Kendi bağlanabilen yeni bir akışkan kompozit geliştirilmesi
Improving a new self-adhesive flowable composite
- Tez No: 369933
- Danışmanlar: DOÇ. DR. MUSTAFA ÜLKER
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: makaslama bağlanma dayanımı, kendi bağlanabilen, fonksiyonel monomer, Dental bonding, Dental cementum, Dental materyaller, Dental stres analizi, Dental çimentolar, Kompozit reçineler, Monomerler, shear bond strength, self-adhesive, functional monomer, Dental bonding, Dental cementum, Dental materials, Dental stress analysis, Dental cements, Composite resins, Monomers
- Yıl: 2014
- Dil: Türkçe
- Üniversite: Selçuk Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı öncelikle farklı fonksiyonel monomerler (10-MDP, Bis –GPDM P, Bis-HEMA P, HEMA P, 4-META & 10-MDP + 4-META) içeren altı farklı deneysel kendi bağlanabilen akışkan kompozit üretmek ve dentin makaslama bağlanma dayanımlarını bir adet kendi bağlanabilen ticari akışkan kompozit (Vertise Flow, Kerr) ve üç adet all in one adeziv/akışkan kompozit kombinasyonu (Optibond All In One/Premise Flowable, Kerr; G Bond/G-Aenial Universal Flo, GC; Clearfil S3 Bond/Clearfil Majesty Flow, Kuraray) ile karşılaştımak idi. Ayrıca en yüksek dentin bağlanma dayanımına sahip deneysel kendi bağlanabilen akışkan kompozitin bazı fiziksel ve mekanik özellikleri de aynı ticari materyallerle karşılaştırıldı. 250 çürüksüz insan üçüncü molar dişi kullanılarak düz dentin yüzeyleri elde edildi. Dişler düz dentin yüzeyleri açıkta kalacak şekilde hızlı sertleşen akrilik rezin ile silindirik kalıplara gömüldü. Ticari bonding ajanlar ve kompozitler üretici firmaların talimatlarına göre uygulanırken, deneysel kendi bağlanabilen akışkan kompozitler, Vertise Flow gibi uygulandı (n=25). Materyaller silindirik şekilli plastik kalıplara yerleştirilerek rezin bloklar oluşturuldu. Örnekler makaslama bağlanma dayanım testi öncesinde 24 saat boyunca 37 ºC de distile su içerisinde bekletildi. Seçilen deneysel kendi bağlanabilen akışkan kompozitin ve diğer ticari akışkan kompozitlerin basma dayanımı 24 saat sonra 1 mm/ dk kuvvet uygulanarak belirlendi. Eğilme dayanımı standart üç nokta bükülme testi ile değerlendirildi. Yüzey pürüzlülüğü mekanik profilometre ile belirlendi. Örneklerin sertliği Vickers mikrosertlik testi kullanılarak incelendi. Polimerizasyon derecesi FTIR/ATR analizi ile belirlendi. Diş-adeziv ara yüzeyleri SEM ile incelendi. Verilerinin değerlendirilmesinde tek yönlü varyans analizi (one way ANOVA) ve Tukey HSD testi kullanıldı. Bütün self-etch adezivler, ticari ve deneysel kendi bağlanabilen akışkan kompozitlerden daha yüksek bağlanma dayanımı gösterdi (p<0.05). 10-MDP ve 4-META monomeri içeren deneysel kendi bağlanabilen akışkan kompozitin bağlanma dayanımı diğer bütün deneysel kendi bağlanabilen akışkan kompozitlerden ve Vertise Flow'dan daha yüksek idi.10-MDP ve 4-META monomeri içeren deneysel kendi bağlanabilen akışkan kompozitin basma dayanım, yüzey sertlik ve yüzey pürüzlülük değerleri diğer akışkan kompozitlerden daha düşük idi (p<0.05). 10-MDP ve 4-META monomeri içeren deneysel kendi bağlanabilen akışkan kompozitin eğilme dayanım ve polimerizasyon derecesi değerleri Vertise Flow'dan daha yüksek idi (p<0.05) Ticari kendi bağlanabilen akışkan kompozitlerden daha iyi bağlanma performansına sahip kendi bağlanabilen akışkan kompozit üretilebilir. Ancak, kompoziti dentine bağlamak için hala en iyi yol ayrı bir adeziv kullanmaktır.
