Cd-Zn ve Cd-Sn ikili ötektik alaşımlarının doğrusal katılaştırılması

Directional solidificaion of the Cd-Zn and Cd-Sn binary eutectic alloys

  1. Tez No: 197259
  2. Yazar: HİCRAN YILDIRIM
  3. Danışmanlar: PROF.DR. MEHMET GÜNDÜZ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
  6. Anahtar Kelimeler: kili ötektik alaşımlar, katılaştırma, mikroyapı, Binary eutectic alloys, solidification, microstructure
  7. Yıl: 2005
  8. Dil: Türkçe
  9. Üniversite: Erciyes Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Fizik Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 92

Özet

Cd-Zn ve Cd-Sn K L ÖTEKT K ALAŞIMLARININ DOĞRUSALKATILAŞTIRILMASIHicran YILDIRIMErciyes Üniversitesi, Fen Bilimleri EnstitüsüYüksek Lisans Tezi, Ağustos 2005Tez Danışmanı: Prof. Dr. Mehmet GÜNDÜZÖZETBu çalışmanın amacı, mikroyapı parametresi olan λE (lameller arası mesafe)'nin˙büyütme hızı V ve soğutma hızı T gibi katılaştırma parametrelerinin fonksiyonu olarakdeğişimini incelemektir. Bu nedenle Cd-Zn ötektik alaşım sisteminden altı, Cd-Snötektik alaşım sisteminden ise beş numune farklı hızlarda doğrusal olarakkatılaştırılmıştır.Ötektik numunelerin hazırlanması için yüksek saflıktaki (%99,99) metallerin ağırlıkçaoranı ayarlandıktan sonra vakumlu eritme fırınındaki grafit potası içerisinde eritilmiştir.Daha sonra eriyik haldeki alaşım önceden sıcak döküm fırınına yerleştirilen grafitpotalarına (4mm iç çapında, 6,35mm dış çapında ve 200 mm uzunluğunda) dökülmüş vekatılaştırılmıştır. Sıcak döküm fırınından çıkartılan bir numune Bridgman tipi doğrusalkatılaştırma fırınına yerleştirilerek doğrusal olarak katılaştırılmıştır. Bu işlem aynısıcaklık gradyentinde (G), değişik katılaştırma hızlarında V (8-80) µm/s diğernumunelere de uygulanmıştır. Mikroyapıyı açığa çıkarmak için, hazırlanmış olannumuneler üzerine metalografik işlemler uygulanmıştır. Bu işlemlerden sonra λEdeğerlerini bulmak için numunelerin fotografları mikroskoba monte edilen fotografçekme ünitesi aracılığıyla çekilmiştir. Doğrusal kesişim metodu kullanılarak bu˙fotograflardan λE değerleri bulunmuştur. λE'nin V ve T 'ya göre değişimi ve bağlılığı˙lineer regresyon analizi yöntemi kullanılarak belirlenmiştir. V ve T 'nın artmasına bağlıolarak λE'nin azaldığı görülmüştür.Son olarak elde edilen deneysel sonuçlar, teorik model ve önceki deneysel sonuçlarlakarşılaştırılmış ve birbirleri ile uyum içerisinde oldukları gözlenmiştir.

Özet (Çeviri)

