Geri Dön

Kalsiyum alüminatum spinel esaslı dökülebilir refrakterlerde kullanılabilirliğinin incelenmesi

The investigation of the usage of the calcium aluminate in spinel based refractory castables

  1. Tez No: 151261
  2. Yazar: UMUT KARAKAŞ
  3. Danışmanlar: PROF. DR. SERDAR ÖZGEN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2004
  8. Dil: Türkçe
  9. Üniversite: İstanbul Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Seramik Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 62

Özet

KALSİYUM ALUMINATIN SPINEL ESASLI DOKULEBILIR REFRAKTERLERDE KULLANILABİLİRLİĞİNİN İNCELENMESİ ÖZET 1970 yıllardan bu yana refrakter endüstrisinde meydana gelen hızlı değişimlere paralel olarak dökülebilir refrakterlerin kullanım alanında da büyük bir artış olmuştur. Tuğla refrakterlere göre daha ucuz ve üretiminin daha az zahmetli olması gibi özelliklerinden dolayı dökülebilir refrakterlerin kullanımı gün geçtikçe önem kazanmaktadır. Bu çalışmada ilk önce Andreasen denklemine göre belirlene tane boyut dağılım modülüne bağlı kalarak değişik pişirme sıcaklıklarında kalsiyum alüminatm çimento ile vereceği reaksiyonlar ve bu reaksiyonların görünür porozite, hacim ağırlığı, soğukta basma mukavemeti, kalıcı genleşme-büzülme ve termal şok dayanımı gibi refrakterler açısından önem arz eden özelliklerin ne derece değiştiği incelenmiş, karışımlarda kullanılacak olan optimum çimento miktarı belirlenmiştir. İkinci aşamada ise karışımlara belirli oranlarda ilave edilen kalsiyum alüminatm spinel esaslı dökülebilir refrakter karışımlarında vereceği reaksiyonlar sonucu yukarıda sayılan özelliklerin değişimleri incelenmiş ve spinel esaslı dökülebilir refrakter karışımlarında kullanılabilecek optimum kalsiyum alüminat miktarı belirlenmiştir. İlave edilen bu hammaddelerin yanında sistemin reolojik özeliklerinin arttırılması amacı ile yapıya %8 oranında reaktif alümina ilavesi yapılmıştır. Sonuç olarak, ilk aşamada kalsiyum alüminatm %5 çimento oranı ile birlikte kullanılmasının uygun olacağı, kalsiyum alüminatm spinel esaslı karışımlarda denenmesi sonucunda ise artan kalsiyum alüminat oranına paralel olarak yapının büzülmeye doğru gittiği saptanmıştır. Termal şok dayanımında %6 kalsiyum alüminat ilavesinin termal şok dayanımında düşüşe neden olmadığı ancak bu oranın aşılması halinde ise termal şok dayanımında azalma meydana geldiği saptanmıştır. Ayrıca kalsiyum alüminatm sentetik bir malzeme olmasından dolayı su miktarını arttırdığı dolayısıyla priz alma süresini geciktirdiği tespit edilmiştir. ıx

Özet (Çeviri)

THE INVESTIGATION OF THE USAGE OF THE CALCIUM ALUMINATE IN SPINEL BASED REFRACTORY CASTABLES SUMMARY Usage and the consumption of the castables were increased by the developments of the refractory industry since the 1970's. According to, brick refractories, due to its low cost and the rapid usage, the importance of the castables increase day by day. In this study, firstly, the effect of the reactions between calcium aluminate and cement on the apparent porosity, bulk density, cold crushing strength, thermal expansion-shrinkage and thermal shock resistance are investigated at different temperatures with the grain size distribution determined by using the Andreasen equation and cement ratio was obtained. Secondly, the variation of the properties described in the first part is investigated according to the reactions between calcium aluminate and spinel, when these raw materials are mixtured with certain proportions, then optimum ratio of calcium aluminate for mixture of spinel based refractory castables is generally obtained. A reactive alumina (8 %) is added to the mixture to increase reological properties of the system. Consequently, in the first part it is determined that %5 of cement should be mixtured by calcium aluminate for the mixture. The spinel based refractory castables structure starts to shrink by increasing of the rate of calcium aluminate in this mixture. Addition of %6 calcium aluminate to the mixture does not change the thermal shock resistance but exceeding this ratio decreases the thermal shock resistance. Since the calcium aluminate is a synthetic material contains some water in it, solidification time increases.

Benzer Tezler

  1. Effects of particle granulation optimisation and new binder development on properties of alumina based castable refractories

    Tane boyut dağılımı optimizasyonunun ve yeni bağlayıcı geliştirilmesinin alümina esaslı dökülebilir refrakterlerin özelliklerine etkileri

    MELİS OKTAY

    Yüksek Lisans

    İngilizce

    İngilizce

    2018

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. ÖMER SERDAR ÖZGEN

  2. Reaktif spark plazma yöntemi ile kalsiyum karbonat katkılı alüminyum oksinitrürün üretimi, karakterizasyonu ve özellikleri

    Production, characterization and properties of CaCO3 doped AlON with reactive spark plasma sintering

    SAMET KAYA

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. FİLİZ ŞAHİN

  3. Microstructural characterization of corroded MgO-based refractory materials

    Korozyona uğramış MgO-esaslı refrakter malzemelerin mikroyapısal karakterizasyonu

    YENER MERCANKÖŞK

    Yüksek Lisans

    İngilizce

    İngilizce

    2002

    Metalurji Mühendisliğiİzmir Yüksek Teknoloji Enstitüsü

    Metalurji Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. SEDAT AKKURT

    PROF. DR. MUHSİN ÇİFTÇİOĞLU

  4. Kalsiyum alüminat çimentosu ile portland çimentosunun karşılaştırılması

    Comparison of aluminate cement and portland cement

    MURAT AYDIN

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Maden Mühendisliği ve MadencilikÇukurova Üniversitesi

    Maden Mühendisliği Ana Bilim Dalı

    PROF. DR. SUPHİ URAL

  5. İkincil alüminyum cürufunun çimento ve beton üretiminde değerlendirilmesi

    Evaluation of secondary aluminium dross in cement and concrete production

    GÖKHAN ÇİL

    Doktora

    Türkçe

    Türkçe

    2023

    Metalurji MühendisliğiSakarya Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. KENAN YILDIZ