Demir esaslı intermetalik malzemelerin mikrodalga sinterleme ile üretimi ve difüzyon kaynağı ile birleştirilmesi
The production of Fe-based intermetallics by microwave sintering and their diffusion bonding
- Tez No: 275829
- Danışmanlar: DOÇ. DR. ŞÜKRÜ TALAŞ
- Tez Türü: Doktora
- Konular: Metalurji Mühendisliği, Teknik Eğitim, Metallurgical Engineering, Technical Education
- Anahtar Kelimeler: Difüzyon Kaynağı, İntermetalik, Toz Metalurjisi, Sinterleme, Diffusion Bonding, Intermetallics, Powder Metallurgy, Sintering
- Yıl: 2010
- Dil: Türkçe
- Üniversite: Afyon Kocatepe Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 201
Özet
Toz metalurjisi yöntemiyle üretilen endüstriyel parçalar düşük maliyete, düşük yoğunluğa ve kolay üretilebilme özelliğine sahiptir. Bununla birlikte yüksek sıcaklıklarda yüksek oksidasyon direnci sergilemektedir. Potansiyel uygulama malzemesi olarak Fe3Al ve FeAl intermetalik bileşikler üzerine yapılan çalışmalar üretim sürecinde yaşanan zorlukları en aza indirmeye yoğunlaşmaktadır. Toz metalurjisi yöntemiyle üretimin fizibilite edilmesi amacıyla, Fe-Al ve Fe-Al-Ti toz karışımları hem geleneksel ve hem de Mikrodalga sinterleme yöntemiyle üretilmesi ve ayrıca difüzyon kaynağı ile üretilen toz karışımlarının birleştirilmesi gerçekleştirilmiştir. Fe-Al ve Fe-Al-Ti toz karışımlarının özellikle Mikrodalga sinterleme ile üretimi üzerine yapılan çalışmaların olmaması bu çalışmanın orijinalliğine katkıda bulunmaktadır.Bu çalışmada Al 75?m, Ti ve Fe 45?m boyutunda >%99 saflıkta tozlar kullanılmıştır. Bu tozlardan değişik oranlarda Fe-26Al, Fe-30Al, Fe-33Al ve Fe-26Al-14Ti/16/20, Fe-30Al-14Ti/16/20, Fe-33Al-14Ti/16/20 homojen karışım sağlanarak bağlayıcı kullanmadan tek eksenli presleme yapılarak ham mukavemetleri sağlanmıştır. Numunelerin sinterlenmesi Mikrodalga ve geleneksel fırında, argon atmosferinde 450, 500, 550, 600, 650, 700, 750, 800 0C'de ve ayrıca vakum ortamında (kuarts tüp içerisinde) aynı sıcaklıklarda yapılmıştır. Sinterleme süreleri 0,5, 1 ve 1,5 saat olarak belirlenmiştir. Çok düşük sıcaklıklar ve çok yüksek sıcaklıklarda numunelerden beklenen performans elde edilememiştir. Bu yüzden bu çalışmada sıcaklık aralığı 550-650 0C arasında gerçekleştirilmiştir. Difüzyon kaynağı, 600 0C'de 3 MPa basınçta, 1 saat sürede vakum ortamında yapılmıştır. Numunelerin difüzyon kaynağında Cu aratabaka kullanılarak esas metalin mukavemetine yakın değerde birleşme sağlanmıştır.Sinterlenmiş numunelerin XRD ve SEM analizleri değerlendirilmiştir. Sinterleme sıcaklığına bağlı kesme mukavemeti ve sertlik değerleri ölçülmüştür. Difüzyon kaynak yöntemi ile birleştirilen numunelerin mikroyapı analizleri ve kesme mukavemeti ölçülmüştür. Numunelerin kesme mukavemet değerlerinin belirlenmesinde Iosepescu yöntemi kullanılmıştır. Bu yöntemle, sinterlenmiş numunelerde kesme mukavemet değerleri 70 MPa ve sinterleme işleminden sonra difüzyon kaynağı yapılmış numunelerde kesme mukavemet değerleri 55 MPa ölçülmüştür.
