Çeşitli nano malzeme ile güçlendirilmiş odun esaslı levhaların karakteristik özelliklerinin belirlenmesi

Determination of characteristic properties of wood- based boards reinforced with various nano material

PDF İndir

  1. Tez No: 858157
  2. Yazar: KADİR DOĞAN
  3. Danışmanlar: DOÇ. DR. ALPEREN KAYMAKCI
  4. Tez Türü: Doktora
  5. Konular: Ağaç İşleri, Wood Products
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2024
  8. Dil: Türkçe
  9. Üniversite: Kastamonu Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Orman Endüstri Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 236

Özet

Bu tez çalışmasında; toz formunda 18-50 nm tane boyutlarında olan, Magnezyum oksit (MgO), Çinko oksit (ZnO) ve Silisyum dioksit (SiO2) nano katkı malzemeleri %1, %3 ve %5 olarak üç farklı oranda, Üre formaldehit (UF) ve Melamin üre formaldehit (MUF) tutkalları içerisine katılmıştır. Nano katkı maddelerinin, yapı malzemesi olarak kullanılan yönlendirilmiş yongalevha (OSB)'nin fiziksel özelliklerinden olan; 24 saat suda kalınlık şişmesi, formaldehit ve rutubet içeriği, boyutsal değişim, yanma direnci, esmer çürüklük mantarına karşı dayanım, ısı geçirgenliği, termogravimetrik analiz (TGA) ısı özellikleri incelenmiştir. Aynı zamanda nano katkı malzemesinin levha içerisinde şerit yongalar üzerinde dağılım özellikleri SEM mikroskopu ile araştırılmıştır. Mekanik direnç değerlerinden; çekme, eğilme, eğilmede elastikiyet modülü ve çekme-makaslama değerleri incelenmiştir. Çalışmada, OSB üretimi için Karaçam (Pinus nigra A.) ve Kızılçam (Pinus burutia T.) odunu yongaları (flake) karışık olarak, Kronospan orman ürünlerinden temin edilmiştir. Levhaların üretiminde kullanılan tutkallar; %60'lik üre formaldehit (UF) tutkalı, %60'lık, melamin içeriği %5 olan melamin üre formaldehit (MUF) tutkalı Kronospan Orman Ürünleri firması tutkal fabrikasından temin edilmiştir. Her bir tutkal çeşidi için tutkal; katı tutkal miktarı kuru yonganın %11 olarak verilmiştir. Formaldehit emisyon değerini azaltmak için kullanılan %50 konsantrasyonlu catcher kimyasalı Kronospan orman ürünleri tutkal fabrikasından temin edilmiştir. Catcher katı miktarı, katı tutkal miktarına oranı %5 olacak şekilde tutkal içerisine ilave edilmiştir. Sertleştirici olarak %20 sulu çözeltili amonyum klorür Kronospan orman ürünlerinden temin edilmiş ve tutkal içerisine, katı sertleştirici miktarı, katı tutkal miktarı oranı %2 olacak şekilde katılmıştır. Su itici özelliğinde olan %50 konsantrasyonda parafin emülsiyonu Mercan parafin firmasından sağlanmıştır. Parafin emülsiyonu, sıvı olarak tutkal içerisine tüketim oranı katı parafin miktarı kuru yongaya oranla %1 olacak şekilde karıştırılmıştır. Üretilen nano katkısız ve nano katkılı numuneler üzerine ilgili standartlarda belirtilen ebatlara uygun olarak deney numuneleri hazırlanmış ve deneyleri gerçekleştirilmiştir. Çalışma sonucunda elde edilen veriler SAS 9,4 istatistik programı yardımıyla analiz edilmiş ve sonuçlar yorumlanmıştır. Çalışma sonucunda; UF ve MUF tutkalına katılan nano katkı maddelerinin herbiri için numune yoğunluk ortalama değerleri hedeflenen yoğunluk ve tolerans değerleri arasındadır. UF tutkalı ve MUF tutkalı içerisine katılan MgO nano katkı malzemesi oranı arttıkça eğilme, elastikiyet ve çekme mukavemet değerinde düşüş, fiziksel özelliklerden 24 