Betonarme yapılarda dual-faz çeliğinin kullanılabilirliğinin ve korozyon direncinin araştırılması

An investigation on the usability and corrosion resistance of the dual-phase steel in the reinforced concrete structures

  1. Tez No: 232118
  2. Yazar: OĞUZHAN KELEŞTEMUR
  3. Danışmanlar: PROF. DR. MUSTAFA AKSOY, YRD. DOÇ. DR. SERVET YILDIZ
  4. Tez Türü: Doktora
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2008
  8. Dil: Türkçe
  9. Üniversite: Fırat Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Yapı Eğitimi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 128

Özet

Bu tez çalışmasında, inşaat sektörünün temel yapı malzemesi olan ve yurdumuzda bol miktarda üretilen düşük karbonlu SAE1010 inşaat çeliğinden dual-faz çeliği üretilerek, elde edilen bu çeliğin mekanik özellikleri ve beton içerisindeki korozyon davranışı üzerine temperleme ısıl işleminin etkisi incelenmiştir.İnşaat çeliğine, (?+?) bölgesinde 20, 40 ve 60 dk süre ile ostenitleme yapıldıktan sonra buz+su karışımında su verilerek farklı martenzit hacim oranlarına sahip dual-faz çelikleri elde edilmiştir. Daha sonra bu dual-faz çelikleri 200, 300 ve 400 oC sıcaklıklarda 45 dk süre ile temperlenerek sakin havada soğutulmuştur. Elde edilen dual-faz çeliklerinin metalografik incelemeleri tamamlandıktan sonra, çekme dayanımı, akma dayanımı, kesit daralması, toplam uzama, rezilyans modülü ve tokluk gibi mekanik özellikleri geniş bir biçimde incelenmiştir. Ayrıca kırılan yüzeyler taramalı elektron mikroskobu (SEM) ile incelenerek kırılmanın türü belirlenmiştir. Elde edilen dual-faz çeliklerinin mekanik özelliklerinin yanı sıra beton içerisindeki korozyon davranışları da belirlenmiştir.Çalışma neticesinde, dual-faz çeliklerinin mekanik özelliklerinin martenzit fazının sertliğine ve oranına bağlı olarak değiştiği gözlenmiştir. Temperleme ısıl işlemine bağlı olarak bu çeliklerin çekme, akma ve rezilyans modülü değerlerinin düştüğü, uzama, kesit daralması ve tokluk değerlerinin ise arttığı belirlenmiştir. Ayrıca, dual-faz çeliklerinin beton içerisindeki korozyon direncinin elde edildikleri ferritik-perlitik çelikten daha düşük olduğu ve temperleme ısıl işlemi ile korozyon direncinin daha da azaldığı tespit edilmiştir.

Özet (Çeviri)

In this dissertation study, SAE1010 structural carbon steel, which is the fundamental construction material of construction industry and wide range of product in our country, has been studied as dual phase steel by applying appropriate heat treatment and its mechanical properties and corrosion behavior in the concrete have been investigated for various tempering conditions.Dual-phase steel having different martensite volume ratio has been obtained by applying different quenching conditions; its (?+?) structure, which is obtained over A1 temperature by heating, is immersed into the ice+water medium and then it is annealed for various duration; 20, 40 and 60 minutes. Additionally, these dual-phase steels have been tempered at 200, 300 and 400 oC for 45 minutes and then cooled to the room temperature. Mechanical properties such as tensile strength, yielding strength, reduction of cross sectional area, total elongation, resilience modulus and toughness have been determined and metallographic examination of the steels has been done. In addition, fractographic examination has been studied with Scanning Electron Microscope (SEM) as well as their corrosion behavior in concrete.It is observed that mechanical properties of dual-phase steel have changed according to the hardness and ratios of martensite phases. Tensile strength, yield strength and resilience modulus of the steels have reduced, the total elongation, reduction of the cross sectional area and toughness have been increased upon to the tempering heat treatment. However, corrosion resistance of dual-phase steel in concrete decreases comparing to that of ferritic-perlitic structure and corrosion resistance have reduced with tempering heat treatment.

Benzer Tezler

  1. Çok katlı betonarme yapılarda farklı sismik izolatör sistemlerin ve kat adetinin deprem davranışına etkisi

    Başlık çevirisi yok

    HAKAN ABDULHAMİT TÜRK

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    İnşaat MühendisliğiKonya Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MURAT ÖZTÜRK

  2. Aktif ve pasif yapı kontrolü

    Active and passive structural control systems

    ÖZGÜL ZOBU

    Yüksek Lisans

    Türkçe

    Türkçe

    1997

    İnşaat Mühendisliğiİstanbul Teknik Üniversitesi

    Yapı Ana Bilim Dalı

    DOÇ. DR. A. NECMETTİN GÜNDÜZ

  3. Sanayii yapılarında üretim rolü ve idare bölümü arasındaki biçimleniş özellikleri

    Formal properties between the production hall and the adminstration section in the industrial buildings

    ÖMER ÇAMOĞLU

    Yüksek Lisans

    Türkçe

    Türkçe

    2001

    Mimarlıkİstanbul Teknik Üniversitesi

    Mimarlık Ana Bilim Dalı

    PROF. DR. METE S. ÜNÜGÜR

  4. Betonarme çerçevelerin özel köşe çaprazları ile güçlendirilmesi

    Retrofitting reinforced concrete frames by special knee braces

    KIVANÇ TAŞKIN

    Doktora

    Türkçe

    Türkçe

    2011

    İnşaat Mühendisliğiİstanbul Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. H. FARUK KARADOĞAN

    PROF. DR. NESRİN YARDIMCI

  5. Perde-çerçeve betonarme sistemlerde deprem etkisi altında doğrusal olmayan davranışın incelenmesi

    Nonlinear behavior of reinforced concrete dual structural systems subjected to earthquake excitation

    MEHMET BURAK YILMAZ

    Doktora

    Türkçe

    Türkçe

    2014

    Deprem Mühendisliğiİstanbul Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. ZEKAİ CELEP