Biyoaktif cam ve hidroksiapatit ile modifiye edilmiş kompomer restoratif materyallerin mekanik ve demineralizasyona direnç özelliklerinin incelenmesi
To investigate the mechanical and demineralization resistance properties of compomer restorative materials modified with bioactive glass and hydroxyapatite particles
- Tez No: 384462
- Danışmanlar: PROF. DR. ELİF SEPET, PROF. DR. İSMAİL AYDIN
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Biyoaktif camlar, Demineralizasyon, Dental materyaller, Dental restorasyon, Dental stres analizi, Diş demineralizasyonu, Hidroksiapatitler, Mekanik özellikler, Bioactive glass, Demineralization, Dental materials, Dental restoration, Dental stress analysis, Tooth demineralization, Hydroxyapatites, Mechanical properties
- Yıl: 2014
- Dil: Türkçe
- Üniversite: İstanbul Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Pedodonti Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada kompomer restoratif materyallere (KRM) eklenen biyoaktif cam (BAC) ve hidroksiapatitin (HA), materyalin mekanik özelliklerini ve minenin demineralizasyona direncine etkisinin incelenmesi amaç olarak belirlenmiştir. KRM'nin içerisine ağırlıkça %1, %2, %3 ve %4 oranlarında HA ve BAC tozları eklenerek oluşturulan 9 deneysel grubun basma dayanımı, eğilme dayanımı ve kırılma tokluğu testleri gerçekleştirilmiştir. Demineralizasyona direncin incelenmesinde Sınıf V kavitelere materyaller uygulanarak, yapay çürük lezyonları oluşturulmuştur. Mine demineralizasyon oranının değerlendirilmesinde Vickers mikrosertlik yöntemi kullanılmıştır. Kırılma tokluğu testi örnekleri SEM ile incelenmiştir. Veriler Oneway Anova, Tukey HDS, paired sample t testleriyle istatistiksel olarak değerlendirilmiştir. Tüm gruplar içerisinde %4 HA grubunun basma dayanımının kontrol grubuyla benzer diğer gruplardan ise yüksek olduğu saptanmıştır (p<0.01). Farklı oranlarda BAC içeren grupların basma dayanımının düşük olduğu görülmüştür. %4 HA grubu hariç diğer gruplarda eğilme dayanımının düşük olduğu saptanmıştır (p<0.01). %1 HA ve %4 BAC ilavesi materyalin elastikiyet katsayısını anlamlı şekilde düşürmüştür. %3 HA, %3 ve %4 BAC ilavesi kırılma tokluğu değerlerini anlamlı derecede artırmıştır (p<0.05, p<0.01). HA ve BAC gruplarında restorasyona uzak mine dokusunda ve restorasyon kompleksinin en zayıf bölgesi olan komşu mine yüzeyinde kontrol grubuna oranla mine mikrosertlik değerleri yüksek olarak bulunmuştur. SEM incelemelerinde, deneysel KRM'nin yüzey görüntülerinin heterojen bir yapıda olduğu, nano-HA partiküllerinin kümeleşme eğilimi gösterdiği, BAC partiküllerinin dağınık bir şekilde lokalize olduğu ve örneklerin yüzeylerinin pürüzlü olduğu gözlenmiştir. Sonuç olarak, KRM'nin BAC ve HA ile modifiye edilmesinin katkı miktarına bağlı olarak materyalin mekanik özelliklerini etkilediği görülmektedir. KRM'ye BAC ve HA katılması materyale komşu ve uzak mine dokusunun demineralizasyona direnç etkisini artıran bir faktör olarak değerlendirilmiştir.
Özet (Çeviri)
The aim of this study was to evaluate the mechanical properties and demineralization resistance of enamel by adding hydroxyapatite (HA) and bioactive glass (BAC) in the compomer restorative materials.1%, 2%, 3% and 4% w/w HA and BAC particles were added mechanically to the compomers.The specimens prepared for compressive strength, flexural strength and fracture toughness tests were assigned to 9 experimental groups. To examine the resistance to demineralization Class V cavities were prepared on extracted teeth and restorated and artificial caries lesions were created. Changes in microhardness were used to evaluate the enamel demineralization rate; the final value was expressed as Vickers degrees. SEM was utilized to study surfaces of the specimens in the fracture toughness test. The statistical analyses were performed by Oneway Anova, Tukey HDS, paired sample t tests. Compressive strength and flexural strength of control group was significantly higher compared to the other groups except HA 4% (p<0.01). It was found that adding the BAC particles to the compomers decreases the compressive strength. The addition of 1% HA and 4% BAC resulted in a decrease in elastic modulus. The addition of 3% HA, 3% and 4% BAC significantly increased the fracture toughness of the material (p<0.05,p<0.01). HA and BAC groups revealed higher microhardness values at the exposed enamel and marginal exposed enamel than control group. SEM images of the experimental compomers showed a heterogeneous surface and agglomerated nano-HA particles weren't distributed homogeneously in the matrix. BAC and HA modified specimens showed a rougher surface. In conclusion, data has demonstrated that the addition of BAC and HA into compomers could affect the mechanical properties of the material and improve demineralization resistance properties of enamel, depending on the amount of additive.
Benzer Tezler
- Synthesis and characterization of bone cement based on new bioactive glass ceramic with pmma materials
Pmma malzemeleri ile yeni biyoaktif cam seramik esaslı kemik çimentosunun sentezi ve karakterizasyonu
ANMAR FOUAD KADHIM IBADI
Yüksek Lisans
İngilizce
2023
Metalurji MühendisliğiKarabük ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ALPER İNCESU
- Smart ph and thermosensitive injectable hydrogels: Chitosan – hydroxyapatite – heparin based functionalised biomaterials for bone regeneration
Akıllı, pH ve sıcaklığa duyarlı, enjekte edilebilir hidrojeller: Kemik yenilenmesi için kitosan – hidroksiapatit – heparin bazlı fonksiyonel biyomalzemeler
FATMA ZEHRA KOÇAK
Doktora
İngilizce
2021
BiyomühendislikLancaster UnıversıtyMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. IHTESHAM UR REHMAN
- Modifiye biyoaktif cam üretimi ve karakterizasyonu
Synthesis and characterization of modified bioactive glasses
ALKIN ESKİMERGEN
Yüksek Lisans
Türkçe
2023
Metalurji Mühendisliğiİstanbul Üniversitesi-CerrahpaşaMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ALİYE ARABACI
- Pirinç kabuğu kökenli silika içerikli MgO, SrO ve Al2O3 ilaveli 45S5 biyoaktif cam üretimi ve karakterizasyonu
Production of 45S5 bioactive glass obtained silica from rice husk ash doped with MgO,SrO and Al2O3 and its characterization
ZEYNEP ANIL KONUKOĞLU
Yüksek Lisans
Türkçe
2013
BiyomühendislikYıldız Teknik ÜniversitesiBiyomühendislik Ana Bilim Dalı
DOÇ. DR. SEVİL YÜCEL
- Biyoaktif cam ve hidroksiapatit içeren polikaprolakton nanoliflerin elektroeğirme yöntemi ile hazırlanması ve karakterizasyonu
Preparation and characterization of bioactive glass and hydroxyapatite containing polycaprolactone nanofibers by electrospinning method
RABİA KONYALI EKEN
Yüksek Lisans
Türkçe
2019
Polimer Bilim ve TeknolojisiManisa Celal Bayar ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. AYLİN MÜYESSER DELİORMANLI