İletken politiyofen/poli (etilen teraftalat) kompozit liflerinin hazırlanması, karakterizasyonu ve elektromanyetik dalga koruyucu özelliğinin incelenmesi
Preparation, characterization and electromagnetic shielding effectiveness of conducting polythiophene/poly (ethylene terapthalate) composite fibers
- Tez No: 300860
- Danışmanlar: PROF. DR. MEHMET SAÇAK
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Polimer Bilim ve Teknolojisi, Chemistry, Polymer Science and Technology
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2011
- Dil: Türkçe
- Üniversite: Ankara Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 96
Özet
İletken politiyofen (PTh)/poli(etilen teraftalat) (PET) kompozit lifleri, asetonitril içerisinde FeCl3 yükseltgeni kullanılarak PET liflerin bulunduğu ortamda tiyofenin oksidatif polimerizasyonu ile hazırlandı. Kompozit liflerin % PTh içeriği ve yüzey direnci üzerine sıcaklık, polimerizasyon süresi, yükseltgen ve monomer derişimi gibi polimerizasyon şartlarının etkileri ayrıntılı araştırıldı. Çalışmada diklorometan ile şişirme ön işleminden geçirilmiş PET liflerin kullanılmasının kompozit liflerin % PTh içeriğini artırdığı gözlendi. En yüksek % PTh içeriği (%5,7) ve en düşük yüzey direncine (75,0 k?/cm2) sahip kompozit lifler, 1,25 M FeCl3 ve 0,42 M tiyofen ile 20 oC'de 30 dakika süren polimerizasyon koşullarında elde edildi. Kompozit liflerin, içerdiği PTh miktarının artmasıyla yoğunluk ve çaplarının saf PET'e göre arttığı gözlendi. Örneklerin karakterizasyonunda FTIR, TGA, XRD ve SEM teknikleri kullanıldı. Kompozit liflerin yüzey dirençleri üzerine deterjan ve kuru temizleme sıvısı kullanılarak yapılan yıkama işlemlerinin etkileri araştırıldı. Ayrıca farklı sıcaklıklardaki ortamlarda 5 gün süreyle bekletilen kompozit örneklerinin yüzey dirençleri takip edildiğinde örneklerin yüzey direncinde önemli bir değişikliğin olmadığı gözlendi. İletken kompozit liflerin elektromanyetik dalga koruyucu özelliğinin incelenmesi amacıyla kompozitin radyo ve mikrodalga frekans aralığındaki elektromanyetik koruma etkinliği (EMSE) ölçülerek frekans artışı ile koruma etkinliğinin azaldığı gözlendi.
Özet (Çeviri)
Conductive polythiophene (PTh)/poly(ethylene terapthalate) (PET) composite fibers were prepared by polymerization of thiophene in the presence of PET fibers in acetonitrile medium using FeCl3 as oxidant. The effects of polymerization conditions such as temperature, polymerization time, the concentrations of oxidant and monomer on PTh content and surface resistivity of PTh/PET composite fiber were investigated in detail. It was observed that the uses of dichloromethane pre-swelled PET fibers increased the PTh content of composite fiber. Composite fiber having the highest PTh content (5.7 %) and the lowest surface resistivity (75.0 k?/cm2) was obtained at T= 20 °C with 1.25 mole/L FeCl3 and 0.42 mole/L thiophene concentrations. The densities and diameters of composite fibers were increased with increasing PTh content of composite in comparison with PET fiber. Characterization of samples was carried out with FTIR, TGA, XRD and SEM techniques. The washing effects of laundering detergant and dry cleaninig liquid on surface resistivities of composite fibers were investigated. Morever, the surface resisitivities of composite fibers which were treated with different temperatures for 5 days were measured and any variation was observed in surface resistivity of samples. In order to investigate the electromangetic shielding property of conducting PTh/PET composites, electromagnetic shielding effectiveness (EMSE) measurements were performed in radio and microwave frequency ranges and it was observed that the shielding effectiveness was decreased with increasing frequency.
Benzer Tezler
- Karbazol türevi polimerlerin yüzey özelliklerinin araştırılması
Investigation of surface properties of carbazol derivative polymers
BEYZA UZUN
Yüksek Lisans
Türkçe
2024
KimyaÇanakkale Onsekiz Mart ÜniversitesiMatematik ve Fen Bilimleri Eğitimi Ana Bilim Dalı
DOÇ. DR. AYSEL AYDIN KOCAEREN
- Functional conjugated polymers
Fonksiyonel konjuge polimerler
HÜSEYİN AKBULUT
Doktora
İngilizce
2015
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. YUSUF YAĞCI
- Ketonic resin-polypyrrole copolymers
Ketonik reçine–polipirol kopolimerleri
GİZEM KURTULMUŞ
Yüksek Lisans
İngilizce
2019
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. NİLGÜN KIZILCAN
- N-Substitue pirollerin sentezi ve polimerizasyonu
Synthesis and polymerization of N-Substituted pyrroles
AHMET YETKİN
- Metanol oksidasyon performansının arttırılması için iletken polimer destekli elektrot modifikasyonu
Conductive polymer supported electrode modification to improve methanol oxidation performance
ÖMER FURKAN COŞKUN
Yüksek Lisans
Türkçe
2022
EnerjiEskişehir Osmangazi ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. EVRİM HÜR