Living radical polymerization of hydroxyethyl methacrylate and its block copolymerization with poly(dimethyl siloxane) macroazoinitiator

Hidroksietil metakrilatın yaşayan radikal polimerleşmesi ve poli(dimetil siloksan) makrobaşlatıcı ile blok kopolimerleşmesi

  1. Tez No: 238247
  2. Yazar: ELİF VARGÜN
  3. Danışmanlar: PROF. DR. ALİ USANMAZ
  4. Tez Türü: Doktora
  5. Konular: Polimer Bilim ve Teknolojisi, Polymer Science and Technology
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2009
  8. Dil: İngilizce
  9. Üniversite: Orta Doğu Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Polimer Bilim ve Teknolojisi Bölümü
  12. Bilim Dalı: Polimer Bilim ve Teknolojisi Ana Bilim Dalı
  13. Sayfa Sayısı: 166

Özet

Hidrofilik poli(2-hidroksietil metakrilat), PHEMA, ve hidrofobik poli(dimetil siloksan), PDMS segment içeren kopolimerler biyomalzeme olarak sıklıkla kullanılır. Bu amfifilik kopolimerler ayrıca polimer çözeltilerinde emülsiyonlaştırıcı ve polimer karışımlarında uyum sağlayıcı olarak kullanılmaktadır. Bu amaçla, HEMA'nın radyasyonla çözelti polimerleşmesi, ATRP ve RAFT metotları çalışıldı. Radyasyonla sulu çözelti polimerleşmesi ile elde edilen PHEMA'nın ısıl bozunma mekanizması detaylıca çalışıldı. DSC, TGA ve Kütle Spektroskopisi analizleri bozunmanın, bağlanma ve monomer parçalanması ile depolimerleşme şeklinde olduğunu gösterdi. HEMA'nın ATRP polimerleşmesi etil-2-bromoizobutirat (EBriB) başlatıcı ve CuCl/bipiridin katalizörü ile MEK/1-propanol çözücü karışımında yapıldı. Cu(II) kompleksleri ve ATRP ile elde edilen PHEMA polimerleri UV-vis, FTIR and 1H-NMR teknikleriyle karakterize edildi. Ayrıca, HEMA RAFT yöntemiyle farklı [RAFT]/[AIBN] oranlarında ve üç farklı çözücüde (metil etilketon, etil asetat ve toluen) polimerleştirildi. HEMA'nın [RAFT]/ [AIBN]= 18 oranında, 80 oC de MEK ve etil asetat çözücülerinde kontrollü polimerleşmesi yüzde 40 dönüşüme kadar birinci dereceden kinetik göstermiştir. Makrobaşlatıcı PDMS-MAI iki fonksiyonlu PDMS'den sentezlenmiş ve daha sonra MMA, EMA, HEMA and TMS-HEMA monomerleri ile kopolimerleştirilmiştir. Blok kopolimerlerin karakterizasyonunda FTIR, 1H-NMR, katı faz NMR, GPC, XPS, SEM ve DSC gibi farklı yöntemler kullanılmıştır. P(DMS-b-TMSHEMA) kopolimeri P(DMS-b-HEMA) blok kopolimerine silil grupların uzaklaştırılması yoluyla dönüştürülmüştür. P(DMS-b-MMA) ve P(DMS-b-EMA) kopolimerlerinden farklı olarak P(DMS-b-HEMA) kopolimerinde fazlara ayrılmış bir morfoloji görülmüştür.

Özet (Çeviri)

Hydrophilic poly(2-hydroxyethyl methacrylate), PHEMA, and hydrophobic poly(dimethyl siloxane), PDMS, segments containing copolymers have been widely used as a biomaterial. These amphiphilic copolymers also used as an emulsifying agent in polymer solutions and compatibilizer in polymer blends. In this case, solution polymerizations of HEMA by radiation, ATRP and RAFT methods were studied. The thermal degradation mechanism of PHEMA, which was prepared in aqueous solution by gamma radiation technique, was studied in detail. The DSC, TGA and Mass Spectroscopy analyses revealed that the degradation is linkage and depolymerization with a combination of monomer fragmentation. The ATRP of HEMA was performed with ethyl-2-bromoisobutyrate (EBriB) initiator and CuCl/bipyridine catalyst in MEK/1-propanol solvent mixture. Cu(II) complexes and PHEMA obtained via ATRP were characterized by UV-vis, FTIR and 1H-NMR analysis. The RAFT polymerization of HEMA with different [RAFT]/[AIBN] ratios were also investigated in three solvents (methyl ethylketone, ethyl acetate and toluene). The controlled polymerization of HEMA with the ratio of [RAFT]/ [AIBN]=18 at 80 oC in MEK and ethyl acetate, shows the first-order kinetic up to the nearly 40 % conversion Macroazoinitiator PDMS-MAI was synthesized from bifunctional PDMS and then copolymerized with MMA, EMA, HEMA and TMS-HEMA monomers Different characterization methods such as FTIR, 1H-NMR, solid state NMR, GPC, XPS, SEM, DSC, etc. have been used for the characterization of block copolymers. P(DMS-b-TMSHEMA) was converted to the P(DMS-b-HEMA) block copolymer by deprotection of TMS groups. The phase separated morphology was observed for the P(DMS-b-HEMA) copolymer, which was different from P(DMS-b-MMA) and P(DMS-b-EMA) copolymers.

Benzer Tezler

  1. Synthesis of 3,5-bis(perfluorobenzyloxy)benzyl acrylate containing polymers

    3,5-bis(perflorobenziloksi)benzil akrilat içeren polimerlerin sentezi

    TUBA ÇAKIR ÇANAK

    Doktora

    İngilizce

    İngilizce

    2012

    Polimer Bilim ve Teknolojisiİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    PROF. DR. İ. ERSİN SERHATLI

  2. Yüksek performanslı sıvı kromatografisi için farklı polaritelere sahip, fonksiyonel gruplu kolon dolgu materyallerinin sentezi ve kromatografik karakterizasyonu

    The synthesis and chromatographic characterization of functionalized column packing materials with different polarities for high performance liquid chromatography

    ENDER ÜNSAL

    Doktora

    Türkçe

    Türkçe

    2006

    BiyoteknolojiHacettepe Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF.DR. SÜLEYMAN ALİ TUNCEL

  3. Kontrollü/ yaşayan radikal polimerizasyon teknikleri ile graft kopolimer hidrojel sentezi, karakterizasyonu ve hidrojel özelliklerinin incelenmesi

    Investigation of graft copolymer hydrojel synthesis, characterization and hydrojel properties by controlled/ living radical polymerization techniques

    ÜMRAN ASLAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    KimyaVan Yüzüncü Yıl Üniversitesi

    Kimya Ana Bilim Dalı

    DOÇ. DR. MELAHAT GÖKTAŞ

  4. Photochemical routes to hyperbranched polymers

    Çok dallanmış polimer sentezi için fotokimyasal yöntemler

    CANSU AYDOĞAN

    Doktora

    İngilizce

    İngilizce

    2018

    Kimyaİstanbul Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. YUSUF YAĞCI

  5. Synthesis of telechelic aliphatic cyclopolymers by controlled radical polymerization

    Kontrollü radikal polimerleşme ile halkalı alifatik telekelik polimer sentezi

    AYDIN CAN

    Yüksek Lisans

    İngilizce

    İngilizce

    2007

    KimyaBoğaziçi Üniversitesi

    Kimya Ana Bilim Dalı

    YRD. DOÇ. DR. ALİ ERSİN ACAR