saat suda şişme ve formaldehit değerinde artış tespit edilmiştir. Mekanik değerlerdeki düşüş, kalınlık şişme ve formaldehit değerlerindeki artışın UF tutkalında MUF tutkalına göre belirgin olarak daha fazla olduğu görülmüştür. MUF tutkalı ile üretilen nano katkısız kontrol numunelerinde ve nano katkılı numunelerde formaldehit emisyon değeri düşüş göstermiştir. Formaldehit değerindeki düşüşün melamin içeriğinin etkisinden olduğu düşünülmektedir. Mukavemet deneyleri sonuçlarına göre; ZnO ve SiO2 nano katkı maddelerinin mukavemetlere olumlu etki ettiği görülmektedir. Fiziksel özelliklerden yanma deneyleri incelendiğinde ZnO nano katkı maddesinin yanma süresi üzerine olumlu etki ettiği, yapı mazemesi olarak numunenin ısı yalıtım özelliği bakımından önemli olan ısı geçirgenlik deneyi sonucuna göre SiO2 katkı oranı arttıkça ısı iletkenlik değerinin azaldığı görülmektedir. Numunelerin boyutsal genişleme deneylerinde boy ve ende genişleme, daralma ve kalınlık artışları incelenmiştir. Deney sonuçları, numunenin üst ve alt yüzey şerit yongalarının üretim yönüne doğru ve üretime dik olarak kesiliş yönüne doğru olarak yorumlanmıştır. Analiz sonuçlarına göre; %30 nem 20°C sıcaklıktan %65 nem 20°C sıcaklık şartlarına geçişlerde üretim yönüne dik yönde boyutsal değişimlerde boy, en ve kalınlık artışlarında önemli bir fark görülmemiştir. %65 nem 20°C sıcaklıktan %85 nem 20°C sıcaklık şartlarına geçişlerde üretim yönüne doğru değişimlerde önemli bir fark yok iken üretim dik yönde boyutsal değişimlerde numune eninde meydana gelen değişimin daha az olduğu ve numune eninde en az genişleme UF tutkalı SiO2 %3 katkı oranında ve MUF tutkalı nano katkısız numunelerde olduğu görülmektedir. Numunelerin boyutsal daralma deneylerinde boy ve ende daralma ve kalınlıklarda azalış incelenmiştir. Deney sonuçları numunenin üst ve alt yüzey şerit yongalarının üretim yönüne doğru ve üretime dik olarak kesiliş yönüne göre yorumlanmıştır. Analiz sonuçlarına göre; %85 nem 20°C sıcaklıktan %65 nem 20°C sıcaklık şartlarına gelindiğinde şerit yonga serilme yönleri üretim yönüne dik olarak kesilen numunelerin enlerinde daralma oranının daha az olduğu ve bunun UF tutkalı SiO2 %1, MUF tutkalı nano katkısız numuneler ve MgO %5 katkı oranınlı numunelerde olduğu görülmektedir. %65 nem 20°C sıcaklıktan %30 nem 20°C sıcaklık şartlarına gelindiğinde ise üretim yönüne ve üretime dik olarak kesilen numunelerin boy, en ve kalınlıkta azalma oranlarında önemli bir farkılılığın olmadığı görülmektedir. Isı geçirgenlik özelliğinin belirlendiği deney sonuçlarına göre; en düşük ısı iletkenliği değerinin MUF tutkalı SiO2 nano katkısı %5 oranında olduğu görülmektedir. Isı geçirgenlik süresinin az olduğu grupların ise UF tutkalı nano katkısız numunelerinde, MUF tutkalı SiO2 nano katkılı %1,%3 oranında ve MUF tutkalı MgO nano katkısı %5 oranında olduğu görülmektedir. Termal ısı özelliklerin belirlendiği TGA testi analiz sonuçlarına göre; her iki tutukal grubu arasında nano katkısız numunelerde ve nano katkılı numunler arasında önemli bir fark bulunmamıştır. Yangın tepki deneylerinde nano katkı maddelerinin OSB'nin yanma özelliklerine olumsuz bir etkisinin olmadığı görülmüştür. Yangın tepki deneylerinde alev yüksekliğinin her grup ve nano katkı maddeleri için standartın belirlediği sınır değeri geçmediği gözlemlenmiştir.

