CrN, TİN kaplanmış ve kaplanmamış AISI 304 paslanmaz çeliğinin korozyon özellikleri

The corrosion features of stainless steels coated with CrN and TİN and non-coated

  1. Tez No: 184581
  2. Yazar: MUSTAFA UYSAL
  3. Danışmanlar: PROF. DR. MUAMMER NALBANT, DOÇ. DR. TÜLİN KIYAK
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Teknik Eğitim, Mechanical Engineering, Technical Education
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2006
  8. Dil: Türkçe
  9. Üniversite: Gazi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Eğitimi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 112

Özet

CrN, TiN KAPLANMIŞ VE KAPLANMAMIŞ AISI 304 PASLANMAZÇELİĞİNİN KOROZYON ÖZELLİKLERİ(Yüksek Lisans Tezi)Mustafa UYSALGAZİ ÜNİVERSİTESİFEN BİLİMLERİ ENSTİTÜSÜMayıs 2006ÖZETLiteratürde TiN ve CrN kaplamaların korozyon özellikleri hakkında yeterliçalışmaya rastlanmamıştır. Bu çalışmada paslanmaz çelik üzerine PVDyöntemine göre yapılan TiN ve CrN ince kaplamaların paslanmaz çeliğekazandırdığı korozyon özellikleri araştırılmıştır.Her üç çeliğin 0,5 M NaCl ortamında serbest korozyon ve aşırı polarizasyonkoşullarında elde edilen Elektrokimyasal bulguları ile EDS, SEM ve ICP çözeltianaliz sonuçları beraberce değerlendirilmiştir. Kullanılan elektrokimyasalteknikler, yarı kararlı potansiyodinamik polarizasyon eğrileri, açık devrepotansiyeli (ADP) ölçümleri ve kronoamperometridir.Deneysel sonuçlara göre, numunelerin özellikle lokalize korozyon özelliklerininbaşlıca çelik üzerindeki kaplama hatalarına, kaplama yüzeyinin üretimisonrasında ve polarizasyon aşamasında oksijen bağlama özelliğine vepolarizasyon derecesine bağlı olduğu belirlenmiştir.Her üç numune içinde TiN kaplamaların kaplama hatalarının bulunduğuyerlerde ileri derecede çukur korozyonu eğilimi gözlenirken CrN kaplamalardapolarizasyon sonucunda kaplama hatalarının önemli ölçüde pasifleştiğibelirlenmiştir. Paslanmaz çelik numunelerin ise yüzeyin her yerinde lokalizekorozyona uğradığı ve korozyon hızının ise polarizasyon derecesine bağlı olarakdiğer numunelerden 10-30 kat daha büyük olduğu bulunmuştur.Bilim Kodu : 708.3.028Anahtar Kelimeler : PVD, TiN, CrN, Korozyon, Paslanmaz ÇelikSayfa Adedi : 95Tez Yöneticisi : Prof. Dr. Muammer NALBANTDoç. Dr. Tülin KIYAK

Özet (Çeviri)

THE CORROSION FEATURES OF STAINLESS STEELS COATED WITHCRN AND TIN AND NON-COATED(M.Sc. Thesis)Mustafa UYSALGAZİ UNIVERSITYINSTITUTE OF SCIENCE AND TECHNOLOGYMay 2006ABSTRACTIn the literature, a sufficient study has not been encountered about thecorrosion features of TiN and CrN coated stainless steel. In this study corrosionbehaviour of coated AISI 304 stainless steel through the method of PVD hasbeen investigated.The electro chemical results of each steels were acquired under the conditions offree corrosion where over polarization in the 0,5 M NaCl was evaluated togetherwith the results of EDS, SEM, and ICP solution analysis. The electro chemicaltechniques used were semi stable potantiodynamic polarization curves, opencircuit potential (OCP) measures and cronoampermeter.According to the experimental results it localized corrosion features of thesamples mainly depend on the coating defects, oxygen binding features after theproduction of coating surface and at the stage of polarization and the degree ofpolarization.High degree of pitting corrosion tendency at coating defects after TiN coatingsexis on the supaces each of three samples. It has been evaluated that CrNcoatings are passive significantly at the end of polarization. Also it has beendetermined that localized corrosion voidely spready over the surface of stainlesssteel samples. Thus, the corrosion rate depends on the polarization degree is 10- 30 times higher than that of the other samples.Science Code : 708.3.028Key Words : PVD, TiN, CrN, Corrosion, Coatings, Stainless steelPage Number : 95Adviser : Prof. Dr. Muammer NALBANTDoç. Dr. Tülin KIYAK

Benzer Tezler

  1. Pvd kaplanmış biomalzeme olarak kullanılan AISI 316 L paslanmaz çeliğinin sodyum hyaluronat ve kuru ortamdaki aşınma davranışlarının incelenmesi

    Investigation of wear behavior in the sodium hyaluronate and in dry area of the pvd coated AISI 316 L stainless steel

    TAHSİN KAMIŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2017

    Makine MühendisliğiSelçuk Üniversitesi

    Makine Ana Bilim Dalı

    PROF. DR. HAYRETTİN DÜZCÜKOĞLU

  2. Kesici takımların fonksiyonel derecelendirilmiş TİCN ve TİBCN ile kaplanmasının karakterizasyonu

    Characterization of functionally graded TİCN and TİBCN coating of cutting tools

    CEM ERTEK

    Doktora

    Türkçe

    Türkçe

    2013

    Makine MühendisliğiYıldız Teknik Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. AYŞEGÜL AKDOĞAN EKER

  3. Nitrür esaslı seramik ince film kaplamaların deniz suyu ortamındaki tribokorozyon davranışlarının incelenmesi

    Investigation of tribocorrosion behaviour of nitride based ceramic thin film coatings in sea water

    SABRİ ALKAN

    Doktora

    Türkçe

    Türkçe

    2019

    DenizcilikBartın Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. MUSTAFA SABRİ GÖK

  4. İnce sert seramik kaplamaların kazımalı aşınma davranışları ile endüstriyel zımbalama işlemine uygulanması

    Fretting wear behavior of thin hard ceramic coatings with an application of industrial punching operation

    ALEV OSMA

    Doktora

    Türkçe

    Türkçe

    1999

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    PROF.DR. E. SABRİ KAYALI

  5. PVD yöntemi ile TiN, CrN ve TiN /CrN kaplanmış soğuk iş takım çeliğinin aşınma performanslarının deneysel incelenmesi

    Investgation of wear performance of TiN, CrN and TiN /CrN coated cold work steel by using physical vapour deposition (PVD) method

    NUSRETTİN KALKAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2008

    Metalurji MühendisliğiSelçuk Üniversitesi

    Makine Eğitimi Ana Bilim Dalı

    YRD. DOÇ. DR. HAYRETTİN DÜZCÜKOĞLU