Poli (etilen terefitalat) (PET) eriyiklerine çeşitli organik ve inorganik aditiflerin ilave edilerek boyanma özelliklerinin iyileştirilmesi

Improvement of dyeing properties of poly (ethylene terephthalate) (PET) by addition of various organic and inorganic additives

PDF İndir

  1. Tez No: 329497
  2. Yazar: SERVET GÜNEŞ
  3. Danışmanlar: YRD. DOÇ. DR. İLHAN ÖZEN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Tekstil ve Tekstil Mühendisliği, Textile and Textile Engineering
  6. Anahtar Kelimeler: Polimer, polietilen tereftalat (PET), kil, montmorillonit, nanokompozit, Polymer, poly(ethylene terephthalate) (PET), clay, montmorillonite, nanocomposite
  7. Yıl: 2013
  8. Dil: Türkçe
  9. Üniversite: Erciyes Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Tekstil Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 90

Özet

Bu tez çalışmasında, eriyikten çekme yöntemi ile polietilen tereftalat (PET)/organokil nanokompozit iplikler elde edilmiş ve bu ipliklerin fiziksel ve boyanma özelliklerinin incelenmesi amaçlanmıştır. Bu kapsamda, iki montmorillonit kil interkalasyon ajanları kullanılarak sentezlenmiş ve PET/organokil (85/15 w/w) masterbatch'leri hazırlanmıştır. Daha sonra, farklı miktarlarda (%0.5-5) organokil içeren nanokompozit filamentler elde edilmiş ve farklı konsantrasyonlarda (%0.5-1.5) iki dispers boya ile atmosferik (100oC keriersiz ve kerierli) ve yüksek sıcaklıktaki (122oC) boyama koşullarında boyanmıştır.HT, kerierli ve keriersiz boyama yöntemleri ile boyanan numunelerin renk verimi ve renk farklarının ölçümleri yapılmıştır. Ayrıca, her bir boyama koşulu altında modifiye edilmemiş PET standart olarak ele alınmış, diğer nanokompozit ipliklerle arasındaki ?L*, ?a*, ?b*, ?C* ve ?hº ve K/S değerleri bulunmuş ve elde edilen renk özellikleri ve renk verimleri yorumlanmıştır. HT, kerierli ve keriersiz boyama yöntemleri ile boyanan nanokompozit iplikler tenasite, % kopma uzaması ve % kaynama çekmesi açısından karşılaştırılmıştır.Sonuçta, kil konsantrasyonun artışı mekanik özellikleri azaltmıştır. Buna rağmen, PET/organokil nanokompozit filamentlerin boyanabilirliği iyileşmiştir.

Özet (Çeviri)

In this study, poly(ethylene terephthalate) (PET)/organoclay nanocomposite filaments are generated by melt-spinning method and their physical and dyeing properties are aimed to be investigated. In this scope, two montmorillonite types of clay were modified using an intercalating agent synthesized and PET/organoclay (85/15 w/w) master batches were prepared. Afterwards, nanocomposite filaments containing different amounts of organoclay (0.5-5 wt.%) were produced and dyed with two disperse dyes at atmospheric (100oC with/without carrier) and high temperature (122oC) dyeing conditions.Measurements of color efficiency and color differences were conducted on the samples, dyed by the methods of atmospheric and high temperature dyeing conditions and the results were evaluated. Besides, neat PET as the standard, the values of ?L*, ?a*, ?b*, ?C* ve ?hº ve K/S were obtained by comparing the other nanocomposite filaments and the color properties and color strengths were interpreted. Moreover, tenacity, elongation at break and boiling shrinkage of the PET/organoclay nanocomposite filaments dyed at atmospheric and high temperature dyeing conditions were compared at the end of the dyeing tests.Finally, increased clay concentration led to reduced mechanical properties. Nonetheless, PET/organoclay nanocomposite filaments showed enhanced dyeability.

Benzer Tezler

  1. Tez No

    118927

    Melt blending of poly (ethylene terephthalate) and high density polyethylene in the presence of carbon black

    Poli (etilen terefitalat) ve yüksek yoğunluklu polietilen'in karbon siyahlı ortamda eriyik karışımları

    HASAN ÇAKMAK

    Yüksek Lisans

    İngilizce

    İngilizce

    2002

    KimyaOrta Doğu Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. TEOMAN TİNÇER

  2. Tez No

    259001

    Investigation of barrier properties of as cast and biaxially stretched PET/EVOH and PETI/EVOH blend films

    PET/EVOH ve PETI/EVOH karışım filmlerinin dökme ve çift eksenli gerdirilmiş hallerinin bariyer özelliklerinin incelenmesi

    CAHİT DALGIÇDİR

    Yüksek Lisans

    İngilizce

    İngilizce

    2009

    Makine MühendisliğiSabancı Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    DR. İLHAN ÖZEN

    PROF. YUSUF MENCELOĞLU

  3. Tez No

    301649

    Organokil esaslı nanokompozit endüstriyel liflerin üretilmesi ve karakterizasyonu

    Processing and characterization of organoclay based industrial fibers

    DİLEK TURAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2012

    Kimya MühendisliğiKocaeli Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    DOÇ. DR. GÜRALP ÖZKOÇ

  4. Tez No

    143309

    Ter blend of poly (ethylene terephthalate), polypropylene and low density polyethylene

    Poli (etilen terefitalat), polipropilen ve düşük yoğunluklu polietilenin üçlü karışımları üzerine çalışma

    ERKAN DOĞAN

    Yüksek Lisans

    İngilizce

    İngilizce

    2003

    Polimer Bilim ve TeknolojisiOrta Doğu Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    PROF. DR. TEOMAN TİNÇER

  5. Tez No

    119109

    Poly (ethylene terephthalate) and high density polyethylene in melt blending in the presence of transesterification catalyst

    Poli (etilen teraftalat)'ın yüksek yoğunluklu polietilen ile transesterifikasyon katalizörlü ortamda eriyik karışımı

    BİNNUR ÖZKAN

    Yüksek Lisans

    İngilizce

    İngilizce

    2002

    KimyaOrta Doğu Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. TEOMAN TİNÇER

Geri Dön