Özet (Çeviri)

In this thesis study, Magnezium oxide (MgO), Zinc oxide (ZnO) and Silisium dioxide (SiO2) nano additive materials in powder form with grain size of 18-50 nm were added to urea formaldehyde (UF) and melamine urea formaldehyde (MUF) resins in three different ratios as 1%, 3% and 5%. Pysical properties of oriented strand board (OSB) used as a building; thickness swelling in water 24h, formaldehyde and moisture content, dimensional change, fire resistance, resistance to brown rot fungus, heat permeability, thermogravimetric analysis (TGA) thermal properties were examined. At the same time, the distribution properties of the nano additive material on the strand partickle in the board were investigated using an SEM microscope. From mechanical resistance values; tensile strength, bending strength, modulus of elasticity in bending and tensile-shear strength were examined. In the study, mixed Black pine (Pinus nigra A.) and Red pine (Pinus burutia T.) wood strand partickle were obtained from Kronospan wood products for OSB production. Resins were used in the production of board; 60% urea formaldehyde (UF) resin and 60% melamine urea formaldehyde (MUF) resin with 5% melamine content were supplied from the Kronospan Wood Products company resin factory. Resin for each type of resin was added as solid 11% of the dry strand partickle. The 50% concentration catcher chemical used to reduce formaldehyde emission value was supplied from Kronospan Wood Products resin factory. Catcher solid amount was added into the resin at a ratio of 5% to the solid glue amount. Ammonium chloride in 20% aqueous solution as a hardener was obtained from Kronospan Wood Products and was added into the resin in a way that the ratio of solid hardener amount to solid glue amount was 2%. Paraffin emulsion at 50% concentration, which has water-repellent properties, was provided by Mercan paraffin firm. Paraffin emulsion was mixed into the liquid glue in such a way that the consumption rate of solid paraffin was 1% compared to dry chip. Test samples were prepared and tested in accordance with the dimensions specified in the relevant standards on the produced nano-free and nano-added samples. The data obtained as a result of the study were analyzed with the help of SAS 9,4 statistical program and the results were interpreted. In the results of study; the sample density average values for each of the nano additives added to UF and MUF resin are between the intended density value and tolerance values. As the ratio of MgO nano additive material added to UF resin and MUF resin increased, a decrease in bending, elasticity and tensile strength values, and an increase in 24-hour water swelling and formaldehyde values were detected. It was observed that the decrease in mechanical values, thickness swelling and increase in formaldehyde values were significantly higher in UF resin than in MUF resin. The formaldehyde emission value decreased in control samples without nano additives and in samples with nano additives produced with MUF resin. It is thought that the decrease in formaldehyde value is due to the effect of melamine content. According to the results of strength tests; It is seen that ZnO and SiO2 nano additives have a positive effect on strength. When the combustion experiments from physical properties are examined, it is seen that the ZnO nano additive has a positive effect on the burning time feature and as a result of the heat permeability test, which is important for the thermal insulation feature of the sample as a building material, as the SiO contribution rate increases, the thermal conductivity value decreases, meaning it can increase the insulation performance of the material. In dimensional expansion experiments, elongation, expansion and thickness increases in length, width and thickness were examined. The test results were interpreted as towards the production direction of the upper and lower surface flakes of the sample and towards the cutting direction perpendicular to the production. According to the analysis results; No significant difference was observed in the dimensional changes perpendicular to the production direction in the increases in length, width and thickness in the transition from 30% humidity and 20°C to 65% humidity and 20°C temperature conditions. While there is no significant difference in the changes towards the production direction in the transition from 65% humidity, 20°c temperature to 85% humidity, 20°c temperature conditions, in the dimensional changes in the perpendicular direction of production, the change in the sample width is less and the least expansion in the sample width is observed. UF resin SiO2 3% contribution ratio and in samples without nano additives of MUF glue. In dimensional contraction experiments, shrinkage in length and width measurements and decrease in thickness were examined. The test results were again interpreted as towards the production direction of the upper and lower surface flakes of the sample and towards the cutting direction perpendicular to the production. According to the analysis results; When it comes to 85% humidity, 20°C temperature and 65% humidity, 20°C temperature conditions, it is seen that the shrinkage rate in the width of the samples whose flake laying directions are cut perpendicular to the production direction is less. seen in the samples. When it comes to 65% humidity and 20°C temperature conditions and 30% humidity and 20°C temperature conditions, it is seen that there is no significant difference in the reduction rates in length, width and thickness of the samples cut perpendicular to the production direction and production. According to the test results in which the heat permeability property was determined; It is seen that the lowest thermal conductivity value is 5% with the SiO2 nano contribution of MUF resin. It is seen that the groups with the lowest heat permeability time are in the samples without UF resin nano additives, MUF glue with SiO2 nano additives at a rate of 1% and 3%, and MUF resin MgO nano additive at a rate of 5%. According to the TGA test analysis results where thermal heat properties are determined; There was no significant difference between the two adhesive groups in samples without nano additives and samples with nano additives. In the fire reaction tests, it was observed that nano additives did not have a negative effect on the combustion properties of OSB. It was observed in fire reaction test that the flame height did not exceed the limit value determined by the standard for each group and nano additives.

