Geri Dön

Elektro erozyon yönteminin zirkonyum oksit seramikler üzerindeki etkilerinin incelenmesi

Evaluation of the effects of the electrical discharge machining on zirconium oxide ceramics

  1. Tez No: 352792
  2. Yazar: NERGİZ RONA
  3. Danışmanlar: DOÇ. DR. MURAT YENİSEY
  4. Tez Türü: Doktora
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Elektro Erozyon, zirkonyum oksit, makaslama bağlanma dayanımı, seramik, yüzey İşlemi, 3-nokta eğme testi, Electrical Discharge machining, zirconium oxide, shear bond strength, ceramic, surface treatment, 3-point bending
  7. Yıl: 2014
  8. Dil: Türkçe
  9. Üniversite: Ondokuz Mayıs Üniversitesi
  10. Enstitü: Sağlık Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 130

Özet

Elektro erozyon ile işleme (EEİ) yöntemi kontrollü şartlar altında iş parçasını aşındırmak için kıvılcımlar serisinin kullanıldığı bir yöntemdir. Bu çalışmanın amacı, EEİ yönteminin zirkonyum oksit seramiklerdeki rezin siman-seramik bağlantısına etkisini incelemek ve yöntemin mekanik etkilerini değerlendirmektir.Makaslama bağlantı testi için 4,8×4,8×4,8 mm ebatlarında 60 adet zirkonyum örnek hazırlandı. Örnekler dört gruba ayrıldı. Sırasıyla bu gruplara şu yüzey işlemleri yapıldı: GK(Kontrol): 110µm Al2O3 ile kumlama+ silan, GR: Rocatec Pre+Rocatec plus+ silan, GL: Er:YAG lazer +silan, GEE: 2A'lik akım ile 10 dk. EEİ+silan. Yüzey işlemi yapılan zirkonyum örnekler dual-cure rezin siman ile kompozit örneklere simante edildi. Ardından 5-55oC'lerde 6000 kez termal devirlendirme uygulanan örneklere Universal test cihazında 0,5 mm/dk. kafa hızı ile makaslama testi uygulandı. Veriler tek yönlü varyans analizi (ANOVA) ve Tukey testi ile istatistiksel olarak değerlendirildi. 3-nokta eğme testi için 1,2×4×20 mm ebatlarında 60 adet zirkonyum örnek hazırlandı. Bu örnekler dört gruba ayrıldı. Gruplara sırasıyla; Kumlama, tribokimyasal silika kaplama lazerle pürüzlendirme ve EEİ yöntemleri uygulandı. Daha sonra universal test cihazına yerleştirilen örneklere 3-nokta eğme testi uygulandı. Elde edilen veriler tek yönlü varyans analizi (ANOVA) ve Tukey testi ile istatistiksel olarak değerlendirildi.En yüksek bağlantı değerleri Grup EE'den elde edildi ve bu grup ile Grup K, Grup L arasında istatistiksel olarak anlamlı fark bulundu (p0,05).EEİ yöntemi, yüzey işlemi olarak Y-TZP seramiklerde rezin simanlarla olan bağlantıyı arttırmış ve seramiğin mekanik özelliklerine olumsuz bir etkisi gözlenmemiştir.

Özet (Çeviri)

Electrical Discharge Machining (EDM) is a method which uses series of sparks to erode the workpiece under controlled conditions.The aim of this study is to evaluate the effect of EDM on resin-ceramic bonding and mechanical effects of the method on zirconium oxide ceramics. For shear bond strength test; 60 pieces 4.8×4.8×4.8 in size zirconia specimens were prepared. Then the specimens were divided into four groups and different surface treatments were applied: GK (Control): Air-particle abrasion(110µm Al2O3)+silane, GR:Tribochemical silica coating (Rocatec Pre +Rocatec plus)+ silane. GL: Er:YAG laser +Silane. GEE: 2A, 10 minutes EDM+silane. Each conditioned ceramic specimen was bonded to a composite block using a dual-cure resin cement. Then 6000 times thermal cycled prior to bond tests. The shear bond strength tests were performed in a universal testing machine with a crosshead speed of 0.5 mm/min. The mean bond strengths of the specimens of each block were statistically analyzed using ANOVA and Tukey's test. For 3-point bending test; 1.2×4×20 mm in size 60 zirconia specimens were prepared. Then specimens were assigned to four groups following four treatment conditions: Air particle abrasion, Tribochemical silica coating, Laser treatment, EDM. After surface treatments 3-point bending test were performed in a universal testing machine (crosshead speed: 0.5mm/min). Mean flexural strength values were statistically analyzed using ANOVA and Tukey's test.Analysis showed that the bond strength was significantly higher in Group EE, than in Groups L,K (p0.05). As a surface treatment EDM increased the zirconia-resin bonding and did not effect the zirconia negatively about mechanical properties.

Benzer Tezler

  1. Electro-erozyon ile kalıp imalatı ve uygulama alanlarının araştırılması

    Başlık çevirisi yok

    OMAR KADIBBAN

    Yüksek Lisans

    Türkçe

    Türkçe

    1993

    Endüstri ve Endüstri MühendisliğiYıldız Teknik Üniversitesi

    Endüstri Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. MESUT ÖZGÜRLER

  2. WEDM yönteminde işlem parametrelerinin mikroyapı ve yüzey pürüzlülüğüne etkisi

    The Effects of process parameters on the microstructure and surface roughness in the WEDM process

    ULAŞ ÇAYDAŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2002

    Makine MühendisliğiFırat Üniversitesi

    Makine Eğitimi Ana Bilim Dalı

    Y.DOÇ.DR. AHMET HASÇALIK

  3. Elektro erozyon ile tornalamada boyut ve yüzey tamlığının incelenmesi ve işleme parametrelerinin optimizasyonu

    Optimization of machining parameters and investigation of dimensional and surface finish in electrical discharge turning

    GÖRKEM CAN PALABIYIK

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    Makine MühendisliğiGazi Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. HACI BEKİR ÖZERKAN

  4. Elektro erozyon işleme yönteminde elektrot malzemesi ve işleme parametrelerinin yüzey kalitesi ve elektrot aşınmasına etkilerinin incelenmesi

    Investigation of the effects of electrode material and machining parameters on surface quality and electrode wear in EDM

    SERKAN YAMAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    Makine MühendisliğiYıldız Teknik Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ORHAN ÇAKIR

  5. 17-4 PH paslanmaz çeliğin elektro erozyon ve elektro kimyasal işleme yöntemleriyle işlenebilirliğinin araştırılması ve işleme yüzeylerinde korozyon davranışının incelenmesi

    Investigation of the machinability of 17-4 PH stainless steel by electro erosion and electrochemical machining methods and investigation of corrosion behavior on machining surfaces

    MEHMET ALBAŞKARA

    Doktora

    Türkçe

    Türkçe

    2022

    Makine MühendisliğiErciyes Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. EYYUP GERÇEKCİOĞLU

    DOÇ. DR. SELİS ÖNEL KAYRAN