Toz metalurjisi teknigi ile üretilen bir paslanmaz çelikte katkı elemanlarının asınma direncine etkileri
The effects of alloying elements over wear resistance in stainless steel material produced with powder metallurgy technique
- Tez No: 185315
- Danışmanlar: DOÇ. DR. MEHMET KORKUT
- Tez Türü: Doktora
- Konular: Eğitim ve Öğretim, Metalurji Mühendisliği, Education and Training, Metallurgical Engineering
- Anahtar Kelimeler: Toz metal, Ostenitik paslanmaz çelik, Mikroyapı, Karbürler, Adhesiv aşınma, Abrasiv aşınma, Tokluk, Powder metal, Austenitic stainless steel, Microstructure, Carbides, Adhesive wearing, Abrasive wearing, Toughness
- Yıl: 2006
- Dil: Türkçe
- Üniversite: Fırat Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 156
Özet
ÖZETDoktora TeziTOZ METALURJ TEKN Ğ LE ÜRET LEN B R PASLANMAZ ÇEL KTE KATKIELEMANLARININ AŞINMA D RENC NE ETK LERVAHDETT N KOÇFırat ÜniversitesiFen Bilimleri EnstitüsüMetal Eğitimi Anabilim Dalı2006 Sayfa:139Bu çalışmada, ostenitik paslanmaz çelik tozları içerisine % 1, 2 ve 3 oranlarında molibden,titanyum, kobalt ve bor elementlerinin tozları katılmış; toz metalurjisi tekniği kullanılarak birkompozit malzeme üretimi yapılmıştır. Tozlar soğuk olarak tek yönlü 18 ton'luk bir kuvvetlepreslenerek 1150 ºC'de sinterlenmiştir. Üretimi yapılan kompozit malzemenin mikroyapı, mekaniközellikleri, abrasiv ve adhesiv aşınma davranışları araştırılarak, içerisindeki alaşım elementi ve katkıyüzdesi oranları ile aşınma davranışı arasında ilişki kurulmaya çalışılmıştır.Üretimi toz metalurjisi tekniği ile yapılan kompozit malzemenin, katkı elementlerinin veoranlarının değişmesi ile mikro yapılarında da değişiklikler meydana gelmiştir. Ana matrisincelendiğinde tanelerin küçülmesi, tanelerin parçalanması, tane sınırlarının genişlemesi,çekirdeklenmeler v.b. olayların gerçekleştiği gözlemlenmiştir. Malzemelerin, mikroyapılarınınüzerinde yapılan incelemelerde mikroyapının esas itibarı ile γ-Fe, M23C6 ve M7C3 fazlarından oluştuğutespit edilmiştir.Araştırmalar sonucunda yapılan yeni kompozit malzemelerin, ostenitik paslanmaz çeliğinsertlik, mikrosertlik, tokluk özelliklerini katkı elementlerine ve katılan yüzde miktarlarına bağlı olaraketkilediği ve az çok değiştirdiği görülmüştür. Bütün numuneler göz önüne alındığında takviye ediciolarak kullanılan Mo, Ti, B ve Co elementlerinin ostenitik paslanmaz çeliklerin mekanik özellikleriniolumlu yönde etkilediğini söylemek mümkündür. En düşük yüzey sertliği ve mikro sertlik değerleritakviyesiz ostenitik paslanmaz çelik numunelerde görülmüştür. Üretilen kompozit malzemelerden eniyi mekanik ve aşınma özellikleri değeri bor elementi ile takviye edilmiş numunelerde sağlanırken;bunu sırası ile Ti, Mo ve Co ile takviye edilmiş numuneler izlemiştir.Yapılan çalışmada; ostenitik paslanmaz çeliğin sertliğini, mikrosertliğini, tokluğunu, abrasivve adhesiv aşınma dayanımını içerisine az oranda Mo, Ti, B, Co elementleri katarak değiştirmeninmümkün olduğu tespit edilmiştir. Katkı elementlerinin karbür, borür ya başka türden bileşik oluşturupoluşturmaması; matris içerisinde homojen ve dengeli dağılıp dağılmaması, kompozit malzemeninözelliklerini belirleyen en önemli faktörlerdir.
