Siyah karbonun bitümlü sıcak karışımların özelliklerine etkisinin araştırılması

Research on the effect of carbon black on the features of hot mix asphalt

PDF İndir

  1. Tez No: 237897
  2. Yazar: TACETTİN GEÇKİL
  3. Danışmanlar: YRD. DOÇ. DR. TANER ALATAŞ
  4. Tez Türü: Doktora
  5. Konular: İnşaat Mühendisliği, Civil Engineering
  6. Anahtar Kelimeler: Siyah karbon, Asfalt, Bitümlü sıcak karışım, Superpave yöntemi, Performans sınıfı, Modifiye bitüm, Modifiye karışım, Carbon black, Asphalt, Hot mix asphalt, Superpave method, Performance grade, Modified bitumen, Modified mixture
  7. Yıl: 2008
  8. Dil: Türkçe
  9. Üniversite: Fırat Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 273

Özet

Bu tez çalışmasında, siyah karbonun (SK) bir katkı maddesi olarak bitüm ve bitümlü sıcak karışımların (BSK) performansı üzerinde sağladığı iyileştirmeler, Superpave bağlayıcı şartnamesi ve karışım dizaynı çerçevesinde incelenerek kullanılabilirliği araştırılmıştır.Bu amaçla, Elazığ için son 20 yılın hava sıcaklıkları alınarak, SHRP yöntemine göre bağlayıcı performans sınıfı PG 64?22 olarak belirlenmiştir. PG 64?22 (B 70/100) ana bağlayıcısı esas alınarak, bu bağlayıcı derecesinde bir modifiye bağlayıcı elde edebilmek amacıyla PG 58?28 (B 160/220) bağlayıcısına %5, %10 ve %15 SK ilave edilerek modifiye bağlayıcılar elde edilmiştir. Saf ve modifiye bağlayıcıların özellikleri; dinamik kayma reometresi (DSR), kiriş eğme reometresi (BBR), dönel viskozimetre (RV) ve termogravimetrik analiz (TGA) deneyleri ile incelenmiştir. Daha sonra Elazığ için bir dizayn agrega gradasyonu oluşturularak saf ve SK modifiyeli bağlayıcılarla karışım numuneleri hazırlanmış ve SK'un bitümlü sıcak karışımların performansı üzerindeki etkileri; dolaylı çekme mukavemeti (ITS) ve nem hassasiyeti, dolaylı çekme esneklik modülü (ITSM) ve sünme sertliği deneyleri ile incelenmiştir. Bağlayıcıların DSR, BBR, RV ve TGA deneyleri sonucunda; saf B 160/220 (PG 58?28) bağlayıcısına göre, SK ilavesiyle bağlayıcının yüksek sıcaklık performans sınıfının yükseldiği, viskozite değerlerinde ve bozulma sıcaklıklarında önemli artışlar olduğu görülmüştür. Ayrıca, genel olarak uygulama bölgesi performans derecesine eşit modifiye bağlayıcının, %10 SK ilavesiyle elde edildiği ve bu oranın bağlayıcı rijitliğinin artmasında etkili olduğu görülmüştür. Karışım deneyleri sonucunda, dolaylı çekme mukavemeti oranındaki en büyük artış miktarı %10 SK katkılı, dolaylı çekme mukavemetleri bakımından ana bağlayıcılı karışıma eşdeğer kabul edilebilecek karışım %10 SK katkılı, esneklik modülü değeri bakımından ana bağlayıcılı karışıma eşdeğer kabul edilebilecek karışım, %15 SK katkılı modifiye karışımlardan elde edilmiştir. Sünme sertliği değeri bakımından ana bağlayıcılı karışıma eşdeğer kabul edilebilecek karışım, 40 oC sıcaklık için yaklaşık %2 SK katkılı; 60 oC sıcaklık için %10 SK katkılı modifiye karışımlarından elde edilebileceği görülmüştür.Çalışma sonucunda, bağlayıcıların SK ilavesiyle sertleştiği ve sıcaklık hassasiyetlerinin düştüğü; bu bağlayıcılarla hazırlanan karışımların yorulma direnci, kohezyon ve durabilitesinin iyileşerek deformasyonlara ve su tesirlerine karşı mukavemetinin arttığı görülmüştür.

