
Türkçe
2023
Makine MühendisliğiKarabük ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. RECEP DEMİRSÖZ
- Gaz tungsten ark kaynak yöntemiyle S235JR ve SAF2205 çeliklerin benzer kaynaklarında akımın ve benzer olmayan kaynaklarında farklı ilave tellerin içyapı ve mekanik davranışa etkilerinin incelenmesi
Investigation of the effects of current in similar welds and different filler metals in dissimilar welds of S235JR and SAF2205 steels on microstructure and mechanical behavior using the gas tungsten arc welding method
ÇAĞATAY SÜMBÜLTEPE
Yüksek Lisans
Türkçe
2025
Makine Mühendisliğiİskenderun Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. GÜREL ÇAM
PROF. DR. AHMET ÇAKAN
DR. ÖĞR. ÜYESİ MEHMET DEMİR
- TIG kaynak yöntemi ile bırleştirilen AISI316 kalite paslanmaz çeliğin dayanımı üzerine bir çalışma
A study on the strength of AISI316 quality stainless steel combined with TIG welding method
AYBERK ERDEM
Yüksek Lisans
Türkçe
2023
Makine MühendisliğiKarabük ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. RECEP DEMİRSÖZ
- Ostenitik paslanmaz çeliklerin örtülü elektrodla ark kaynağında parametrelerin bilgisayarla tespiti
Başlık çevirisi yok
H. KUBİLAY KIYICI