Fiber takviyeli kendiliğinden yerleşen betonun mekanik ve durabilite özelliklerinin araştırılması

Investigation of mechanical and durability properties of fiber reinforced self compacting concrete

PDF İndir

  1. Tez No: 246947
  2. Yazar: NUSRET BOZKURT
  3. Danışmanlar: DOÇ. DR. SALİH YAZICIOĞLU
  4. Tez Türü: Doktora
  5. Konular: Teknik Eğitim, İnşaat Mühendisliği, Technical Education, Civil Engineering
  6. Anahtar Kelimeler: Mekanik özellikler, durabilite özellikleri, fiber takviyeli kendiliğinden yerleşen beton, Mechanical properties, durability properties, fibre reinforced self compacting concrete
  7. Yıl: 2009
  8. Dil: Türkçe
  9. Üniversite: Fırat Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Yapı Eğitimi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 184

Özet

Bu tez çalışmasının amacı fiber takviyeli kendiliğinden yerleşen betonun mekanik ve durabilite özelliklerini araştırmaktır. Bu amaçla çökme-yayılma, V-kutusu ve L-kutusu deneyleri uygulanarak taze beton özellikleri belirlenen biri fibersiz kontrol kendiliğinden yerleşen beton (KYB) ve 24 fiber takviyeli kendiliğinden yerleşen beton (FTKYB) tasarlanmıştır. FTKYB tasarımında 4 farklı uzunluk ve boy/çap oranına sahip çelik fiber ile 2 farklı uzunluk ve boy/çap oranında polipropilen sentetik fiber kullanılmıştır. Fiberler karışımlarda tekil ve 2'li, 4'lü kombinasyonlarda kullanılmıştır. Böylece çalışmada tekil fiber etkisi ve karma fiberlerin sinerjisi incelendiği gibi toplam fiber hacmine farklı boyutsal özelliklere sahip fiberlerin girmesi ile fiber boyut yoğunluğu etkisi incelenmiştir. Üretilen betonların normal şartlar altındaki mekanik özelliklerini belirlemek için basınç dayanımı, yarmada çekme dayanımı, eğilmede çekme dayanımı ve ultrasonik ses geçirgenlik (USG) hızı tayini deneyleri ile rölatif porozite deneyleri gerçekleştirilmiştir. Durabilite özelliklerini belirlemek için ise sırası ile yüksek sıcaklık, donma-çözünme, asit dayanıklılık, ıslanma-kuruma ve karbonasyon deneyleri yapılmıştır. Normal şartlar altında uygulanan tüm deneyler durabilite deneyleri sonrasında tekrar uygulanarak durabilite deneyleri sonrasındaki mekanik özellikler belirlenmiştir. Ayrıca bazı numunelerin SEM görüntü analizleri yapılarak içyapı özellikleri incelenmiştir.Genel sonuç olarak, tekil fiber kullanılan karışımlarda fiber uzunluk ve boy/çap oranının düşürülmesi ile taze beton özelliklerinde gelişme gözlenmiştir. Karma fiberli olarak tasarlanan karışımlarda, toplam fiber hacminde uzun ve boy/çap oranı yüksek fiber yoğunluğunun düşürülmesi ile taze beton özellikleri gelişmiştir. Uygulanan mekanik deneyler sonrasında karışımında mikro fiber kullanılan serilerin basınç dayanımında artış gözlenirken, makro fiberlerin basınç dayanımını düşürdüğü; yarmada çekme ve eğilmede çekme dayanımlarında ise makro fiber içeren serilerin mikro fiber içeren serilere göre daha yüksek değerler verdiği belirlenmiştir. Ayrıca makro fiberlerin mikro fiberler ile eşleştiği karma fiberli serilerde mekanik özelliklerin daha üstün olduğu belirlenmiştir. En yüksek dayanım kayıpları, yüksek sıcaklık deneyi uygulanan FTKYB serilerinden elde edilmiştir.

