Polymerization and characterization of allyl methacrylate
Alil metakrilatın polimerleştirilmesi ve poly(alil metakrilatın)karakterizasyonu
- Tez No: 180937
- Danışmanlar: PROF. DR. ALİ USANMAZ
- Tez Türü: Yüksek Lisans
- Konular: Polimer Bilim ve Teknolojisi, Polymer Science and Technology
- Anahtar Kelimeler: alil metakrilat, bozunma, X-ışın fotoelektron spektroskopisi(XFS), Kütle Spectrometresi (MS), Thermogravimetrik Analiz (TGA), allyl methacrylate, degradation, X-Ray Photoelectron Spectroscopy(XPS), Mass Spectroscopy (MS), Thermal Gravimetric Analysis(TGA)
- Yıl: 2006
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Polimer Bilim ve Teknolojisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 99
Özet
Alil metakrilat, AMA farklı koşullarda kimyasal başlatıcı ve γ-ışınları kullanılarakpolimerleştirilmiştir. Elde edilen polimer, genellikle bilinen çözücülerdeçözünmeyen jel tipindedir. Kimyasal başlatıcılarla başlatılan polimerleşmedeArrhenius aktivasyon enerjisi 82.3 kJ/mol olarak hesaplanmıştır. Polimer FT-IR,NMR, DSC, TGA, XPS, XRD, DLS, ve MS metodları ile karakterize edilmiştir. Alilyan gruplarının %98-99'u polimerizasyon bittikten sonra yerlerini korurken, %1-2'si çapraz bağlanma ve/veya halka reaksiyonu ile lakton oluşturuşlardır.Spektroskopik ve ısısal sonuçlar, polimerizasyonun halka polimerizasyonuolmadığını, fakat son grup halka polimerleşmesi olabileceğini göstermektedir. DLS'de molekül ağırlığı 1.1x106 olarak ölçülmüştür. Polimerin çözünmez olması çaprazbağlanmadan çok yüksek molekül ağırlığından kaynaklanmaktadır. Polimerin DSC'de gözlenen Tg 'si 94ºC' dir. Ancak 150-200ºC' de yaşlandırmadan sonra Tg211ºC' ye yükselmiştir. Polimer 350ºC' de yapılan ısısal işlemden sonra yan-bağlantı tipi bozunma ve bunu izleyen yan grup halka reaksiyonu sonucu laktonve/veya anhidrit vermiştir. XPS analizi AIBN ve CCl4 radikal gruplarınınoligomerlerde bulunduğunu göstermektedir. MS ve TGA termogramları polimerinçözünürlüğüne bağlı olarak iki veya üç aşamada bozunduğunu göstermektedir.Birinci aşamada, 225-350ºC, alil grupları yan-bağlantı tipi bozunmaktadir. kinciaşamada ise, 395-515ºC, rastgele bölünme ve depolimerizasyon tipi bozunmaoluşmaktadır.
Özet (Çeviri)
Allyl methacrylate, AMA was polymerized by chemical initiator and by γ-radiationunder different conditions. The polymer obtained is mostly gel type with somesoluble fractions at lower conversions. Arrhenius activation energy is 82.3 kJ/molfor chemical initiated polymerization. The polymer was characterized by FT-IR,NMR, DSC, TGA, XPS, XRD, DLS, and MS methods. It was found that about 98-99% of allyl side groups retained as pendant even after completion of thepolymerization, while 1-2% may give crosslinking and/or cyclization that yieldslactones and anhydrides. The spectroscopic and thermal results of the workshowed that the reaction is not cyclopolymerization, but may have end groupcyclization. Molecular weight of 1.1x106 was measured by DLS. Therefore,insolubility is due to the high molecular weight of polymer, even in the earlystage of polymerization rather than crosslinking. The Tg of PAMA was observedas 94ºC before curing, upon curing at 150-200ºC, Tg increased to 211ºC asmeasured by DSC. The thermal treatment of polymer at about 350ºC gaveanhydride by linkage type degradation, following side group cyclization. The XPSanalysis showed the presence of radical fragments of AIBN and CCl4 associatedwith oligomers. The MS and TGA thermograms showed two or three stagedegradations depending on solubility. The first stage was mostly linkage typedegradation for the fragmentation of pendant allyl groups at 225-350ºC. In thesecond stage, at 395-515ºC, the degradation is random scission anddepolymerization.
Benzer Tezler
- Synthesis and characterization of hydrogels from allyl methacrylate and acrylamide copolymer
Alil metakrilat ve akrilamid kopolimerinden hidrojel sentezi ve karakterizasyonu
NESLİHAN AYAZOĞLU
Yüksek Lisans
İngilizce
2011
Polimer Bilim ve TeknolojisiOrta Doğu Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Bölümü
DR. SELDA KESKİN
PROF. DR. ALİ USANMAZ
- Alkali dirence sahip akrilik emülsiyon polimerlerinin sentezi ve karakterizasyonu
Synthesis and characterization of alkali resistant acrylic emulsion polymers
BUSE MÜZEYYEN POYRAZ
Yüksek Lisans
Türkçe
2020
KimyaGebze Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ İLKE ANAÇ
- N-vinilkaprolaktam esaslı jellerin sentezi ve karakterizasyonu
Synthesis and characterization of N-vinylcaprolactam based gels
ELÇİN ÇAKAL
Yüksek Lisans
Türkçe
2009
Kimya Mühendisliğiİstanbul ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. SELVA ÇAVUŞ
- İyonik sıvı destekli PVDF polielektrolitlerin kontrollü polimerizasyonla hazırlanması ve karakterizasyonu
Preparation and characterization of ionic liquid supported PVDF polyelectrolytes by controlled polymerization
BURAK BEKDAŞ
Yüksek Lisans
Türkçe
2021
Polimer Bilim ve TeknolojisiMarmara ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. NİLHAN KAYAMAN APOHAN
DOÇ. DR. BURCU OKTAY
- The synthesis and characterization of periphery functional multiarm star polymers
Çevre fonksiyonlu çok kollu yıldız polimerlerin sentezi ve karakterizasyonu
NEŞE ÇAKIR YİĞİT
Doktora
İngilizce
2017
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. GÜRKAN HIZAL