Effect of orientation on salt water fog enhanced fatique crack growth behavior of 7050 T73651 aluminum alloy
Başlık çevirisi mevcut değil.
- Tez No: 2715
- Danışmanlar: PROF. DR. MUSTAFA DORUK
- Tez Türü: Doktora
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Çatlak büyüme hızı, korozyonlu yorulma, çatlak uzunluğu, gerilim şiddet aralığı, tuzlu su sisi. -vı
- Yıl: 1987
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Belirtilmemiş.
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 117
Özet
DZET 7D5D T73651 ALÜMİNYUM ALAŞIMININ TUZLU SU SİSİNDEKİ ÇATLAK BÜYÜME DAVRANIŞININ YÖNLERE GÜRE DE?İŞİMİ GÜRBÜZ, Rıza Doktora Tezi, Metalürji Müh. Bölümü Tez Yöneticisi: Prof.Dr. Mustafa Doruk Aralık 1987, 1D3 sayfa Bu çalışmada özellikle havacılık endüstrisi için geliştirilmiş yeni bir malzeme olan 7050 T73651 alüminyum alaşımının yorulma çatlak büyüme davranışı incelendi. Laboratuvar havasında ve %5 NaCl çözeltisi ile oluşturulan tuzlu su sisinde gerçekleştirilen deneylerde sabit yük genlikli pozitif sinüs dalgaları kullanıldı. Altı değişik yönde hazırlanan C-T deney örnekleriyle yapılan çalışmalar sonucunda, tuzlu su sisi ortamının genel olarak tüm yönlerde etkili olduğu, çatlak büyüme hızını arttırdığı, yorulma ömrünü ise düşürdüğü bulundu. Çatlak büyüme davranışının ve korozif ortamdan etkilenme oranının yönlere göre önemli farklılıklar gösterdiği saptandı. En güçlü yönün L-S, en zayıf yönün ise S-L olduğu bulundu. Kırılan örneklerin kırılma yüzeylerinin taramalı -v-elektron mikroskobu ile incelenmesi, yorulma çatlaklarının taneleri keserek ilerlediğini, çatlak yüzeyinde yorulma çizgilerinin ve çok sayıda ikincil çatlakların oluştuğunu gösterdi. Çatlak büyüme davranışının ifadesinde, iki eğimli Paris denkleminin uygulanması havadaki deney bulguları için kabul edilebilir sonuçlar verdi.
Özet (Çeviri)
ABSTRACT EFFECT OF ORIENTATION ON SALT WATER FOG ENHANCED FATIGUE CRACK GROWTH BEHAVIOR OF 7050 T73651 ALUMINUM ALLOY GÜRBÜZ, Rıza Ph.D. in Metallurgical Engineering Supervisor: Prof.Dr. Mustafa DDruk December 1987, 1G3. pages The fatigue crack growth behavior of 7050 T73651 high strength aluminum alloy that is developed especially for aircraft industry was investigated in this study. The tests mere conducted by using 1" C-T specimens machined in 6 orientations under the action of constant amplitude sinusoidal load cycles. The tests were first carried out in laboratory air and then repeated in salt water fog of 5% NaCl solution to observe the effect of environment on fatigue crack growth behavior. The fatigue lives and the fatigue crack growth rates of the specimens have been seriously affected from the environment. The severity of the effect, however, was observed to be dependent on the orientation. The strongest orientation was determined to be L-S while the weakest to be S-L. -iii-The examination of the fracture surfaces by scanning electron microscope, SEM, shamed that the fracture was of transgranular type. Fatigue striations and secondary cracks were observed extensively on fracture surfaces. The use of two-slope Paris equation for the description of fatigue crack growth rates was found to be acceptable for the tests in air. Hey words: Fatigue crack growth rate, corrosion fatigue, crack length, stress intensity range, salt water fog. -iv-
Benzer Tezler
- Synthesis and characterization of microporous titano/vanadosilicate zeotype films for humidity sensing applications
Nem sensörü uygulamaları ı̇çı̇n mı̇kro gözeneklı̇ tı̇tano/vanadosı̇lı̇kat zeotı̇p fı̇lmlerı̇n sentezı̇ ve karakterı̇zasyonu
RAMONA DAVOUDNEZHAD
Doktora
İngilizce
2022
Bilim ve TeknolojiOrta Doğu Teknik ÜniversitesiMikro ve Nanoteknoloji Ana Bilim Dalı
PROF. DR. BURCU AKATA KURÇ
PROF. DR. NECATİ ÖZKAN
- Preparation of cholesterol imprinted polymeric sorbents
Kolesterol baskılanmış polimerik sorbentlerin hazırlanması
VEYİS KARAKOÇ
- Türkiye kökenli pirina yağından sıvı-sıvı ekstraksiyonu ile serbest yağ asitlerinin giderilmesi üzerinde bir inceleme
An Investigation on the deacidification of Turkish sulphur olive oil by liquid-liquid extraction
SELMA TÜRKAY
- O-asetilpeptidoglukan esteraz (APE1) enziminin tepkime mekanizmasının ın silico yöntemlerle aydınlatılması
Elucidation of reaction mechanism of APE1 enzyme with in silico methods
ZEYNEP AKSAKAL
Yüksek Lisans
Türkçe
2019
Kimyaİstanbul Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. NURCAN TÜZÜN
PROF. DR. FETHİYE AYLİN SUNGUR