Mekanik alaşımlamanın volfram ağır alaşımlarının yüksek sıcaklık sinterleme davranışlarına olan etkilerinin incelenmesi
Investigations of mechanical alloying effect on high temperature sintering behaviors of tungsten heavy alloys
- Tez No: 126751
- Danışmanlar: PROF. DR. M. LÜTFİ ÖVEÇOĞLU
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2002
- Dil: Türkçe
- Üniversite: İstanbul Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Seramik Sanat Dalı
- Sayfa Sayısı: 82
Özet
MEKANİK ALAŞIMLAMANIN VOLFRAM AĞIR ALAŞIMLARININ YÜKSEK SICAKLIK SİNTERLEME DAVRANIŞLARINA OLAN ETKİLERİNİN İNCELENMESİ ÖZET Bu yüksek lisans tezinde, elemental tozlardan yola çıkarak W-Ni-Fe üçlü sistemindeki 56Ni-24Fe-20W bileşimi atritör ortamında 10, 20, 30, 40 ve 50 saat süreyle mekanik olarak alaşımlanmıştır. Elde edilen bu mekanik alaşımlanmış yapıya hedef 90W7Ni3Fe bileşimini oluşturacak şekilde başlangıç W tozu ilavesi yapılmıştır. Elde edilen bu 90W7Ni3Fe bileşimindeki bu karışımlar 150 MPa'da preslendikten sonra 1460°C ve 1500°C'da sinterlenmişlerdir. İkinci bir paralel set olarak 50 saat atritör ortamında mekanik alaşımlanan 56Ni-24Fe-20W bileşimindeki tozdan hareketle yine başlangıç W tozu ilavesiyle 75W-80W-85W-90W-95W-(7/3 Ni:Fe) bileşimleri hazırlanmıştır. Tüm bu bileşimler de 150 MPa'da preslendikten sonra 1500°C'dasinterIenmiştir. Yapılan bu deneysel çalışmalar; atritörde mekanik alaşımlanan tozların taramalı elektron mikroskobu (SEM)'de gerçekleştirilen mikroyapı incelemeleri, dilatometre çalışmaları,, numunelerin boyutlarına göre yaş yoğunluk, Arşimed prensibine göre sinterlenmiş yoğunluk ölçümleri, optik mikroskobi ve sertlik ölçümleriyle desteklenen karakterizasyon çalışmasıyla desteklenmiştir. Mekanik alaşımlama işlemiyle zamana bağlı olarak mikroyapısal incelme ve homojenizasyon tespit edilmiştir. Fakat mekanik alaşımlanan bu yapıların 1500°C gibi yüksek bir sinterleme sıcaklığında sinterlenmesi durumunda tüm numunelerin aralarındaki başlangıç farklılıklarını ortadan kaldıran ve benzer özellik gösteren mikroyapılar elde edilmiştir. Bu amaçla dilatometre çalışmaları sonucunda seçilen 1460°C sıcaklığında ldk., 10dk., 30dk. ve 60 dk'lık sürelerle gerçekleştirilen sinterleme işlemi zamana ve mekanik alaşımlama süresine bağlı olarak mikroyapısal farklılıkları ortaya koymuş olup aynı sinterleme sıcaklığında daha düşük volfram tane boyutuna ve daha yüksek sertliğe sahip volfram ağır alaşımlarının üretilebileceğinin işaretini vermiştir. xı
Özet (Çeviri)
INVESTIGATIONS OF MECHANICAL ALLOYING EFFECT ON HIGH TEMPERATURE SINTERING BEHAVIORS OF TUNGSTEN HEAVY ALLOYS SUMMARY In this presented thesis, the comparative high temperature sintering behaviour of different composition of mechanically alloyed ternary W-Ni-Fe systems were investigated. In order to achieve this, preblended powder mixture constituting the composition of 56Ni-24Fe-20W was mechanically alloyed in an attritor mill for 10, 20, 30, 40, 50 hours. The mechanically alloyed composition was used for preparation of 90W7Ni3Fe heavy alloy mixtures by the addition of initial W powder. Resultant powder mixtures were compacted into cylindrical shapes under 150 MPa and sintered at 1460°C and 1500°C under a protective athmosphere. A second experimental set was also prepared for 50 hours mechanically