Ferritik paslanmaz çeliğin korozyon davranışına karbür yapıcı alaşım elementlerinin etkilerinin incelenmesi
The investigation of effects of carbid forming alloying elements on corrosion behaviour of ferritic stainless steel
- Tez No: 169343
- Danışmanlar: Y.DOÇ.DR. TÜLAY YILDIZ
- Tez Türü: Doktora
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Ferritik paslanmaz çelik, korozyon, alaşım elementi, ısıl işlem. IX, Ferritic stainless steel, corrosion, alloying element, heat treatment X
- Yıl: 2005
- Dil: Türkçe
- Üniversite: Fırat Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 145
Özet
ÖZET Doktora Tezi FERRİTİK PASLANMAZ ÇELİĞİN KOROZYON DAVRANIŞINA KARBÜR YAPICI ALAŞIM ELEMENTLERİNİN ETKİLERİNİN İNCELENMESİ Hülya EREN Fırat Üniversitesi Fen Bilimleri Enstitüsü Metalürji Anabilim Dalı 2005, Sayfa: 134 Bu çalışmada ferritik paslanmaz çelik içerisine % 0.5, % 1 ve % 3 oranlarında niyobyum ve % 1 oranlarında molibden, vanadyum ve titanyum ilave edilerek elde edilen numunelerin korozyon davranışları incelenmiştir. Numuneler döküm yöntemiyle üretildikten sonra sıcak dövme ile şekillendirilmiştir. Korozyon deneyleri AC impedans tekniği ve kütle kaybı yöntemleri ile yapılmıştır. AC impedans deneyleri sonunda elde edilen polarizasyon dirençleri yardımıyla korozyon akımları kütle kaybı deneyleri sonucunda ağırlık kaybı belirlenerek korozyon hızlan hesaplanmıştır. Korozyon ortamı olarak 0.1 M H2SO4 ve 0.3 M HC1 çözeltileri kullamlmıştır. Numuneler korozyon testleri öncesi üç gruba ayrılmışlardır. Birinci grup numuneler ısıl işleme tabi tutulmamış, yani üretim şartlarında olan numunelerdir. İkinci grup numuneler 30 dakika boyunca 1 100 °C de tavlanarak, üçüncü grup numuneler ise 180 dakika boyunca 1100 °C de tavlanarak suda soğutulmuşlardır. SEM incelemeleri için numuneler 30 dakika ve 360 dakika korozyona maruz bırakılmıştır. Sonuçta 1100 °C de uygulanan ısıl işleminin bütün numunelerin korozyon dirençlerini artırdığı gözlenmiştir. Ayrıca, korozyon dirençleri birbirine çok yakın olmasına rağmen en iyi sonuç molibdenli numunede gözlenmiştir. Bu tür çeliklerin sülfürik asit ortamına oranla klorürlü ortamlarda daha dayanıklı olduğu belirlenmiştir.
Özet (Çeviri)
ABSTRACT PhD Thesis THE INVESTIGATION OF EFFECTS OF CARBID FORMING ALLOYING ELEMENTS ON CORROSION BEHAVIOUR OF FERRTTIC STAINLESS STEEL Hülya EREN Fırat University Graduate School of Natural and Applied Sciences Department of Metallurgy Education 2005, Page: 134 In this study, corrosion behavior of 0.5, 1.0, 3.0 wt. % amounts niobium added ferritic stainless steel and 1.0 % wt. amounts molybdenum, vanadium and titanium added ferritic stainless steel have been investigated. Samples were obtained with use of casting and forging process. Corrosion experiments were performed by means of AC impedance technique and mass loss methods. Corrosion currents and corrosion rates were calculated from polarization resists obtained AC impedans technique; mass loss obtained with mass loss tests, respectively. 0.1 M H2SO4 and 0.3 M HC1 solutions were used as corrosive environment. Samples were classified as three groups before corrosion tests. The first group samples were expose any heat treatment, i.e. they are under production conditions. The second group of samples were quenched after annealing at 1 100 °C for 1/2 hours although third group samples were annealing at 1 100 °C for 3 hours and then quenched. SEM investigations were performed on surfaces of samples which exposed to aggressive environment for 30 and 360 minutes. As a result; it was observed that heat treatment applied at 1100 °C has increased corrosion resistance of samples. Although they are very close the other, the best result observed from molybdenum containing samples. It was determined that these species steels are more resistant in chloride solutions than sulphuric acid solutions.
Benzer Tezler
- %17 kromlu ferritik paslanmaz çeliklerin nokta kaynağında kaynak parametrelerinin tanelerarası korozyon ve çekme makaslama dayanımı üzerindeki etkisinin incelenmesi
Investigation of the effects of the welding parameters upon the intergranular corrosion and tensile shear strengths in the spot welding of 17% chromium ferritic stainless steels
BAHADIR GÜLBAHAR
- AISI 430 paslanmaz çeliklerin V bükme işleminde ileri ve geri yaylanmanın deneysel olarak incelenmesi
Experimental investigation of spring-go and spring-back in V die bending process of AISI 430 stainless steel
SİNAN ARSLAN
Yüksek Lisans
Türkçe
2018
Makine MühendisliğiHitit ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ MUHAMMED EMİN ERDİN
- Dubleks paslanmaz çelik (1.4462) malzemenin farklı iletim hızlarında erozif aşınma davranışı üzerine bir çalışma
A study on the erosive wear behavior of duplex stainless steel (1.4462) at different transmission rates
MEHMET ALİ KAHRAMAN
Yüksek Lisans
Türkçe
2023
Makine MühendisliğiKarabük ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. RECEP DEMİRSÖZ
- Borlanmış 430F ferritik paslanmaz çeliğin aşınma davranışı üzerine bir çalışma
A study on the wear behavior of borided 430F ferritic stainless steels
MÜCAHİT UYAR
Yüksek Lisans
Türkçe
2019
Metalurji MühendisliğiAfyon Kocatepe ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. HALİL AYTEKİN
- N-substituye karbazollerin endüstriyel metallerin korozyonunu önlemedeki etkileri
Corrosion inhibition effect of N-substituted carbazole on the corrosion of some industrial metals
SADIK ÖZTÜRK