Bonding ajan uygulamasına ihtiyaç duymayan restoratif materyallerin daimi diş yüzeylerine bağlanma dayanımının değerlendirilmesi
Evaluation of the bond strength of restorative materials applied without a separate bonding agent to teeth in the permanent dentition
- Tez No: 1003885
- Danışmanlar: DOÇ. DR. MERVE CANDAN
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Mikrogerilim bağlanma dayanımı, yapay çürük dentin, restoratif materyal, Microtensile bond strength, artificial caries-affected dentin, restorative material
- Yıl: 2026
- Dil: Türkçe
- Üniversite: Eskişehir Osmangazi Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Pedodonti Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı, yüksek viskoziteli cam iyonomer siman, rezin modifiye cam iyonomer siman, kendiliğinden sertleşen kompozit, alkasit ve kompozit rezin materyallerin sağlam ve yapay çürük oluşturulmuş dentin yüzeyleri üzerindeki mikrogerilim bağlanma dayanımı (µGBD), kırık tipleri, SEM ile değerlendirilen arayüz özelliklerini karşılaştırmalı olarak incelemektir. Gereç ve Yöntem: Çalışmada 96 adet insan 3. molar dişi kullanılmıştır. Oklüzal mine uzaklaştırılarak standart dentin yüzeyleri oluşturulmuş ve örnekler sağlam dentin ve yapay çürük oluşturulmuş dentin olmak üzere iki dentin tipine ayrılmıştır. Dentin örnekler Equia Forte HT, Fuji IX GP, Fuji II LC, Cention Forte, Stela ve Filtek Z550 restoratif materyalleri ile restore edilmiştir. Örneklerden 1 mm2 yüzey alanına sahip çubuklar hazırlanmış ve mikrogerilim bağlanma dayanımı testi uygulanmıştır. Kırık tipleri dental loupe altında değerlendirilmiştir. Restoratif materyal–dentin arayüzü SEM analizleri ile değerlendirilmiştir. Verilerin değerlendirilmesinde iki yönlü varyans analizi ve Tukey HSD post-hoc testi kullanılmıştır. Bulgular: Materyal türü, dentin tipi ve materyalxdentin etkileşimi µGBD değerlerini etkilemiştir. Filtek Z550 grubunun sağlam dentin tipinde elde edilen µGBD değerleri diğer tüm materyallerden istatistiksel olarak anlamlı derecede yüksek bulunurken, aynı grupta yapay çürük dentin tipinde elde edilen µGBD değerleri sağlam dentin tipine kıyasla istatistiksel olarak anlamlı derecede daha düşük saptanmıştır (p<0,01). Tüm gruplarda en sık adeziv kırıklar gözlenmiştir. Sonuç: Çalışmanın bulguları, materyallerin dentin yüzeylerine bağlanma davranışlarının, dentin yüzeyi, materyalin kimyasal yapısı ve materyalxdentin etkileşimi ile ilişkili olabileceğini düşündürmektedir. Bununla birlikte, bulguların klinik olarak doğrulanması için in vivo çalışmalara ihtiyaç duyulmaktadır.
Özet (Çeviri)
Aim: This study comparatively evaluated the microtensile bond strength (µTBS), failure modes, and SEM-assessed interfacial characteristics of a high-viscosity glass ionomer cement, a resin-modified glass ionomer cement, a self-cure composite, an alkasite-based restorative material, and a composite resin on sound and artificially caries-affected dentin surfaces. Materials and Methods: Sixty human third molar teeth were included. Following occlusal enamel removal, standardized dentin surfaces were prepared and specimens were allocated to two dentin types: sound dentin and artificially caries-affected dentin. Dentin specimens were restored with Equia Forte HT, Fuji IX GP, Fuji II LC, Cention Forte, Stela, and Filtek Z550. Beam-shaped specimens with a 1 mm² cross-sectional area were obtained and subjected to the µTBS test. Failure modes were assessed under a dental loupe, and the restorative material–dentin interface was evaluated using SEM. Data were analyzed using two-way analysis of variance and Tukey HSD post-hoc test. Results: Material type, dentin type, and the material×dentin interaction significantly affected the µTBS values. In the Filtek Z550 group, µTBS on sound dentin was significantly higher than in all other materials, whereas µTBS on artificially caries-affected dentin was significantly lower than on sound dentin within the same group (p<0.01). Adhesive failures were most frequently observed in all groups. Conclusion: The findings of the present study suggest that the bonding behavior of the tested materials to dentin surfaces may be associated with the dentin surface condition, the chemical composition of the material, and the material×dentin interaction. Nevertheless, in vivo studies are required to clinically validate these findings.
Benzer Tezler
- Deneysel antioksidan ajan uygulamasının ve flor salan bonding materyali kullanımının, beyazlatma işlemı uygulanmış mineye yapıştırılan ortodontik braketlerin bağlanma dayanımı üzerine etkisinin değerlendirilmesi
Evaluation of the effect of experimental antioxidant treatment and the use of fluoridereleasing boning material on the shear bond strength of orthodontic brackets in bleached teeth
EZGİ AY
Doktora
Türkçe
2023
Diş HekimliğiSağlık Bilimleri ÜniversitesiOrtodonti Ana Bilim Dalı
DR. ÖĞR. ÜYESİ DERYA DURSUN
- Synthesis of low noise, fast drying packaging tape adhesive via emulsion polymerization
Emülsiyon polimerleşmesi ile hızlı kuruyan, sessiz koli bandı için yapıştırıcı sentezi
CANSU AKARSU DÜLGAR
Doktora
İngilizce
2017
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. İBRAHİM ERSİN SERHATLI
- Soğuk plazma uygulamasının sabit protetik restorasyonların tamirindeki etkinliğinin incelenmesi
Investigation of the effectiveness of non-thermal plasma application on repair of fixed prosthetic restorations
MEHMET KÖSE
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş Hekimliğiİzmir Katip Çelebi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ÖZLEM ÇÖLGEÇEN
- Beyazlatma işlemi sonrası yapılan kompozit restorasyonların bağlanma dayanımına antioksidan ajan ve bekletme süresinin etkisi
The effect of antioxidant and delayed bonding time on shear bond strength of composite restoration after bleaching procedure
NESLİHAN GÜLERYÜZ
Doktora
Türkçe
2011
Diş HekimliğiMarmara ÜniversitesiDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
PROF. DR. CAFER TÜRKMEN
- Güncel adezivlerin uygulanma aşamasındaki gecikmelerin dentine bağlanma başarılarına olan etkilerinin incelenmesi
Investigation of the effects of current adhesives in application on delays on the success of dentin bonding
AHMET GÜLTEKİN
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiAkdeniz ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. OSMAN TOLGA HARORLI