Özet (Çeviri)

In this thesis, the improvements made by carbon black (CB) as an additive in the performance of bitumen and hot mix asphalt (HMA) and its employability were analyzed by researching within the terms of Superpave binder specification and the mixture design.To this end, getting air temperatures of past twenty years in Elazığ, binder performance grade was determined as PG 64-22 according to SHRP method. Based on PG 64-22 main binding, modified binders were obtained by adding 5%, 10% and 15% SK to PG 58-28 (B 160/220) binder in order to get a modified binder on the level of this binder. The features of pure and modified binders were analyzed by dynamic shear rheometer (DSR), bending beam rheometer (BBR), rotational viscometer (RV) and thermogravimetric analysis (TGA) experiments. Afterwards, forming a design aggregate gradation for Elazığ, mixture samples were prepared with pure and SK-modified binders, and the effects of SK on the performance of bituminous hot mixtures with indirect tensile strength (ITS) and moisture susceptibility, indirect tensile stiffness modulus (ITSM) and creep stiffness experiments. As a result of DSR, BBR, RV and TGA experiments of binders, according to pure B 160/220 (PG 58-28) binder, it was observed that high-temperature performance grade of the binder increased with SK addition, and there were significant increases in viscosity value and degradation temperatures. In addition, it was found that the modified binder generally equal to application area performance level was obtained by 10% SK addition and this rate was effective in the rise of binder stiffness. As a result of mixture experiments, maximum increase in indirect tensile strength rate was obtained from modified mixtures with 10% SK, the mixture that could be accepted as equal to the mixture with main binding in terms of indirect tensile strength was obtained from modified mixtures with 10% SK and the mixture that could be accepted as equal to the mixture with main binders in terms of stiffness modulus was obtained from modified mixtures with 15% SK. It was observed that the mixture which could be accepted as equal to the mixture with main binder in terms of creep stiffness could be obtained from modified mixtures with 2% SK at 40oC and modified mixtures with 10% SK at 60oC.At the end of the study, it was found that binders hardened and temperature sensitivity decreased; the fatigue resistance, cohesion and durability of the mixtures prepared with these binders improved and their strength against permanent deformations and water effects increased.

Benzer Tezler

  1. Tez No

    650212

    Nano zirkonyum dioksit ve piroliz yöntemi ile elde edilen siyah karbonun bitümün modifiye edilmesinde kullanılması ve reolojik özelliklerinin incelenmesi

    The use of black carbon obtained by nano zirconium dioxide and pyrolysis in the modification of bitumin and investigation of the reological properties

    MUSTAFA AKBULUT

    Yüksek Lisans

    Türkçe

    Türkçe

    2020

    UlaşımErzurum Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MUHAMMED YASİN ÇODUR

  2. Tez No

    666471

    Atık lastiklerden elde edilen siyah karbonun bitüm ve bitümlü sıcak karışımlara etkisi

    The effect of black carbon obtained from waste tires on bitumen and bitumen hot mixtures

    ZÜLFÜKAR AKSAĞAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Ulaşımİnönü Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. TACETTİN GEÇKİL

  3. Tez No

    587651

    İstanbul'da siyah karbonun zamansal değişiminin ve çevresel parametrelerle ilişkisinin belirlenmesi

    Determinaton of the temporal variatons of black carbon and relation to the enviromental parameters in Istanbul

    ÖZCAN AKIN

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Çevre Mühendisliğiİstanbul Üniversitesi-Cerrahpaşa

    Çevre Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ÜLKÜ ALVER ŞAHİN

  4. Tez No

    268382

    Aydın ilindeki zeytin bahçelerinin pestisitlerin pasif birikimi açısından araştırılması ve bölgenin haritalanması

    Passive accumulation of pesticides in olive gardens in Aydın province and mapping of the region for organic farming

    DUYGU ATEŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2010

    ZiraatNamık Kemal Üniversitesi

    Bitki Koruma Ana Bilim Dalı

    DOÇ. DR. CAFER TURGUT

    PROF. DR. NURAY ÖZER

  5. Tez No

    884280

    İndirgen ortamda sırsız siyah seramikler ve Karacasu kilinden uygulamalar

    Unglazed black ceramics in a reducing atmosphere and applications from Karacasu clay

    KADİR ERTÜRK

    Sanatta Yeterlik

    Türkçe

    Türkçe

    2024

    Güzel SanatlarDokuz Eylül Üniversitesi

    Seramik ve Cam Tasarımı Ana Sanat Dalı

    PROF. HALİL YOLERİ

Geri Dön