DIRECTIONAL SOLIDIFICATION of the Cd-Zn and Cd-Sn BINARYEUTECTIC ALLOYSHicran YILDIRIMErciyes University, Graduate School of Natural and Applied SciencesM.S. Thesis, August 2005Thesis Supervisor: Prof. Dr. Mehmet GÜNDÜZABSTRACTThe purpose of this work was to investigate the microstructural parameter λE (thelamellar spacing) as a function of the solidification parameters such as temperature˙growth rate V and cooling rate T . Therefore, six samples from Cd-Zn eutectic alloysystem and five samples from Cd-Sn eutectic alloy system were directionally solidifiedwith different V.The eutectic samples were prepared by melting weighed quantities of metals (99,99 %)high purity in a gpaphite crucible within a vacuum melting furnace. After the moltenalloy was poured into graphite crucibles ( 4 mm ID, 6,35 mm OD and 200 mm lenght)which were placed in the hot filling furnace and then directioanally solidified. Onesample which was taken from the filling furnace was positioned into the Bridgman typedirectional solidification furnace in order to directioanally solidified. The same processhas been applied to the other samples with different solidification V (8-80) µm/s in thesame G. After this process, the photographs of samples have been taken. In order toexamine the microstructure of the samples, metallographic processes have been carriedout on the directionally solidified samples. After this process, the photographs of thesamples were taken via photographic unit in order to find the values of λE. The value ofλE were found by means of applying linear intercept method on the photographs. The λEvalue was analysied by regression analysis. It has been found that λE decreases with the˙increasing values of V and T .Finally, the results obtained in this study have been compared with theoretical modelsand the previous experimental results. It has been observed that they were in agreement.

Benzer Tezler

  1. İkili ötektik alaşımların doğrusal katılaştırılması ve mekaniksel özelliklerinin incelenmesi

    Directional solidification of binary eutectic alloys and investigation of mechanical properties

    HASAN KAYA

    Doktora

    Türkçe

    Türkçe

    2001

    Fizik ve Fizik MühendisliğiGazi Üniversitesi

    Fizik Ana Bilim Dalı

    PROF.DR. ATİLLA ÖZMEN

  2. İkili metalik alaşımların katı-sıvı arayüzey enerjilerinin ölçümü

    The measurement of solid-liquid interface energy in binary metallic alloys

    BUKET SAATÇİ

    Doktora

    Türkçe

    Türkçe

    2000

    Fizik ve Fizik MühendisliğiErciyes Üniversitesi

    Fizik Ana Bilim Dalı

    PROF.DR. MEHMET GÜNDÜZ

  3. Synthesis of copper zinc tin sulfide CZT(S,Se) with solution based method and formation and characterization of CZT(S,Se) thin films for photovoltaic application

    Solüsyon yöntemiyle CZTS sentezi ve fotovoltaik devreler için CZTS ince film oluşturma ve film özelliklerini inceleme

    RIDVAN ERĞUN

    Yüksek Lisans

    İngilizce

    İngilizce

    2015

    Enerjiİstanbul Teknik Üniversitesi

    Nanobilim ve Nanomühendislik Ana Bilim Dalı

    DOÇ. DR. ELİF ÜLKÜ ARICI

  4. Orta toroslardaki kızıltepe (Bolkardağı-Ulukışla-Niğde) altın- gümüş-çinko-kurşun yatağının bazı jeolojik, mineralojik ve jeokimyasal özelliklerinin incelenmesi

    Investigon of some geoligical, mineralogical and geochemical properties of kiziltepe (Bolkardaği-Ulukişla-Niğde) gold-si̇lver-zi̇nc-lead deposit in the central taurus belt

    MEHMET GÜLTEKİN

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Jeoloji MühendisliğiKonya Teknik Üniversitesi

    Jeoloji Mühendisliği Ana Bilim Dalı

    PROF. DR. ŞUAYİP KÜPELİ

  5. Saray (Tekirdağ) ve Pınarhisar (Kırklareli) kömürlerinin sülfür ve iz element içeriğinin kökeni ve kömürlerin çevresel etkisinin hidrojeokimyasal açıdan değerlendirilmesi

    The origin of the sulfur and trace elements of the Saray (Tekirdağ) and Pinarhisar (Kirklareli) coals and evaluation of environmental effects on hydrogeochemistry

    CEMİLE ERARSLAN

    Doktora

    Türkçe

    Türkçe

    2018

    Jeoloji Mühendisliğiİstanbul Teknik Üniversitesi

    Jeoloji Mühendisliği Ana Bilim Dalı

    PROF. DR. YÜKSEL ÖRGÜN TUTAY