Bor fosfat katkılı termal şoka dayanıklı seramikler

Thermal shock resistant ceramic with borane phosphote addetive

PDF İndir

  1. Tez No: 212770
  2. Yazar: ALİ SACİD AĞIR
  3. Danışmanlar: PROF. DR. METİN GÜRÜ, YRD. DOÇ. DR. BÜLENT BARAN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya Mühendisliği, Seramik Mühendisliği, Chemical Engineering, Ceramic Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2007
  8. Dil: Türkçe
  9. Üniversite: Gazi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: İleri Teknolojiler Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 95

Özet

Bu çalışma; 2003K120470?07 kodlu, ?Termal şoka dayanıklı, bor fosfat katkılı, hızlı pişirimle elde edilen seramiklerin üretimi? adlı DPT tarafından desteklenen projeye katkı amacıyla çalışılmıştır. Bu çalışmada termal şoka dayanabilen seramik türü olarak kordierit ve anorthit fazları seçilmiştir. İlk olarak daha sonra hazırlanacak karışımlarda kullanılmak üzere borofosfat sentezi gerçekleştirilmiştir. Elde edilen bor fosfat 1000oC `da kalsine edilmiş ve XRD, Kimyasal Analizleri ile karekterize edilmiştir. Diğer yandan (MgO, Al2O3, SiO2) faz diyagramında kordierit fazını en çok kapsayan ve kordieritin oluşabildiği en düşük sıcaklıktaki uygun ötektik noktalar seçilmiştir. Seçilen bu noktaların bileşimleri kaolin, talk, alumina hammaddelerine göre hesaplanmış ve karışımlar hazırlanmıştır. Kordierit için hazırlanan 7 adet karışım iki eşit kısma ayrılmış ikinci kısımlarına %10 BPO4 ilavesi yapılmıştır. Benzer çalışma (CaO, Al2O3,SiO2) faz diyagramında anorthit fazı için de yapılmış ve wollastonit, kaolinit, kalsit kullanılarak 6 adet karışım hazırlanmıştır. Elde edilen 6 adet karışım iki kısma ayrılmış ve yine ikinci kısımlara % 10 BPO4 ilavesi yapılmıştır. Karışımlar presle aynı basınçta şekillendirilmiş ve aynı koşullarda ve aynı ısıtma hızıyla v elektrikli fırında kordierit için 1100, 1150, 1200, 1250, 1300, 1350 anorthit için 1000, 1050, 1100, 1150, 1200,1250 oC'a pişirmiştir. Örneklere pişmeden önce DTA ve TG analizleri pişen örneklere ise X ışını kırınımı analizleri uygulanmıştır. Anahtar Kelimeler : Kordierit, Anorthite, BPO4, Termal şok, Genleşme katsayısı, Hızlı pişirim, Sıvı faz sinterleşmesi, Ötektik

Özet (Çeviri)

This study was performed for 203K120470-07 coded, ?Manufacture of ceramic that has thermal shocked strength, boron fosfat additive, formed according to fast firing? named DTP supported Project. Kordierite and anorthite phases was choosen as thermal shocked strength ceramic types. First of all, boronfosfat was synthesised to use following step. Synthesised boronfosfat was calcined at 1000 OC and its charactarization analysis were performed using XRD and Chemical Analysis. On the other hand, suitable eutectic point of minimum temperature that is the most inclued the kordierte phase and forming cordierte at (MgO, Al2O3, SiO2) phase diagram was choosen. Composition of these choosen points are calculated according to kaoline, talc, alumina raw materials and mixtures are prepared. 7 mixtures that prepared for kordierte, were splited in two equal parts, for its second part %10 BPO4 was added. Likeness study was performed for anorhite phase at (CaO, Al2O3, SiO2) phase diagram and using wallostonite, kaolinit, calsite, 6 mixture was formed. Prepared 6 mixture were splited two parts and %10 BPO4 was added again in vii second part. Mixture was shaped with pressing at the same pressure and fired using electric furnace at and same condition and the same heating shedule for cordieritre 1100, 1150, 1200, 1250, 1300, 1350 and for anorthite 100, 1050, 1100, 1150, 1200, 1250 OC. Before firing DTA and TG analysis were applied for samples and X-ray diffraction analysis were applied for firing samples. Key Words : Cordierite, Anorthite, BPO4, Thermal shock, Expansion Coefficient, Fast Firing, Liquid Phase Sintering, Eutectic

Benzer Tezler

  1. Tez No

    246307

    Bor katkılı demir fosfat camlarının sentezi ve özellikleri

    Synthesis and properties of boron doped iron phosphate glasses

    BURCU YÜCE

    Yüksek Lisans

    Türkçe

    Türkçe

    2009

    Fizik ve Fizik MühendisliğiKafkas Üniversitesi

    Fizik Bölümü

    PROF. DR. MEVLÜT KARABULUT

  2. Tez No

    819688

    Proton değişim membranlı yakıt pilleri için membran sentezi ve karakterizasyonu

    Synthesis and characterization of the membranes for proton exchange membrane fuel cells

    AYGÜN ÇALI

    Doktora

    Türkçe

    Türkçe

    2023

    Kimya MühendisliğiGazi Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. İRFAN AR

  3. Tez No

    882894

    Development of a bioactive glass-ceramic co-doped with lanthanum and boron and its biological in vitro studies for bone regeneration applications

    Lantan ve bor katkılı biyoaktif cam seramik geliştirilmesi ve kemik rejenerasyonu uygulamaları için in-vitro biyolojik çalışmaları

    RIHAB BADRADDIN SHUKUR AL-AKASHI

    Yüksek Lisans

    İngilizce

    İngilizce

    2024

    Mühendislik BilimleriKarabük Üniversitesi

    Biyomedikal Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ERKAN KOÇ

  4. Tez No

    198422

    Hegzagonal bor nitrür toz sentezi ve sinterleme davranışları

    Hexagonal boron nitride powder synthesis and sintering behaviours

    İRFAN TÖRE

    Doktora

    Türkçe

    Türkçe

    2006

    Seramik MühendisliğiAnadolu Üniversitesi

    Seramik Mühendisliği Ana Bilim Dalı

    PROF. DR. NURAN AY

  5. Tez No

    374086

    Hafniyum katkılı demir borofosfat camlarının yapısı ve özellikleri

    Structural features of hafnium containing borophosphate glasses

    CENK AYDIN

    Yüksek Lisans

    Türkçe

    Türkçe

    2014

    Fizik ve Fizik MühendisliğiKafkas Üniversitesi

    Fizik Ana Bilim Dalı

    PROF. DR. MEVLÜT KARABULUT

Geri Dön