Nicrmo ve CoCrMo dental malzemelerin korozyonuna yapay ağız ortamında florür iyonlarının etkisi
Effect of fluoride ions in the artificial oral environment on the corrosion of nicrmo and CoCrMo dental materials
- Tez No: 904310
- Danışmanlar: PROF. DR. MÜŞERREF ÖNAL
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Alaşım elementleri, Alaşımlar, Diş hekimliği, Korozyon, Metaller, Alloy elements, Alloys, Dentistry, Corrosion, Metals
- Yıl: 2024
- Dil: Türkçe
- Üniversite: Ankara Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Günümüzde, metalik dental malzemeler biyouyumlu olmaları sebebiyle diş hekimliğinde ortodontik tedavilerde yaygın olarak kullanılmaktadır. Ancak günlük yaşamda diş macunları, ilaçlar, gıdalar ve özellikle soğuk-sıcak içecekler (pH<7) bu malzemelerin zamanla aşınarak korozyona uğramasına neden olmaktadır. Korozyon nedeniyle ağız ortamına geçen metal iyonları canlı doku içerisine nüfus ederek çeşitli alerjik hastalıklara yol açmaktadır. Bu nedenle, dental malzemelerin korozyonunu önlemek son derece önemlidir. Bu tezde, dental NiCrMo ve CoCrMo malzemelerle yapılan elektrokimyasal deneyler sitrik asit (1mM, 10mM, 50mM), üre (1mM, 10mM, 50mM) ve yapay tükürük ortamlarında florür iyonlarının etkisi (pH 5.35, 37±0.1°C) elektrokimyasal yöntemlerle araştırılmıştır. Elektrokimyasal empedans spektroskopisi yöntemine (EIS) göre, sitrik asit ortamda NiCrMo alaşımı/çözelti ara yüzünde yük transfer kontrolü bir reaksiyon yürürken CoCrMo alaşımında difüzyon kontrollü bir reaksiyon gerçekleşmiştir. Ayrıca sitrik asit ve üre derişimi arttıkça direnç azalmıştır. Flor iyonları varlığında ise bu direncin daha da azaldığı ortaya çıkmıştır. Yapay tükürük ortamında CoCrMo alaşımın empedans direnci (≈15kΩ.cm2) NiCrMo alaşımına göre daha fazla (≈13kΩ.cm2) olduğu tespit edilmiştir. Bu sonuçları akım-potansiyel (TAFEL) eğrilerinden elde edilen veriler desteklemiştir. Elektrokimyasal yöntemlere göre, asidik yiyecek veya içeceklerin alınımında NiCrMo alaşımının daha dayanıklı olacağını ve yapay tükürük ortamında ise CoCrMo alaşımın daha uzun ömürlü olacağı sonuçlarına varılmıştır.
Özet (Çeviri)
Today, metallic dental materials are widely used in orthodontic treatments in dentistry due to their biocompatibility. However, in daily life, toothpastes, medicines, foods and especially cold-hot drinks (pH<7) cause these materials to wear and corrode over time. Metal ions passing into the oral environment due to corrosion penetrate into living tissue and cause various allergic diseases. Therefore, it is extremely important to prevent corrosion of dental materials. In this thesis, electrochemical experiments with dental NiCrMo and CoCrMo materials were investigated by electrochemical methods in citric acid (1mM, 10mM, 50mM), urea (1mM, 10mM, 50mM) and artificial saliva environments (pH 5.35, 37±0.1°C). According to the electrochemical impedance spectroscopy (EIS) method, a charge transfer controlled reaction was carried out at the NiCrMo alloy/solution interface in citric acid medium, while a diffusion controlled reaction took place on the CoCrMo alloy. In addition, the resistance (Rp) decreased with increasing concentrations of citric acid and urea. In the presence of fluorine ions, the Rp was found to decrease even more. The impedance resistance of CoCrMo alloy (≈15kΩ.cm2) was higher than that of NiCrMo alloy (≈13kΩ.cm2) in artificial saliva. These results were supported by the data obtained from current-potential (TAFEL) curves. According to electrochemical methods, it was concluded that NiCrMo alloy would be more durable in the ingestion of acidic food or beverages and CoCrMo alloy would be more durable in an artificial saliva environment.
Benzer Tezler
- Döküm yoluyla elde edilen titanyuma farklı yüzey işlemleri uyguladıktan sonra 3 tip titanyum porseleni ile bağlantısının değerlendirilmesi
Appreciate of bonding of 3 titanium porcelain with casting titanium applying different surface treatment
ASLI ACAR
Doktora
Türkçe
2005
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ.DR. ÖZGÜR İNAN
- P- tipi silisyum yarıiletkeni ile yapılan bipolar ve simetrik kontak yapıların I-V ve C-V karakteristikleri incelenerek çeşitli parametrelerin hesaplanması
The Study of I-V and C-V characteristic of bipolar and symmetric contact structures by using the semiconductor of p-type
ABDULKADİR DARTICI
Yüksek Lisans
Türkçe
1992
Fizik ve Fizik MühendisliğiErciyes ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. NECATİ YALÇIN
- Development of nickel based HER and OER catalysts for anion exchange membrane electrolyzer
Anyon değişim membran elektrolizörler için nikel temelli HER ve OER katalizör geliştirilmesi
YAKUBU SAWADOGO ADAM
- Prediction and optimization of hydrogen production
Hidrojen üretiminin tahmini ve optimizasyonu
ŞEKİP CANER ESMERLİ
Yüksek Lisans
İngilizce
2024
Makine MühendisliğiAdana Alparslan Türkeş Bilim ve Teknoloji ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. CEYLA GÜNGÖR
- Plazma kaynak metodu ile özellikleri geliştirilmiş plazma püskürtme kaplamaların tribolojik davranışlarının incelenmesi
Investigation of tribological behavior of plasma-sprayed coatings modified with plasma welding method
İSMAİL BAYAR
Yüksek Lisans
Türkçe
2016
Makine MühendisliğiEskişehir Osmangazi ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. MUSTAFA ULUTAN