Benzer Tezler

  1. Tez No

    316422

    Ahşap sandviç panel ve laminat parke üretiminde nanopartikül kullanımı ve teknolojik özellikler üzerine etkisi

    Nanoparticles use in manufacture of wood-based sandwich panels and laminate flooring and its effects on technological properties

    ZEKİ CANDAN

    Doktora

    Türkçe

    Türkçe

    2012

    Mühendislik Bilimleriİstanbul Üniversitesi

    Orman Endüstri Mühendisliği Ana Bilim Dalı

    PROF. DR. TURGAY AKBULUT

  2. Tez No

    392238

    An experimental study on the interfacial characteristics of fiber reinforced polymeric composites enhanced with nano-scale materials

    Nano boyuttaki malzemeler ile güçlendirilmiş elyaf takviyeli polimerik kompozitlerin arayüz karakteristikleri üzerine deneysel bir çalışma

    ECE BELEN

    Yüksek Lisans

    İngilizce

    İngilizce

    2014

    Mühendislik BilimleriSabancı Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MEHMET YILDIZ

    YRD. DOÇ. DR. SERKAN ÜNAL

  3. Tez No

    348678

    An experimental study on the incorporation of carbon nanotubes into resin transfer molded composites

    Karbon nanotüp ile güçlendirilmiş elyaf takviyeli kompozitlerin üretimi üzerine deneysel bir çalışma

    FAZLI FATİH MELEMEZ

    Yüksek Lisans

    İngilizce

    İngilizce

    2013

    Havacılık MühendisliğiSabancı Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MEHMET YILDIZ

  4. Tez No

    467257

    Acoustic properties of styrene butadiene rubber-isocyanate composition reinforced with carbon nanotubes and silicon oxide nano-powder

    Silikon oksit nano tozları ve karbon nanotüpleri ile güçlendirilmiş stiren bütadien kauçuk-izosiyanat kompozisyonunun akustik özellikleri

    ALKAN SANCAK

    Yüksek Lisans

    İngilizce

    İngilizce

    2017

    Mühendislik Bilimleriİstanbul Teknik Üniversitesi

    Nanobilim ve Nanomühendislik Ana Bilim Dalı

    PROF. DR. LEVENT TRABZON

  5. Tez No

    809426

    Farklı çevre koşullarında polietilen bazlı Bi2O3 ile güçlendirilmiş nanokompozit şeritlerin dielektrik, mekanik özelliklerinin incelenmesi ve yapay zeka ile tahmini

    Investigation of dielectric and mechanical properties of polyethylene based Bi2O3 reinforced nanocomposite strips in different environmental conditions and estimation with artificial intelligence

    NAZLICAN ŞAHİN

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Fizik ve Fizik MühendisliğiYıldız Teknik Üniversitesi

    Fizik Ana Bilim Dalı

    PROF. DR. ZEYNEP GÜVEN ÖZDEMİR

    PROF. DR. KADİR ESMER

Geri Dön