Synthesis and characterization of waterborne and phosphorus containing flame-retardent polyurethane coatings

Fosfor içeren yanmaz özellikli suda yayınık poliüretan boya sentezi ve karakterizasyonu

  1. Tez No: 119411
  2. Yazar: FUNDA ÇELEBİ
  3. Danışmanlar: PROF. DR. LEYLA ARAS, PROF. DR. GÜNGÖR GÜNDÜZ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya, Chemistry
  6. Anahtar Kelimeler: Boya, Suda-yayınma, Poliüretan, Yanmaya dayanıklılık, Fosfor fenil dihidroksil. VI, Paint, water-dispersed, polyurethane, flame retardant, phosphorus phenyl dihydroxy. IV
  7. Yıl: 2002
  8. Dil: İngilizce
  9. Üniversite: Orta Doğu Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 114

Özet

öz FOSFOR İÇEREN YANMAZ ÖZELLİKLİ SUDA YAYINIK POLİÜRETAN BOYA SENTEZİ VE KARAKTERİZASYONU Çelebi, Funda Yüksek Lisans, Kimya Bölümü Tez Yöneticisi: Leyla Araş, Prof. Dr. Ortak Tez Yöneticisi: Güngör Gündüz, Prof. Dr. Ocak 2002, 98 sayfa Bu çalışmada, fosfor içerikli bileşiğin değişik oranlarda poliüretan ana zincirine bağlanması sağlanarak, yanmaya dayanıklı suda yayınık poliüretan boyalar üretilmiştir. Yanmaya dayanıklı madde sentezi üç aşamada gerçekleştirilmiştir. Birinci aşamada, benzaldehit ve pentaeritritol tepkimesinden monobenzalpentaeritritol elde edilmiştir. İkinci aşamada, monobenzalpentaeritritolün fosforlanması sağlanmıştır. Son aşama ise oluşan ürünün asetik asit çözeltisi içerisinde hidrolizi sonucu fosfor fenil dihidroksil oluşumunu içermektedir.Suda yayınık poliüretan boya, poliester poliol, izoforon diizosiyanat ve hidrofilik monomer olarak da dimetilol propiyonik asit (DMPA) kullanılarak üretilmiştir. Suda yayınık poliüretan boyaların fiziksel ve termal özelliklerini iyileştirmek amacıyla karşıt bağlayıcı olarak %5 oranında poliizosiyanat ve melamin kullanılmıştır. Ayrıca, poliester/ fosfor içerikli madde oranının değiştirilmesiyle, farklı miktarlarda fosfor içeren yanmaya dayanıklı suda yayınık poliüretan boyalar elde edilmiştir. Sentezlenen ürünlerin yapı özellikleri 'H-NMR, 3,P-NMR ve İR spektrometreleri ile belirlenmiş olup, polimerlerin ısıl davranışları DSC ve TGA yöntemleri ile ortaya çıkırılmıştır. Ayrıca fosfor miktarındaki artışın poliüretan boyanın fiziksel, mekanik ve ısıl özelliklerine etkisi incelenmiştir. Fosfor fenil dihidroksilin poliüretan ana zincirine bağlanmasıyla boyaların sertlik değerlerinin arttığı ancak parlaklık değerlerinin az miktarda düştüğü gözlenmiştir. Bütün boya örnekleri üstün çarpma dayanımı ve esneklik göstermişlerdir. Ayrıca, fosfor miktarındaki artışın yanma esnasında kömürleşme miktarım artırdığı görülmüştür. Poliüretan boyanın yanmaya karşı en üst dayanıklılık değerine 29 oksijen indeksi ile % 1.5 fosfor içerdiğinde ulaşılmıştır. Daha fazla fosfor eklenmesinde ise poliüretan boyanın yanmaya karşı dayanıklılığının azaldığı gözlenmiştir.