alloyed powder mixture to obtain the target compositions of 75W-80W-85W-90W-95W-(7/3 Ni:Fe) heavy alloys. In the experimental studies; scanning electron microscopy (SEM) observations of mechanical alloyed powders were carried out, dilatometric studies were performed from the compacted powders, density measurements were also performed according to Archimedes Principles, optical microscopy observations were realized from the polished sample surfaces and hardness values were also measured in order to characterize the processing effects. Microstructural homogenization and fineness were obtained with the increasing of the mechanical alloying time. In the case of selection relatively high sintering temperature like 1500°C, all compositions were showed nearly similar microstructural features as a result of normalization effect. For this reason lower sintering temperature of 1460°C were selected after careful investigation of dilatometric studies and kinetic sintering experiment realized for duration of 1 min., 10 min., 30 min. and 60 min. This experiment was showed clear microstructural differences and we believe that this is a good sign for the lower temperature sintering production of tungsten heavy alloys with smaller tungsten grain sizes and better mechanical properties. xn
Benzer Tezler
- W-Ni-B ve W-Ni ağır alaşımlarının karşılaştırmalı sinterleme davranışları
The Comparative sintering behaviours of W-Ni-B and W-Ni heavy alloys
PINAR TURAN
Yüksek Lisans
Türkçe
2002
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
PROF. DR. M. LÜTFİ ÖVEÇOĞLU
- Characterization investigations of W-xTi alloys and W-xTi/2 WT% LaB6 composites fabricated by mechanical alloying and sintered using pressureless sintering or spark plasma sintering techniques
Mekanik alaşımlama ve basınçsız sinterleme ile spark plazma sinterleme yöntemleriyle üretilen W-xTi alaşımların ve W-xTi/2 WT% LaB6 kompozitlerinkarakterizasyon çalışmaları
HADI JAHANGIRI
Doktora
İngilizce
2016
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. MUSTAFA LUTFİ ÖVEÇOĞLU
- Microstructural and physical characterization of mechanically alloyed W-1 wt% Ni-x WB (x=0.5, 1.0, 2.0, 4.0) and W-1 wt% Ni-2 wt% WB-y La2O3 (y=0.5, 1) powders and sintered composites
Mekanik alaşımlanmış W-ağ.%1 Ni-ağ. % x WB (x=0.5, 1.0, 2.0, 4.0 ve W-ağ. 1% Ni-ağ. %2 WB-ağ. %yLa2O3 (y=0.5, 1) toz ve sinter kompozitlerin mikroyapısal ve fiziksel karakterizasyonu
DİDEM OVALI
Yüksek Lisans
İngilizce
2013
Metalurji Mühendisliğiİstanbul Teknik Üniversitesiİleri Teknolojiler Ana Bilim Dalı
PROF. DR. M. LÜTFİ ÖVEÇOĞLU
- Mekanik alaşımlama yönteminin sızdırma tekniğiyle üretilen WC-Cu sisteminin yoğunlaşma davranışına etkileri
The effects of mechanical alloying method on densification of the WC-Cu system which is produced by infiltration technique
AYDIN ŞELTE
Yüksek Lisans
Türkçe
2012
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. BURAK ÖZKAL
- Development and characterization investigations of mechanically alloyed and sintered W- TiC -Ni composites
Mekanik alaşımlama yöntemiyle üretilmiş W- TiC-Ni kompozitlerinin geliştirilmesi ve özelliklerinin incelenmesi
AZİZ GENÇ
Yüksek Lisans
İngilizce
2009
Metalurji Mühendisliğiİstanbul Teknik Üniversitesiİleri Teknolojiler Ana Bilim Dalı
PROF. DR. M. LÜTFİ ÖVEÇOĞLU