Mono/di-bromometil benzoil peroksitler (t-BuBP/BBP) ve AgSbF6/ZnCl2 başlatıcı sistemleri ile stirenin katyonik polimerizasyonu
Cationic polymerization of styrene by the mono/di-bromomethyl benzoyl peroxides (t-BuBP/BBP) with AgSbF6/ZnCl2 initiating systems
- Tez No: 139150
- Danışmanlar: DOÇ. DR. SEVİL SAVAŞKAN YILMAZ
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Makromonomerik Peroksi Başlatıcı, Blok Kopolimer, Multikomponent, Graft Kopolimer, Şişme Oram. VI, Macromonomeric Peroxy Initiator, Block Copolymer, Multicomponent, Graft Copolymer, Swelling Ratio. vn
- Yıl: 2003
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Bu çalışmada, mono / di-bromometil benzoil peroksitler (t-BuBP / BBP) ve AgSbFö / ZnCl2 başlatıcı sistemleri kullanılarak stirenin katyonik polimerizasyonu ile makromonomerik peroksi başlatıcılar, Polistiren sentezlendi. Yaşayan katyonik polimer zinciri potasyum metakrilat tuzu İle sonlandınldı ve makromonomerik peroksi başlatıcının ucuna vinil grubu bağlandı. Elde edilen başlatıcılar ^-NMR, İR ve GPC teknikleriyle karakterize edildi. 80°C'de farklı zamanlarda makromonomerik Polistiren başlatıcılann metil metakrilat ile blok kopolimerizasyonu sonucu çözünebilen Poli (S-b-MMA) blok kopolimerler elde edildi. Blok kopolimerler fa-NMR, İR ve SEM teknikleriyle karakterize edildi. Peroksijen grubu içeren Poli (S-b-MMA) blok kopolimerleri, akrilik asit ile 90°C'de 12 saat polimerleştirildi. Elde edilen çapraz bağlı Poli (S-b-MMA-AA) multikomponentlerin CHCl3'deki ve toluendeki şişme oranlan incelendi. Peroksijen grubuna sahip makromonomerik Polistiren başlatıcılar kullanılarak Polibütadien ile 90°C'de graft kopolimerler elde edildi. Çapraz bağlı graft kopolimerlerin CHCl3'deki ve toluendeki şişme oranlan incelendi. Sentezlenen multikomponentler ve graft kopolimerler İR ve SEM teknikleriyle karakterize edildi.
Özet (Çeviri)
SUMMARY Cationic Polymerization of Styrene by the Mono / Di-bromomethyl Benzoyl Peroxides (t-BuBP / BBP) with AgSbF<; / ZnCl2 Initiating Systems In this study, macromonomeric peroxy initiators, Polystyrene were synthesized via cationic polymerization of styrene by the mono / di-bromomethyl benzoyl peroxides (t-BuBP / BBP) with AgSbFg / ZnCfe initiating systems. The living cationic polymer chain was terminated by using potassium methacrylate salt and the vinyl group was added to the end of macromonomeric peroxy initiator. The initiators were characterized by ^-NMR, FT-IR and GPC techniques. Soluble Poly (S-b-MMA) block copolymers were obtained as a result of the block copolymerization of methyl methacrylate (MMA) with macromonomeric Polystyrene initiators in different times at 80°C. Block copolymers were characterized by rH-NMR, FT-IR and SEM techniques. Poly (S-b-MMA) block copolymers having peroxygen groups were polymerized with acrylic acid, AA, for 12 hours at 90°C. The swelling ratios of the crosslinked Poly (s-b-MMA-b-AA) multicomponents were examined in CHCI3 and toluene. Graft copolymers were obtained by using macromonomeric Polystyrene initiators having peroxygen group with polybutadiene (PBd) for 12 hours at 90°C. The swelling ratios of the crosslinked grafts copolymers were investigated in CHCI3 and toluene. Synthesized multicomponents and graft copolymers characterized by FT-IR and SEM techniques.
Benzer Tezler
- Ön işlemenin ve askorbik asitin dondurularak depolanan yılan balıklarının (Anguilla anguilla) kalitesine etkileri
Başlık çevirisi yok
H.VOLKAN GÖKSEL
Yüksek Lisans
Türkçe
1985
Gıda MühendisliğiEge ÜniversitesiSu Ürünleri Ana Bilim Dalı
DOÇ. DR. AYDIN URAL
- Uzun zincirli bazı alkil aromatik hidrokarbonların yüzey aktif madde olarak kullanım alanlarının incelenmesi
Başlık çevirisi yok
SAADET YAPAR
- Dondurularak saklamanın tavuk etinin bazı kalite özellikleri üzerine etkisi
Başlık çevirisi yok
Ö.EVREN ATASOY
Yüksek Lisans
Türkçe
1987
Gıda MühendisliğiEge ÜniversitesiGıda Mühendisliği Ana Bilim Dalı
DR. SUMRU TÖMEK
- Merkezsel ve dışmerkezsel çapraz elemanlı çerçeve yapıların statik ve deprem yüküne göre optimum tasarımı
Optimum desing of concentrically and eccentrically braced frames under static and earthquake loading
F.GÜLTEN GÜLAY