Silikat ve aluminat bazlı yeni ışıldarların hazırlanması ve karakterizasyonu
Preparing and characterization of new silicate and aluminate phosphors
- Tez No: 253340
- Danışmanlar: PROF. DR. NEVZAT KÜLCÜ
- Tez Türü: Doktora
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2009
- Dil: Türkçe
- Üniversite: Mersin Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Bölümü
- Bilim Dalı: Anorganik Kimya Ana Bilim Dalı
- Sayfa Sayısı: 93
Özet
Bu çalışmada, silikat ve aluminat bazlı ışıldar fazları, Katı Hal, Sol Jel ve Hidrotermal yöntemleri kullanılarak sentezlendi. Sentezlenen aluminat bazlı ışıldarlar: M4Al14O25:Eu2+,Dy3+ (M:Sr, Ba); Sr4Al14O25:Eu2+,Dy3+.RE3+ (RE: Ce, Nd, Yb) ve Silikat bazlılar ise: CdSiO3:Mn2+,Eu3+,RE3+ (RE: Y, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Yb), ZnCdSi2O6:R,Gd3+, M2SiO4:Mn2+,Gd3+fazlarıdır. Hazırlanan ışıldar fazların karakterizasyonu Infrared (FT-IR) spektrometresi ve X-ışını toz kırınımı teknikleriyle yapıldı. Işıma özellikleri, luminesans sönüm süreleri ve quantum verimlerinin belirlenmesinde fotoluminesans spektrometresi kullanıldı. Tuzak derinlikleri ve parametreleri ise termoluminesans ışıma eğrilerinden Pik Biçimi ve Bilgisayarla Işıldama Eğrisi Ayrıştırma yöntemleri kullanılarak hesaplandı. Ayrıca, tüm ışıldarların kuantum verimleri Wrighton-Ginley-Morse yöntemiyle tespit edildi.Tüm ışıldar bileşiklerin uzun süreli ışıma için gerekli olan uygun tuzak derinliğine (0.6-0.8 eV) sahip oldukları belirlendi. Tanecik boyutu ve dağılımı ile ışıma şiddeti ve süresi arasındaki ilinti araştırıldı. Tanecik boyutunun küçülmesiyle ışıma şideti ve süresinin arttığı görüldü. Aluminat bazlı ışıldarların kuantum verimlerinin 7-45 arasında, silikat bazlı ışıldarların kuantum verimlerinin ise 1-60 arasında yer aldığı tespit edildi. Aluminat bazlı bileşiklerin termal olarak kararlı oldukları (> 1400 oC) ve görünür bölge ışınlarıyla uyarılabildikleri, silikat bazlı bileşiklerin ise 1100 oC üzerinde kararsız oldukları, genelde UV ışınlarıyla (254 nm) uyarılabildikleri belirlendi. Sonuç olarak, aluminat bazlı ışıldarlar seramik malzamelerin yapımında, silikat bazlı ışıldarlar ise floresan lambaların üretilmesinde kullanılabilecektir.
Özet (Çeviri)
In this study, silicate and aluminate phosphors were synthesized by solid state, sol-gel and hydrothermal methods. Synthesised aluminate phosphors: Sr4Al14O25:Eu2+,Dy3+; Sr4Al14O25: Eu2+, Dy3+.RE3+ (RE:,Ce,Nd, Yb) and Ba4Al14O25:Eu2+, Dy3+. Silicates: CdSiO3:Mn2+; CdSiO3Mn2+,Gd3+ and CdSiO3:Mn,Eu3+,RE3+ (RE=Y,La,Ce,Pr,Nd,Pm,Sm,Eu,Gd,Tb,Dy,Ho,Er,Yb) phases. Characterization of prepared phosphors carried out by using Infrared (FT-IR) spectrometry and x-ray powder diffraction techniques. Photoluminescence spectrophotometry was used for determination of emission properties, luminescence lifetime and quantum yields. In additon, trap depth and parameters were determined by using Peak shape and Computer Glow Curve Deconvolution methods from thermoluminescence glow curves. Also, quantum yields of all phosphors calculated by using Wrighton-Ginley-Morse method.As a result, it was assigned that all of compounds have suitable trap depth (0.6-0.8 eV). Quantum yields of aluminate and silicate phosphors have been lied in 7-45 and 1-60 ranges, respectively. The correlation of the particul size and distribution between emission intensity and luminescence lifetime were investigated. If the particul size decreases, the emission intensity and luminescence lifetime increases. It was determined that aluminate phosphors are thermally stable (> 1400 oC) and can be excited by visible light, also silicates are unstable over 1100 oC and generally are excited by UV light (254 nm). Therefore, aluminate phosphors can be used in producing flourescence lamps and silicates can be used in preparing ceramic materials.
Benzer Tezler
- Lantanoid iyonlarıyla katkılanmış silikat bazlı yeni ışıldarların hazırlanması ve karakterizasyonu
Başlık çevirisi yok
ELİF NAZLI GÜLŞEN
Yüksek Lisans
Türkçe
2023
KimyaBurdur Mehmet Akif Ersoy ÜniversitesiNanobilim ve Nanoteknoloji Ana Bilim Dalı
DOÇ. DR. NURETTİN KÖRÖZLÜ
- Aluminat bazlı nanofosforların sentezi ve ışıma özelliklerinin incelenmesi
Synthesis of aluminate based nanophosphors and investigation of their luminescence properties
HÜMEYRA KARUL
Yüksek Lisans
Türkçe
2015
KimyaMehmet Akif Ersoy ÜniversitesiKimya Ana Bilim Dalı
YRD. DOÇ. FATİH MEHMET EMEN
- Ayanis Kalesi demir esaslı arkeolojik kazı buluntularında tanımlamaya ve korumaya yönelik arkeometrik analizler
Archaeometric analyses for the identification and conservation of iron-based archaeological finds of Ayanis Fortress
ATALAY KARATAK
Doktora
Türkçe
2025
ArkeolojiAnkara Hacı Bayram Veli ÜniversitesiKültür Varlıklarını Koruma Ana Bilim Dalı
PROF. DR. ALİ AKIN AKYOL
PROF. DR. ÜNSAL YALÇIN
- Pomza ikameli geopolimer harçların dayanım ve durabilite performanslarının incelenmesi
Investigation of strength and durability performances of pumice substituted geopolymer mortars
TAHA SALAH WAHHAB AL-ANTAKI
Doktora
Türkçe
2025
İnşaat Mühendisliğiİstanbul Gelişim Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. ANIL NİŞ
- Effect of metal catalyst and tailoring the conditions for cnf/cnt growth through cvd
Karbon nanofiber ve karbon nanotüplerin cvd yöntemiyle seçimli büyütülmesi ve metal katalizörün etkisi
AHU GÜMRAH DUMANLI
Doktora
İngilizce
2008
Metalurji MühendisliğiSabancı ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. YUDA YÜRÜM