Color stability, surface roughness and surface morphology of universal composites

Universal kompozitlerin renk stabilitesinin, yüzey pürüzlülüğünün ve yüzey morfolojisinin değerlendirilmesi

PDF İndir

  1. Tez No: 890410
  2. Yazar: MOHAMMAD MENIAWI
  3. Danışmanlar: PROF. DR. ESRA CAN EROĞLU
  4. Tez Türü: Doktora
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: renk stabilitesi, yüzey pürüzlülüğü, üniversal kompozit, enjekte edilebilir kompozit, Diş renk değişikliği, Nanokompozitler, color stability, surface roughness, universal composites, injectable composite, Tooth discoloration, Nanocomposites
  7. Yıl: 2024
  8. Dil: İngilizce
  9. Üniversite: Yeditepe Üniversitesi
  10. Enstitü: Sağlık Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Restoratif Diş Tedavisi Bilim Dalı
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

MENIAWI, M (2024). Universal kompozitlerin renk stabilitesinin, yüzey pürüzlülüğünün ve yüzey morfolojisinin değerlendirilmesi, Yeditepe Üniversitesi Sağlık Bilimleri Enstitüsü, Restoratif Diş Hekimliği, Doktora tezi, İstanbul Amaç: Bu in vitro çalışmanın amacı universal kompozitlerin renk stabilitesinin, yüzey pürüzlülüğünün (Ra; µm) ve yüzey morfolojisinin değerlendirilmesidir. Gereç ve Yöntem: Çalışmada supra nano-fil Estelite Asteria (EA; Tokuyama, Japonya), nano- hibrit Gaenial A'chord (GA; GC, Japonya), nano-hibrit G-aenial Universal Injectable (GI; GC, Japonya), nano-fil Filtek Universal (UF) ; 3M. ABD) ve nano-fil Filtek Ultimate (FU; 3M, ABD) kompozitlerinin her birinden 40'ar adet olmak üzere toplam 200 adet örnek, 2 mm kalınlıkta ve 10 mm çapında hazırlandı ve üreticilerin talimatlarına göre polimerize edildi (Bluephase N; Ivoclar, ABD). Kompozit örnekler 24 saat 37°C' de distile suda bekletildikten sonra, yüzeyleri 600 gritlik silikon karbit zımpara ile standardize edildi ve Twist DIA lastikleri (Kuraray, Japonya) ve 3, 1 ve 0.5 µm'luk elmas patları (Shofu; Japan, Diamond polish Ultradent; USA) ile cilalandı. Daha sonra her bir kompozit grubundaki örnekler çalışmada kullanılan renklendirici solüsyonları çay, kahve, kırmızı şarap ve yapay tükürük (kontrol) olmak üzere rastgele şekilde dört alt gruba ayrıldı (n=10). Başlangıç renk ölçümleri spektrofotometre (Minolta CM-2600d) ve başlangıç Ra ölçümleri profilometre (Perthometer M1 Mahr, Almanya) ile gerçekleştirildi. Örnekler her gün taze olarak hazırlanan çay ve kahve solüsyonları ve şarap ile renklendirildi. Bu amaçla örnekler 6 saat renklendirici solüsyonda, 18 saat yapay tükürükte bekletildi. Kontrol grubu örnekleri her gün değiştirilen yapay tükürükte saklandı. Renklendirme protokolü 21 gün boyunca tekrarlandı. Renk ölçümleri 7, 14 ve 21. günlerde tekrarlandı ve meydana gelen renk değişikliği (∆E00) hesaplandı. 21. günün sonunda Ra tekrar değerlendirildi. Her gruptan temsili örnekler SEM ile incelendi (Tübitak MAM). Renk değişikliği (∆E00) ve yüzey pürüzlülüğü (Ra) verileri three-way ANOVA ve post hoc Tukey testleri kullanılarak istatistiksel olarak analiz edildi (p<0.05). Bulgular: ∆E00ve Ra, kompozitten (p<0.001), renklendirici solüsyondan (p<0.001) ve değerlendirme süresinden (p<0.001) istatistiksel olarak ileri derecede etkilendi ve iki test yöntemi için de değişkenler arasında istatistiksel olarak anlamlı etkileşim saptandı. Tüm kompozitler ve değerlendirme dönemleri için en yüksek renk değişimi kırmızı şarap solüsyonunda meydana gelirken (p<0.001), bunu siyah çay (p<0.001) ve kahve (p<0.001) ⅹⅴⅰ takip etti. Tüm kompozitler arasında GI ve FU kompozitleri 21. günde kırmızı şarap (12,89±0,97 ve 13.131±0.663), siyah çay (9,47±1,15 ve 10.534±0.349) solüsyonlarının her birinde istatistiksel olarak anlamlı derecede en düşük ∆E00 değerlerini gösterdi. Tüm kompozitler, renklendirici solüsyonlara maruz kaldıktan sonra istatistiksel olarak anlamlı şekilde daha yüksek Ra değeri gösterdi (p<0.001), ancak renklendirici solüsyonlar arasında Uf ve EA kompozitleri hariç anlamlı bir fark saptanmadı (p>0.05). Sonuç: Üniversal kompozitler, renklendirici solüsyonlara maruz kaldıklarında klinik olarak kabul edilemez renk değişikliğine uğramakta ve yüzey pürüzlülükleri artmaktadır, ancak yüzey pürüzlülüğündeki artış plak akümülasyonu için gerekli olan eşik değere ulaşmamaktadır.

