Çimento yerine sığır gübresi külünün kısmi ikamesi ile üretilen pomza agregalı hafif betonun mekanik ve fiziksel özellikleri üzerine etkisinin araştırılması

Investigation of the effect on the mechanical and physical properties of pumice aggregate lightweight concrete produced by partial replacement of cattle manure ash instead of cement

PDF İndir

  1. Tez No: 899988
  2. Yazar: AHMET KORKMAZ
  3. Danışmanlar: PROF. DR. SIRRI ŞAHİN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Ziraat, İnşaat Mühendisliği, Agriculture, Civil Engineering
  6. Anahtar Kelimeler: sığır gübresi külü, pomza, hafif beton, basınç dayanımı, donma çözülme, puzolan Eylül 2024, 67 sayfa, cattle manure ash, pumice, lightweight concrete, compressive strength, freeze-thaw, pozzolan September 2024, 67 Pages
  7. Yıl: 2024
  8. Dil: Türkçe
  9. Üniversite: Atatürk Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Tarımsal Yapılar ve Sulama Ana Bilim Dalı
  12. Bilim Dalı: Tarımsal Yapılar ve Sulama Bilim Dalı
  13. Sayfa Sayısı: 67

Özet

Amaç: Bu çalışma, hafif agrega olarak pomza ve Türkiye'de kırsal alanlarda ısınma amaçlı geleneksel enerji kaynaklarından güneşte kurutulmuş sığır gübresi külünün (SGK) farklı oranlarda çimento yerine ikame edilerek üretilen hafif betonun mekanik ve fiziksel özelliklerini deneysel olarak test etmek amacıyla yapılmıştır. Yöntem: SGK ve CEM I 42,5 R çimento tipi bu çalışmada kullanılmıştır. Karışımlarda çimento yerine ağırlıkça belirli oranlarda (%0, %5, %10, %15 ve %20) SGK ikame edilerek 5 grup halinde toplam 90 adet 150×150×150 mm'lik küp numune üretilmiştir. Taze beton deneyleri olarak, birim ağırlık deneyleri; sertleşmiş beton deneyleri olarak da kuru birim ağırlık ve su emme 28.günde, basınç dayanımı 14, 28, 56.günde ve donma-çözülme sonrası basınç dayanımı deneyleri ise 28.günde yapılmıştır. Bulgular ve Sonuç: Üretilen numunelerin SGK ikamesinin artması ile kontrol numunelerine göre basınç dayanımlarında bir miktar düşüş göstermiş, ancak kür süresinin artmasıyla da dayanımın arttığı görülmüştür. %5, %10, %15 ve %20 oranlarında SGK ikamesi ile üretilen numunelerin 56 günlük basınç dayanımı düşüş oranı değerleri kontrol örnekleri ile karşılaştırıldığında sırasıyla %3, %3,8, %5,3 ve %6,3 olarak belirlenmiştir. Çimentonun yerine SGK ikamesinin kullanılması basınç dayanımında bir azalmaya yol açsa da, 56 günlük numunelerde %6,3'lük bir azalma gözlemlenmiştir. Donma çözülme sonrası basınç dayanımı değerlerine bakıldığında, SGK ikamesinin artmasıyla donma çözülme öncesi basınç dayanımı ile karşılaştırıldığında bir miktar artış belirlenmiştir. Bu durum, hafif agregalı betonların suya doygun olmayan çok sayıda gözeneğe sahip olması ve zarar görmeden gözeneklerdeki buzun genleşmesine izin vermesinden ileri geldiği düşünülmüştür.

Özet (Çeviri)

Purpose: This study was carried out to experimentally test the mechanical and physical properties of lightweight concrete produced by substituting pumice as lightweight aggregate and sun-dried cattle manure ash (CMA), one of the traditional energy sources for heating in rural areas of Turkey, for cement at different ratios. Method: In this study, CMA and CEM I 42.5 R cement types were used. A total of 90 cube specimens (150×150×150 ) mm were produced in five groups by replacing cement with CMA in various percentages (0%, 5%, 10%, 15% and 20%) by weight in the mixtures. Unit weight tests were conducted as fresh concrete tests, while dry unit weight and water absorption tests were performed on the 28th day. Compressive strength tests were conducted on the 14th, 28th and 56th days, and post-freeze-thaw compressive strength tests were conducted on the 28th day. Results and Conclusion: The compressive strength of the produced specimens exhibited a slight decrease compared to the control specimens with an increase in CMA substitution. However, it was observed that the strength increased with the increase in curing time. The reduction rates in compressive strength of the specimens produced with 5%, 10%, 15% and 20% CMA substitution were determined to be 3%, 3,8%, 5,3% and 6,3%, respectively, when compared with the control specimens. Although the use of CMA substitute instead of cement led to a decrease in compressive strength, 6,3% decrease was observed in 56-day-old samples When the post-freeze-thaw compressive strength values were analysed, it was found that there was a slight increase in compressive strength with the increase of CMA substitution compared to the pre-freeze-thaw compressive strength. This is thought to be due to the fact that lightweight aggregate concretes have many pores that are not saturated with water and allow the ice in the pores to expand without being damaged.

Benzer Tezler

  1. Tez No

    540634

    Çimento esaslı silis dumanlı uçucu küllü kompozitlerin sem ve xrd destekli görsel analizlerin yapay sinir ağları ile modellenmesi

    Modeling of sem and xrd visual analysis of cement base silica fume fly ash composites with artificial neural networks

    BURHAN UZBAŞ

    Doktora

    Türkçe

    Türkçe

    2019

    İnşaat MühendisliğiAtatürk Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. ABDULKADİR CÜNEYT AYDIN

  2. Tez No

    291166

    Uçucu küllü silindirle sıkıştırılmış betonlarda dayanıklılık

    Durability of fly ash incorporating roller compacted concrete

    ALİ MARDANİ AGHABAGLOU

    Yüksek Lisans

    Türkçe

    Türkçe

    2011

    İnşaat MühendisliğiEge Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. KAMBİZ RAMYAR

  3. Tez No

    791974

    Experimental and analytical study on the performance of cementitious mixes containing different re-generated end of life materials

    Başlık çevirisi yok

    MATINEH MAHMOUDI

    Yüksek Lisans

    İngilizce

    İngilizce

    2022

    İnşaat MühendisliğiÖzyeğin Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    Assist. Prof. Dr. ZEYNEP BAŞARAN BUNDUR

  4. Tez No

    199133

    Alkalilerle aktive edilmiş yüksek fırın cüruflu harçların özelikleri

    Properties of alkalis activated blast furnace slag mortars

    MEHMET CANBAZ

    Doktora

    Türkçe

    Türkçe

    2007

    Mühendislik BilimleriEskişehir Osmangazi Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF.DR. İLKER BEKİR TOPÇU

  5. Tez No

    467973

    Öğütülmüş riyolit ve trakit minerallerinin puzolanik özelliklerinin araştırılması, uçucu kül ve yüksek fırın cürufu ile karşılaştırılması

    Investigation of the puzzolanic characteristics of grained riolite and trachyte minerals, compared with fly ash and blast furnace slag

    VAHİDDİN ALPEREN BAKİ

    Yüksek Lisans

    Türkçe

    Türkçe

    2017

    İnşaat MühendisliğiKaradeniz Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. ŞAKİR ERDOĞDU

Geri Dön