Removal of cobalt from zinc sulfate solution by cementation prior to zinc electrowinning
Çinko elektrokazanımı öncesi sementasyon yöntemiyle kobaltın çinko sülfat çözeltisinden uzaklaştırılması
- Tez No: 143594
- Danışmanlar: PROF. DR. YAVUZ TOPKAYA
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Kobalt, çöktürme, sementasyon, arseniküçoksit, çinko-kalay alaşımı, saflaştırma, Cobalt, precipitation, cementation, arsenic trioxide, zinc-tin alloy, purification
- Yıl: 2003
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 111
Özet
Bu tezin amacı, kobaltın konvansiyonel metodla ve yeni katkı maddeleri olan %4 ve %10 kalay içeren çinko alaşımı tozları ile çöktürülerek çinko sülfat çözeltisinden uzaklaştırılmasıdır. Deneylerde sentetik olarak hazırlanan 150 g/l Zn ve 75 mg/1 Co içeren liç çözeltisi kullanılmıştır. Konvansiyonel yöntemle yapılan deneylerde incelenen parametreler arseniküçoksit miktarı ve bakır sülfat eklenmesinin kobalt çöktürülmesi üzerine etkisidir. Çinko-kalay alaşım tozları kullanılarak yapılan deneylerde çalışılan parametreler arseniküçoksit miktarı, bakır sülfat ve çinko-kalay eklemeleri, çöktürme süresi ve sıcaklığıdır. Eklenecek olan çinko-kalay alaşımları miktarını belirlemek için farklı iki alaşımla yapılan deneylerdeki tek fark eklenen arseniküçoksittir. %4 kalay-çinko alaşımı miktarı çalışılırken çözeltiye arseniküçoksit ilavesi yapılmıştır. %10 kalay-çinko alaşımı miktarı çalışması ise arsenik katkısız gerçekleştirilmiştir. Çökeleklerin X-ışınları kırınımı (XRD) analizleri yapılmış ve çökelekler tarama elektronu mikroskobunda (SEM) incelenmiştir. Elde edilen sonuçlar, çinko-kalay alaşımlarının saf çinkoya göre daha iyi olduğunu göstermiştir. Çöktürme verimi 4 g/l %4 Sn-Zn alaşımı tozu, 1,2 g/l CuS04.5H20, 0,12 g/l AS2O3 ilavesi ile 85-90°C sıcaklıkta ve 2 saat süre ile sınırlandığında en yüksek değerine ulaşmıştır. Arsenİküçoksit kullanmadan çözeltideki kobalt miktarını 2 mg/1 nin altına indirebilmek için başlangıç Sn/Co ağırlık oranı 13.25:1 olan %10 kalay-çinko alaşımı eklenmelidir; bu durumda deney sıcaklığı 85 °C, süresi ise 2 saattir.
Özet (Çeviri)
The aim of this study was to investigate the removal of cobalt from zinc sulfate solution by cementation with the help of conventional and new type of additives that were 4% Sn-zinc alloy powder and 10% Sn-zinc alloy powder, respectively. Synthetic leach solutions containing 150 g/1 Zn and 75 mg/1 Co were prepared and used in all of the experiments. The parameters researched with the conventional method were the amount of arsenic trioxide and the effect of copper sulfate on cementation of cobalt. While using the alloys, the parameters studied were the amounts of arsenic trioxide, copper sulfate and tin containing zinc alloy powder additions, cementation duration and temperature. The difference in the optimization of alloy additions was in the amount of addition of arsenic trioxide. The amount of 4%Sn-zinc alloy powder was tried to be optimized with the addition of arsenic trioxide whereas the optimization was tried to be done without any arsenic addition while using 10%Sn-zinc alloy. The XRD and SEM studies of the cementates were also performed. The obtained results indicated that tin containing alloys were much better than pure zinc. With the additions of 4 g/1 4%Sn-Zn alloy dust, 1.2 g/1 CuS04.5H20, 0.12 g/1 AS2O3 and in 2 hours of cementation duration at 85-90°C, the maximum amount of cobalt cementation efficiency was achieved. The experiments indicated that cobalt in the solution could be reduced to about 2 mg/1 by using 10%Sn-zinc alloy powder with an initial Sn/Co weight ratio of 13.25:1 without the addition of arsenic trioxide at 85°C in 2 hours of cementation duration.
Benzer Tezler
- Cobalt removal from zinc sulfate solutions prior to zinc electrowinning by cementation
Çinko elektrokazanımı öncesi kobaltın çöktürülerek çinkosülfat çözeltilerinden uzaklaştırılması
GÜVENÇ ERGİN
Yüksek Lisans
İngilizce
2000
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. YAVUZ TOPKAYA
- Yüklü nikel çözeltilerinin saflaştırılması: Sülfatlı ortamda seçimli demir giderimi
Purification of nickel loaded pls: Selective removal of iron content at sulfate media
SU DEMİRBOĞA
Yüksek Lisans
Türkçe
2024
Kimya MühendisliğiEge ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. HAYATİ TÜRKMEN
- Sülfatlı çözeltilerden bakır ve kobaltın H2S ile çöktürülme kinetiğinin incelenmesi
The Investigation of precipitation kinetics of copper and cobalt by H2S in sulphate based solutions
CEM OKTAYBAŞ
- Atık pillerin değerlendirilmesi
Recyling used batteries
HANİFE BANABAK
Yüksek Lisans
Türkçe
1997
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. A. NURSEN İPEKOĞLU
- Tekstil atıksularındaki boyar maddelerin fotokatalitik oksidasyon ile giderimi için zno bazlı katalizörlerin geliştirilmesi
Development of zno based catalysts for photocatalytic degradation of dyes in textile wastewater
BEYZA DEMİR
Yüksek Lisans
Türkçe
2019
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. MELEK TÜTER
PROF. DR. ŞEYMA AYDINOĞLU