Özet (Çeviri)
The aim of this study was first to prepare six experimental self-adhesive flowable composites containing different functional monomers (10-MDP, Bis –GPDM P, Bis-HEMA P, HEMA P, 4-META & 10-MDP + 4-META) and to compare their dentin shear bond strengths with one commercial self-adhesive flowable composite (Vertise Flow, Kerr) and three all-in-one adhesive/flowable composite combinations (Optibond All In One/Premise Flowable, Kerr; G Bond/G-Aenial Universal Flo, GC; Clearfil S3 Bond/Clearfil Majesty Flow, Kuraray). Some physical and mechanical properties of the experimental self-adhesive flowable composite having highest dentin bond strenght was also compared with same commercial materials. Flat dentin surfaces were created on 250 extracted caries free human third molars. The teeth were embedded in cylindrical molds with fast-setting acrylic resins leaving flat dentin surfaces uncovered. While commercial bonding agents and composites were applied according to the manufacturers' directions, experimental self-adhesive composites were applied as Vertise Flow (n=25). Resin blocks were created by packing the material into cylindrical shaped plastic. Specimens were stored in distilled water for 24 h at 37 ºC before shear bond strength testing. Compressive strengths of selected experimental self-adhesive flowable composite and other commercial flowable composites were determined after 24 h at a crosshead speed of 1 mm/ min. Flexural strength was evaluated through a standard three-point bending test. Surface roughness was determined with a mechanical profilometer. Vickers microhardness test was performed to investigate the hardness of the samples. Degree of polymerization was determined with FTIR/ATR analysis. Tooth-adhesive interfaces were analysed by SEM. . Data were analyzed with one-way ANOVA and Tukey's HSD tests. All self-etching adhesives showed higher bond strengths than did all commercial and experimental self-adhesive composites (p<0.05). The bond strength of an experimental self-adhesive composite containing 10-MDP and 4-META monomers was higher than those of other experimental self-adhesive composites and Vertise Flow. Compressive strenght, surface hardness and surface roughness values of the experimental composite containing 10-MDP and 4-META monomer was lower than other flowable composites (p<0.05).Flexural strenght and degree of polymerization values of the experimental composites containing 10-MDP and 4-META monomers was higher than Vertise Flow (p<0.05). A self-adhesive composite that is having better bonding performance than commercial ones can be prepared. However, using a separate adhesive system is still the best way to bond the composite to the dentin.
Benzer Tezler
- Reducing in-vehicle communication overload and enhancing efficiency in autonomous and electrical vehicles
Otonom ve elektrikli araçlarda araç içi iletişim yükünü azaltma ve etkinliğini artırma
YUNUS KAĞAN ÖZDEMİR
Yüksek Lisans
İngilizce
2024
Otomotiv Mühendisliğiİstanbul Teknik ÜniversitesiElektrik Mühendisliği Ana Bilim Dalı
PROF. DR. AHMET CANSIZ
- Synthesis of a novel formaldehyde-free crosslinker for waterborne binder dispersions in textile industry
Tekstil endüstrisindeki su bazlı bağlayıcı dispersiyonları için formaldehit salınımı yapmayan yeni bir çapraz bağlayıcının sentezi
GÖKÇE DEMİRCİOĞLU
Yüksek Lisans
İngilizce
2014
Polimer Bilim ve TeknolojisiBoğaziçi ÜniversitesiKimya Ana Bilim Dalı
DOÇ. DR. ALİ ERSİN ACAR
- New lightweight DoS attack mitigation techniques for RPL based IoT networks
RPL temelli IoT ağları için DoS saldırılarının etkisini azaltacak yeni teknikler
AHMET ARIŞ
Doktora
İngilizce
2019
Bilgisayar Mühendisliği Bilimleri-Bilgisayar ve Kontrolİstanbul Teknik ÜniversitesiBilgisayar Mühendisliği Ana Bilim Dalı
PROF. DR. SEMA FATMA OKTUĞ
- Çevre dostu su bazlı poliüretan nanokompozit verniklerin geliştirilmesi ve film özelliklerinin incelenmesi
Development of eco-friendly water-based polyurethane varnish and investigation of film properties
SONGÜL DUZAN
Yüksek Lisans
Türkçe
2022
Polimer Bilim ve TeknolojisiYalova ÜniversitesiPolimer Malzeme Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ YASEMİN TAMER