Özet (Çeviri)

MENIAWI, M (2024). Color Stability, Surface Roughness and Surface Morphology of Universsal Composites, Yeditepe University, Institute of Health Science, Department of Restorative dentistry, PhD thesis, Istanbul. Objectives: This in vitro study aimed to evaluate the color stability, surface roughness (Ra; µm), and surface morphology of universal composites after exposure to discoloring agents over a period of 21 days. Materials and Methods: A total of 200 cylindrical composite discs (n=40 from each); supra nano-fill Estelite Asteria (EA; Tokuyama, Japan), nano-hybrid G-aenial A'chord (GA; GC, Japan), nano-hybrid G-aenial Universal Injectable (GI; GC, Japan), nano-fill Filtek Universal (UF; 3M. USA) and nano-fill Filtek Ultimate (FU; 3M, USA) were prepared and polymerized (Bluephase N; Ivoclar, USA). Following storage in distilled water for 24 h at 37°C, the specimens were finished with 600 grit SIC paper and polished with Twist DIA (Kuraray, Japan) followed with 3, 1 and 0.5 µm grit diamond pastes (Shofu; Japan, Diamond polish Ultradent; USA). Then, each composite group was randomly divided into four subgroups according to the discoloring agents; Black tea, coffee, red wine, and artificial saliva (n=10) and initial color measurements (spectrophotometer; Minolta CM-2600d) and initial Ra (profilometer; Perthometer M1 Mahr, Germany) were evaluated. The immersion protocol in discoloring agents was repeated for 21 days. Color measurements were performed after 7, 14, and 21 days, and ∆E 00 was calculated, while Ra was evaluated after 21 days. Representative specimens from each group were investigated under SEM (Tübitak MAM). ∆E 00 and Ra data were analyzed using three-way ANOVA and post hoc Tukey's tests (p<0.05). Results: ∆E 00 and Ra were significantly influenced by the composite (p<0.001), discoloring agent (p<0.001), and the evaluation period (p<0.001), while significant interactions were evaluated between the variables for both test methods. For all the composites and evaluation periods, red wine resulted significantly in the highest color change (p<0.001), which was followed by black tea (p<0.001) and coffee (p<0.001). After 21 days, GI and FU resulted significantly in the lowest ∆E 00 among all the tested universal composites for red wine (13.131±0.663; 12.89±0.97 respectively) and black tea (9.47±1.15; 10.534±0.349 respectively). All the composites revealed significantly higher Ra after exposure to discoloring agents (p<0.001), however, no significant differences were evaluated among red wine, black tea and coffee except UF and EA (p>0.05). Conclusion: Universal composites revealed unacceptable color change and increased surface roughness after exposure to discoloring agents over a period of 21 days, however the increase in surface roughness did not reach the critical threshold value for plaque accumulation.

Benzer Tezler

  1. Tez No

    709787

    Direkt kompozit veneer materyali olarak kullanılan kompozitlerin renk stabilitesi ve yüzey pürüzlülüğünün değerlendirilmesi

    Evaluation of color stability and surface roughness of composites used as direct composite veneer material

    OĞUZHAN BALDIRAN

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2021

    Diş HekimliğiOndokuz Mayıs Üniversitesi

    Restoratif Diş Tedavisi Ana Bilim Dalı

    PROF. DR. ERTAN ERTAŞ

  2. Tez No

    1017435

    Farklı pediatrik ilaçların prefabrike zirkonyum kronların yüzey pürüzlülüğü ve renk stabilitesi üzerine etkilerinin in vitro değerlendirilmesi

    The effects of various pediatric medications on the surface roughness and color stability of prefabricated zirconia crowns: An in vitro evaluation

    ELİF SERCAN

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2026

    Diş HekimliğiBolu Abant İzzet Baysal Üniversitesi

    Pedodonti Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ SERPİL SAĞDIÇ

  3. Tez No

    1014143

    Farklı sinterleme yöntemlerinin ve farklı içeceklerin çok katmanlı monolitik zirkonya restorasyonların renk stabilitesine ve yüzeypürüzlüğüne etkisinin incelenmesi

    Investigation of the effects of different sintering methods and different beverages on the color stability and surface roughness of multi-layered monolithic zirconia restorations

    AYBERK YEŞİL

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2026

    Diş HekimliğiOndokuz Mayıs Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. GÖZLEM CEYLAN

  4. Tez No

    978161

    Şeffaf plakların kahve ile renklendirilmesi ve temizleyici ajanların uygulanmasının renk değişimi ve yüzey özelliklerine olan etkisi: Bir in-vitro çalışma

    The effect of coffee staining and cleaning agents on the color change and surface properties of clear aligners: An in vitro study

    OYTUN DEMİR

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2025

    Diş HekimliğiÇukurova Üniversitesi

    Ortodonti Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ AYÇA ÜSTDAL GÜNEY

  5. Tez No

    1018732

    Farklı pH değerindeki sıvıların 3B yazıcı ile üretilen daimi kuron materyallerindeki yüzey özellikleri ve renk değişimlerine etkisinin değerlendirilmesi

    Evaluation of the effects of liquids with different pH values on the surface properties and color changes of permanent crown materials produced by 3D printing

    MERVE SEVGİ ULUIŞIK

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2026

    Diş HekimliğiOndokuz Mayıs Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. TOLGA KÜLÜNK

Geri Dön