Ötektik üstü yüksek kromlu beyaz dökme demirin iç yapı, aşınma ve darbe direnci özelliklerine 'tibal'in etkisi

The effect of 'tibal' on microstructure, wear and notch toughness of hyperotectic high chromium white cast irons

PDF İndir

  1. Tez No: 232117
  2. Yazar: ERHAN KERKÜT
  3. Danışmanlar: PROF. DR. MUSTAFA AKSOY
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Ötektik Üstü Yüksek kromlu Beyaz Dökme Demirler, Asılama, Asınma direnci, Hypereutectic High Chromium White Cast Irons, Inoculation, Wear Resistance
  7. Yıl: 2008
  8. Dil: Türkçe
  9. Üniversite: Fırat Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 115

Özet

Bu çalısmada iki farklı kompozisyondaki ötektik üstü yüksek kromlu beyaz dökme demiriniçyapı ve mekanik özelliklerine TiBAl asılayıcısı ve ısıl islemin etkileri incelenmistir. Numuneler%4.21 C , %17,2 Cr, %2.51 Mo ve %4.22C, %23.9Cr olmak üzere iki farklı kompozisyondaüretilmistir. Numunelerin mikroyapı incelemeleri optik ve taramalı elektron mikroskoplarındayapılmıstır. Faz ve karbürlerin tayini için matris ve karbürlerden analizler alınmıstır. Asınmadeneylerinde üç farklı yük (10N, 20N ve 30N) kullanılmıstır. Deney 10X10 mm lik sabit yüzeyalanına sahip numunelere uygulanmıstır. Asındırıcı olarak 180 mm çapındaki taslama tasıkullanılmıstır. Numunelerin agırlık kayıpları deney esnasında 10-5 hassasiyetli terazide tartılarak tepsiedilmistir. Sertlik deneyinde numunelerin her birinden en az üç ölçüm alınmıs ve ortalama degerleritespite edilmistir. Darbe deneyinde 10X10X50 mm boyutlarında V-çentikli numuneler hazırlanmıstır.Numunelerden elde edilen sonuçlar Fırat Üniversitesi Metalurji ve Malzeme Mühendisligilaboratuarlarındaki Darbe Deney cihazında tespit edilmistir. Numuneler sabit sıcaklıkta (1000 oC) 1 ve2 saat olmak üzere iki farklı ısıl isleme tabi tutulmustur. Sonuç olarak farklı iki kompozisyona sahipnumunelere uygulanan farklı orandaki asılayıcı ve ısıl islemler sonucunda en iyi asınma direncini%1TiBAl ilave edilmis Mo içerikli ısıl islem görmemmis numune verirken, en kötü asınma direncini%3 TiBAl ilave edilmis Mo içermeyen 2 saat ısıl islemli numune vermistir.

Özet (Çeviri)

In this study the effects of TiBAl inoculants and heat treatments on microstructure andmechanical properties of hypereutectic high chromium white cast irons having two different chemicalconcentrations were studied. The samples having 4.21% C , 17.2% Cr, 2.51% Mo and 4.22% C,23.9% Cr were produced in two different chemical concentration. The microstructures of the sampleswere investigated by optical microscope and Scanning Electron microscopy (SEM). The chemicalconcentration of matrix and carbides were determined by EDS to detect the type of carbides andmatrix. Three different loads (10N, 20N and 30N) were used on a wear surface having 10X10 mm areaduring abrasive wear tests. The weight loss of samples was obtained by using a balance having 10-5 grsensitivity. The surface hardness of the samples was measured as HRC and average of threemeasurements. The toughness of the samples having the sizes of 10X10X50 mm was evaluated byusing Charpy V-notch specimens. The heat treatments were applied to the samples as (1000 oC)- 1 and2 h. Finally, the application of heat treatments and inoculations was shown that the best wearresistance was obtained for the samples having 1%TiBAl and Mo additions and as-cast condition. Theworst wear resistance was obtained from the sample having heat treatment (1000 oC-2h), 3%TiBAland without Mo additions.

Benzer Tezler

  1. Tez No

    771542

    Ötektiküstü yüksek kromlu beyaz dökme demirlerde Ce ve B elementlerinin mikroyapı üzerindeki etkileri

    The effects of Ce and B elements on the microstructure ofhypereutectic high chromium white cast iron

    HASAN KAYA

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    Makine MühendisliğiTekirdağ Namık Kemal Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. İBRAHİM SAVAŞ DALMIŞ

    PROF. DR. SERDAR OSMAN YILMAZ

  2. Tez No

    411275

    Yüksek enerjili bilyeli öğütme tekniği ile üretilen ötektik üstü Al-Si-Fe alaşımlarının yapı ve mekanik özelliklerinin incelenmesi

    Investigation of structural and mechanical properties of hypereutectic Al-Si-Fe alloys rpoduced by high energy ball milling technique

    SİBEL GÜL

    Yüksek Lisans

    Türkçe

    Türkçe

    2015

    Fizik ve Fizik MühendisliğiGaziosmanpaşa Üniversitesi

    Fizik Ana Bilim Dalı

    PROF. DR. ORHAN UZUN

  3. Tez No

    432958

    Semi-solid slurry production for thixocasting

    Tiksodöküm için yarı-katı malzeme üretimi

    ZEYNEP ÖZDEMİR

    Yüksek Lisans

    İngilizce

    İngilizce

    2016

    Metalurji MühendisliğiMarmara Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. ALTAN TÜRKELİ

  4. Tez No

    200182

    AISI 4142 çeliğinin ısıl işlem ve ergitme yöntemleriyle yüzey modifikasyonu sonucu mekanik davranışlarının incelenmesi

    The examination of mechanical properties of 4142 steel after surface modification by smelting arc welding (SMAW)

    ABDULAZİZ KOÇ

    Yüksek Lisans

    Türkçe

    Türkçe

    2007

    Metalurji MühendisliğiFırat Üniversitesi

    Metalurji Eğitimi Ana Bilim Dalı

    YRD. DOÇ. DR. TÜLAY YILDIZ

  5. Tez No

    364002

    Seramik kalıba dökülerek üretilen Sn-Zn alaşımlarının mikro yapı ve mekanik özelliklerinin incelenmesi

    Investigation of microstructure and mechanical properties of Sn-Zn alloys which are poured into the ceramic mold

    BEKİR YAVUZER

    Yüksek Lisans

    Türkçe

    Türkçe

    2014

    Mühendislik BilimleriKarabük Üniversitesi

    İmalat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. DURSUN ÖZYÜREK

Geri Dön