Özet (Çeviri)
Industrial parts manufactured by powder metallurgy method has an advantage of low-cost, low-density and can also be easily manufactured. In addition, they show high oxidation resistance at high temperatures. Potential applications as structural materials for FeAl and Fe3Al intermetallic compounds, the studies focus on the minimization of difficulties experienced in the manufacturing process. In order to optimize the manufacture by powder metallurgy method, Fe-Al and Fe-Al-Ti powder mixtures were produced by both conventional and microwave sintering methods and diffusion bonding was employed to join the microwave sintered powder mixtures. The microwave sintering of Fe-Al and Fe-Al-Ti mixtures could not be seen in the literature and this contributes to the authenticity of this study.In this study, Al of 75?m, Ti and Fe of 45?m and high purity powders better than > 99% are used. The powder in different ratios of Fe-26Al, Fe-30Al, Fe-33Al and Fe-26Al-14Ti/16/20, Fe-30Al-14Ti/16/20, Fe-33Al-14Ti/16/20 homogeneous mixture without providing a binding uniaxial compaction has been achieved by making the raw strength. Microwave and conventional furnace sintering of the samples in argon atmosphere, at temperatures of 450, 500 550, 600, 650, 700, 750, 800 0C, and also at the same temperatures in a vacuum in the silica tube silica was produced. Sintering durations of 0,5, 1 and 1,5 hours were selected. Temperatures at high and low ends of the scale were found to be unfeasible for the manufacturing of the specimens. Therefore, temperatures of 550C and 650C were selected for this study. Diffusion bonding at 600 0C and 3 MPa pressure for 60 minutes was performed in a vacuum. The shear strength of samples that are diffusion bonded using Cu interlayer was found close to the strength of the powder compacts.XRD and SEM analysis of sintered samples were evaluated. The shear strength and hardness were measured with respect to the sintering temperature. THe microstructural analysis and the shear strength of the specimens produced by diffusion bonding. Iosepescu method was used for determining the shear strength of the samples. The shear strength values as high as 70 MPa in sintered samples and shear strength values as high as MPa in diffusion bonded specimens were measured.
Benzer Tezler
- Yüksek silisyum ve molibden içeren dökme demirlerin kutu alüminizasyonu ve yüksek sıcaklık oksidasyon davranışının incelenmesi
Pack aluminizing of high Si-Mo cast iron and investigation of high temperature oxidation behavior
FATİH KURT
Yüksek Lisans
Türkçe
2017
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. NURİ SOLAK
- Characteristics of cold sprayed titanium based coatings
Soğuk gaz dinamik püskürtme yöntemiyle üretilmiş titanyum esaslı kaplamaların karakteristiği
AHMET HİLMİ PAKSOY
Yüksek Lisans
İngilizce
2017
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MURAT BAYDOĞAN
DOÇ. DR. ERDEM ATAR
- Investigation of the cutting performances of the diamond tools used in the natural stone industry
Doğal taş sanayisinde kullanılan elmaslı kesicilerin kesim performansının incelenmesi
BERRAK BULUT
Doktora
İngilizce
2021
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MURAT BAYDOĞAN
- Mekanik alaşımlama yöntemiyle Al esaslı intermetalik fazların mekanokimyasal sentezlenmesine yağlayıcı türünün etkisi
Effect of lubricant type on the mechanochemical synthesis of Al-based intermetallic phases by mechanical alloying method
CANKIZ GİZEM DELİBALTA
Yüksek Lisans
Türkçe
2018
Metalurji MühendisliğiGazi ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. YUSUF ÖZÇATALBAŞ
- Demir alüminat esaslı TiC, TiB2 takviyeli kaplama kompozitlerinin geliştirilmesi
Development of iron alumunite based TiC, TiB2 reinforced coating composite's
ERSAN MERTGENÇ
Doktora
Türkçe
2014
Metalurji MühendisliğiAfyon Kocatepe ÜniversitesiMetal Eğitimi Ana Bilim Dalı
PROF. DR. ŞÜKRÜ TALAŞ
YRD. DOÇ. DR. BARIŞ GÖKÇE