Özet (Çeviri)

The aim of this thesis is to carry out an investigation into mechanical and durability properties of fibre reinforced self compacting concrete (FRSCC). The achievement of this aim, a control self compacting concrete (SCC) and 24 FRSCCs determined fresh concrete properties applying slump-flow, V-funnel and L-box tests were designed. In the design of FRSCC, 4 steel and 2 polypropylene synthetic fibres were used in different lengths and aspect ratios. These fibres were used as single and in combination with 2 and 4 of those fibres. In this way, not only the effect of single fibre and the synergy effect of hybrid fibres but also the size concentration effect of fibres had different dimensional properties in total fibre volume were investigated. Compressive strength, splitting tensile, flexural tensile strengths, ultrasonic pulse velocity tests and relative porosity test were carried out to determine mechanical properties of produced concretes at normal conditions. On the other hand, elevated temperature, freezing-thawing, acid resistance, wetting-drying and carbonation tests were performed to identify durability properties of produced concretes. Moreover, again all same tests applying at normal conditions were conducted out after durability tests to detect mechanical properties. Furthermore, internal structural properties of some concrete specimens were investigated through SEM image analyses.General results of thesis; an improvement was observed on fresh concrete properties with decreasing fibres length and aspect ratio in the mixes used single fibres. Another improvement was observed on fresh concrete properties when the concentration of fibres which are so long and have high level of aspect ratios in total fibres volume was decreased in the mixes designed with hybrid fibres. After mechanical tests, on the one hand, concrete series have micro fibres showed an improvement at compressive strength while concrete series have macro fibres decreased, on the other hand, concrete series have macro fibres gave higher splitting and flexural tensile strengths while concrete series have micro fibres were giving lowers. After all tests were applied it was recognised that mechanical properties of concrete series with hybrid fibres which macro fibres match to micro fibres were superior. The highest strength losses were obtained from FRSCCs which applied elevated temperature test.

Benzer Tezler

  1. Tez No

    398096

    Çelik lif uç geometrisinin beton özelliklerine etkisi

    Effects of steel fiber geometry on mechanical properties of concrete

    UĞUR ALPARSLAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2015

    İnşaat Mühendisliğiİstanbul Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ÖZKAN ŞENGÜL

  2. Tez No

    609570

    Dörtlü sistemlerde mineral katkı ikameli karma lifli kendiliğinden yerleşen betonun işlenebilirlik ve mühendislik özelliklerinin incelenmesi

    Investigation of workability and engineering properties of hybrid fiber reinforced self-compacting concrete produced using by quaternary portland cement blends

    İZZEDDİN DÖNMEZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2020

    İnşaat Mühendisliğiİnönü Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. KAZIM TÜRK

  3. Tez No

    781967

    Direct shear strength of fiber reinforced self compacting concrete under acid and sulfate attack

    Lif takviyeli kendinden yerleşen betonun asit ve sülfat atağı altında doğrudan kesme mukavemeti

    AHMAD HAYDAR A AWRAHMAN

    Yüksek Lisans

    İngilizce

    İngilizce

    2023

    İnşaat MühendisliğiGaziantep Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. ABDULKADİR ÇEVİK

    PROF. DR. AZAD ABDULKADİR MOHAMMED

  4. Tez No

    455401

    Mechanical performance of glass textile reinforced cementitious composites

    Cam tekstil donatılı çimentolu kompozitlerin mekanik özellikleri

    HAMED AGHAFAM

    Yüksek Lisans

    İngilizce

    İngilizce

    2016

    Tekstil ve Tekstil Mühendisliğiİstanbul Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. BEKİR YILMAZ PEKMEZCİ

  5. Tez No

    517426

    Mechanical behavior of self-compacting fiber reinforced concrete at elevated temperatures

    Lif takviyeli kendiliğinden yerleşen betonun yüksek sıcaklıklardaki mekanik davranışı

    KHAMEES NAYYEF ABDULHALEEM ABDULHALEEM

    Doktora

    İngilizce

    İngilizce

    2018

    İnşaat MühendisliğiGaziantep Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. ABDULKADİR ÇEVİK

    YRD. DOÇ. DR. MEHMET EREN GÜLŞAN

Geri Dön