Özet (Çeviri)

ABSTRACT SYNTHESIS AND CHARACTERIZATION OF WATERBORNE AND PHOSPHORUS CONTAINING FLAME RETARDANT POLYURETHANE COATINGS Çelebi, Funda M.S., Department of Chemistry Supervisor: Leyla Aras, Prof. Dr. Co-Supervisor: Güngör Gündüz, Prof. Dr. January 2002, 98 pages In this study, phosphorus containing flame retardant water-dispersed polyurethane paints were produced by incorporating different amounts of phosphorus compound onto the polyurethane main chain. The novel flame retardant compound was synthesized in three steps. In the first step, monobenzalpentaerythritol was produced from benzaldehyde and pentaerythritol. In the second step, phosphorylation of monobenzal pentaerythritol was performed. Final step includes the formation of phosphorus phenyl dihydroxyl from the hydrolyzation of the resulting product in acetic acid solution. IllWater-dispersed polyurethane paint was produced using polyester polyol, isophorone diisocyanate and dimethylol propionic acid (DMPA) as a hydrophilic monomer. To improve the physical and thermal properties of the waterborne polyurethanes, 5% (w/w) polyisocyanate and melamine were used as crosslinking agents. By changing the feed ratio of polyester and phosphorus compound, the flame retardant water-dispersed polyurethane paints with different phosphorus contents were obtained. All the synthesized products were characterized by H-NMR, P-NMR and IR spectroscopies, and the thermal stabilities of the polymers were evaluated by their DSC and TGA thermograms. The effects of increasing phosphorus content on the physical and thermal properties of polyurethane paints were also examined. The addition of phosphorus phenyl dihydroxyl to the main chain increased the hardness but slightly decreased the gloss values of the polyurethane paints. All the samples showed superior impact resistance, and flexibility. Increasing phosphorus content increased the char yield and the maximum fire retardancy was reached at 1.5%P content with the limiting oxygen index value of 29. Further addition of phosphorus decreased the flame resistance of polyurethane paints.

Benzer Tezler

  1. Tez No

    153326

    Synthesis and characterization of waterborne silane coupling agent containing silicone-acrylic resin

    Silan bağlayıcı içeren suda yayınık silikon-akrilik reçine sentezi ve karakterizasyonu

    ÖZLEM AKIN

    Yüksek Lisans

    İngilizce

    İngilizce

    2004

    Polimer Bilim ve TeknolojisiOrta Doğu Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    PROF. DR. LEYLA ARAS

    PROF. DR. GÜNGÖR GÜNDÜZ

  2. Tez No

    478670

    Synthesis and characterization of branched, functional polyurethane dispersions as a technology platform for self-crosslinking textile coatings

    Kendiliğinden çapraz bağlanan tekstil kaplamaları için bir teknoloji platformu olarak dallanmış, fonksiyonel poliüretan dispersiyonlarının sentezi ve karakterizasyonu

    AYŞE DURMUŞ SAYAR

    Yüksek Lisans

    İngilizce

    İngilizce

    2017

    KimyaSabancı Üniversitesi

    Malzeme Bilimi ve Nanoteknoloji Ana Bilim Dalı

    YRD. DOÇ. DR. SERKAN ÜNAL

    PROF. DR. YUSUF ZİYA MENCELOĞLU

  3. Tez No

    833178

    Emülsiyon polimerizasyonu ile vinilik ve akrilik kompozit latekslerin sentezi ve karakterizasyonu

    Synthesis and characterization of vinyl and acrylic composite latexes with emulsion polymerization

    NURULLAH KARTALOĞLU

    Doktora

    Türkçe

    Türkçe

    2023

    Polimer Bilim ve TeknolojisiYozgat Bozok Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. ALİ DELİBAŞ

  4. Tez No

    363497

    Synthesis and characterization of acrylic acid-maleic anhydride copolymers and their use in water borne paints

    Akrilik asit – maleik anhidrit kopolimerlerinin sentezi, karakterizasyonu ve su bazlı boyalarda kullanımı

    BAHADIR KAYA

    Yüksek Lisans

    İngilizce

    İngilizce

    2014

    Polimer Bilim ve Teknolojisiİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    PROF. DR. İBRAHİM ERSİN SERHATLI

  5. Tez No

    394258

    Synthesis and characterization of novel waterborne polyurethane dispersions

    Özgün su bazlı poliüretan dispersiyonlarının sentezi ve karakterizasyonu

    NESİBE AYŞE DOĞAN

    Yüksek Lisans

    İngilizce

    İngilizce

    2014

    Mühendislik BilimleriSabancı Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    PROF. DR. YUSUF ZİYA MENCELOĞLU

    YRD. DOÇ. DR. SERKAN ÜNAL

Geri Dön