Özet (Çeviri)
ABSTRACTPhD ThesisTHE EFFECTS OF ALLOYING ELEMENTS OVER WEAR RESISTANCE IN STAINLESSSTEEL MATERIAL PRODUCED WITH POWDER METALLURGY TECHNIQUEVAHDETT N KOÇFırat UniversityGraduate School of Natural and Applied SciencesDepartment of Metallurgy Education2006, Page:139In this study, molybden, titanium, cobalt and boron elements were added to a austeniticstainless steel powder at the percentage of 1, 2 and 3 % and a composite material was produced by useof powder metallurgy techniques. The powder was pressed with 18 tons pressure and sintered at 1150°C temperature. Micro-structural and mechanical properties, abrasive and adhesive behaviours of theproduced composite material were investigated and tried to correlate between alloying elements andtheir percentage.The chanpes of the type and percentapes of alloying elements of composite material whichwere produced by powder metallurgy techniques resutted in the chanpes of the microstructures of thecomposites. When the matrix was examined, grain refinement, disintegration of grains, coarsening ofgrain boundaries, core forming etc. have been observed. It was also observed that the microstructuremainly consisted of γ-Fe, M23C6 and M7C3 phases.The investigations revealed that the alloying elements affected the hardness, microhardnessand toughness of composite austenitic stainless steel in proportion to to their percentage. When allsamples were examined, it was determined that the reinforcing elements (Mo, Ti, B and Co)positively affected the mechanical properties of austenitic stainless steel. The lowest surface hardnessand microhardness values were observed in unreinforced stainless steel samples. While the bestmechanical and wear properties were reached in the samples reinforced with boron, the samplesreinforced with Ti, Mo, and Co have not shown as good mechanical and wear properties as thespeciment reinforced with boron.In this study, it was show that it is possible to chance the hardness, microhardness, toughness,abrasive and adhesive wear resistance of austenitic stainless steel by adding Mo, Ti, B and Co. It wasalso pound that the formation of carbide, boride or any other compound and the disribution of thealloying additions in the matrix are the main factors determining the mechanical properties of thecomposite material.
Benzer Tezler
- TM yöntemiyle üretilmiş alüminyum esaslı SiCp takviyeli kompozit ile 304 paslanmaz çeliğin sürtünme kaynağıyla birleştirilebilirliğinin araştırılması
The investigation of weldability of al based SiCp reinforced composite, which is produced by PM method with 304 stainless steel by friction welding
ZÜLKÜF BALALAN
Doktora
Türkçe
2013
Metalurji MühendisliğiFırat ÜniversitesiMetal Eğitimi Ana Bilim Dalı
PROF. DR. NİYAZİ ÖZDEMİR
- The effect of Cr on microstructure and mechanical properties of 316L stainless steel used as implant material produced by powder metallurgy
Toz metalurjisi ile üretilen implant malzemesi olarak kullanılan 316L paslanmaz çeliklerin mikro yapısı ve mekanik özellikleri üzerine Cr'nin etkisi
FADHIL HUSSEIN OLEIWI
Yüksek Lisans
İngilizce
2023
BiyomühendislikKarabük ÜniversitesiBiyomedikal Mühendisliği Ana Bilim Dalı
DOÇ. DR. MEHMET AKİF ERDEN
DOÇ. DR. HÜSEYİN DEMİRTAŞ
- Grafen katkılı CuCr1Zr kompozit malzeme üretimi ve karakterizasyonu
Production and characterization of graphene added CuCr1Zr composite material
NİDA KURT
Yüksek Lisans
Türkçe
2021
Metalurji MühendisliğiSivas Cumhuriyet ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MEHMET KUL
- Thermal oxidation of titanium-based cold spray coatings for biological and wear-related applications
Biyolojik ve aşınmaya yönelik uygulamalar için soğuk dinamik gaz püskürtme tekniği ile üretilmiş titanyum bazlı kaplamaların termal oksidasyonu
DOĞUKAN ÇETİNER
Doktora
İngilizce
2022
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. HÜSEYİN ÇİMENOĞLU
PROF. DR. ERDEM ATAR
- Toz yataklı lazer ergitme yöntemiyle üretilen ınconel 718 süperalaşımının borlama işlemi sonrası karakterizasyonu
Characterization of inconel 718 superalloy produced by powder bed laser melting after boriding
UĞUR MOGAN
Yüksek Lisans
Türkçe
2023
Metalurji MühendisliğiManisa Celal Bayar ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. AHU ÇELEBİ
DR. ÖĞR. ÜYESİ İLYAS TÜRKMEN