Kağıt ve selüloz sanayi için stiren-akrilat kopolimeri esaslı yüzey tutkallama malzemesi geliştirilmesi

The development of styrene-acrylate copolymers based sizing materials for the paper and pulp industries

  1. Tez No: 398876
  2. Yazar: MEHLİKA ÖZDEMİR ALP
  3. Danışmanlar: PROF. DR. VELİ DENİZ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya Mühendisliği, Polimer Bilim ve Teknolojisi, Chemical Engineering, Polymer Science and Technology
  6. Anahtar Kelimeler: Emülsiyon, Kağıt ve Selüloz, Polimerizasyon, Stiren-Akrilat, Yüzey Tutkallama, Emulsion, Paper and Pulp, Polymerization, Styrene-Acrylate, Surface Sizing
  7. Yıl: 2015
  8. Dil: Türkçe
  9. Üniversite: Kocaeli Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 89

Özet

Bu çalışmada, polimerik yüzey tutkallama malzemesi olarak kullanılmak üzere stiren--2 etil hekzil akrilat kopolimerinin emülsiyon polimerizasyonu ile üretimi gerçekleştirilmiştir. Monomer olarak stiren (%70) ve 2-etil hekzil akrilat (%30) stokiyometrik oranda kullanılmıştır. Emülgatör olarak dört farklı etoksile amin çeşidi seçilmiş ve bu emülgatörler kopolimerizasyonda üç farklı oranda kullanılmıştır. Bu sistemde başlatıcı olarak potasyum persülfat (K), toplam monomer miktarının %1'i oranında kullanılmış ve on iki farklı kopolimer sentezlenmiştir. Bu deneyler daha sonra başlatıcı çeşidi değiştirilerek yani 2,2'-Azobis(2-methylpropionamidine) dihydrochloride (A) kullanılarak tekrar edilmiş ve oniki adet daha farklı kopolimer geliştirilmiştir. Elde edilen emülsiyon polimerlerinin özelliklerinin belirlenmesi için, mol kütlesi tayini, yapısal analiz ve ısıl karakterizasyon teknikleri kullanılmıştır. Daha sonra üretilen stiren-2 etil hekzil akrilat kopolimerleri kağıt kaplama malzemesi olarak kullanılmış ve bu malzemenin yüzey özelliklerine etkileri incelenmiştir. Genel olarak, K başlatıcılı ve ağırlıkça % 3 emülgatör içeren tepkimeler hariç, tüm sentez tepkimelerinde homojen emülsiyonlar elde edilmiştir. Tg değerlerine bakıldığı zaman, emülgatör miktarı %3'ten, %7'ye çıkarıldığında Tg değerleri K başlatıcı ile artarken A başlatıcı ile azalmıştır. Aynı emülgatör tipinde A başlatıcı kullanılan örneklerde K başlatıcısına göre daha küçük tanecik (partikül) yarıçapı değerleri gözlenmiştir. SEM sonuçları incelendiğinde, üç farklı emülgatör ile elde edilen kopolimerler ile kaplanan kağıtların lifli yapılarını korudukları ve benzer görünüme sahip oldukları gözlenmiştir. Tüm kopolimerler arasında en düşük sıvı emiciliği E-3 emülgatörünün %10 oranında kullanılmasıyla ve A başlatıcı ile üretilen kopolimer (E-3/10/A) ile kaplanan kağıtta elde edilmiştir.

Özet (Çeviri)

In this study, styrene-2-ethyl hexyl acrylate copolymer based surface sizing materials were developed for using paper sizing materials by emulsion polymerization. Styrene (30%) and 2-ethyl hexyl acrylate(70%) were used as monomers at stokiometric rate. Four different ethoxylated amine type as emulsifier at three different level were used. Potassium persulfate (K) was charged as initiator by weight of the total amount of monomer system at 1% rate and twelve different copolymer were synthesized. Initiator type has been changed to 2,2'-Azobis(2-methylpropionamidine) dihydrochloride (A) and twelve copolymer samples were obtained from this set. The synthesized polymer properties were characterized by using molecular weight determination, thermal characterization and structural analysis techniques. Then, synthesized styrene-2 ethylhexyl acrylate copolymer used as a paper sizing material on the paper and the performance of sized papers were characterized. In general, homogenous emulsions were obtained in all synthesis reaction except for in case of K initiator and 3% by weight emulsifier were used. While copolymer Tg values with initiator K increased by decreasing emulsifier amount, Tg values of copolymer with initiator A decreased. Copolymer samples with initiator A had lower particle sizes than samples with initiator K at same emulsifier were used. When SEM results are analyzed that the paper coated with synthesized copolymers with three different emulsifier retained their fibrous structures and had similar appearances. The lowest liquid absorbency was found when E-3 emulsifier at 10% wt. and initiator A (E-3/10/A) were used among the all of copolymers.

Benzer Tezler

  1. Endüstri mirası alanları ve tarihi kentsel peyzaj (HUL) ilişkisi, Bursa merinos tekstil fabrikası ve İzmit SEKA kağıt fabrikası örneği

    Industrial heritage sites and historic urban landscape (HUL) relations, Bursa merinos textile factory and Izmit SEKA paper factory cases

    NERGİS YILDIRIM

    Yüksek Lisans

    Türkçe

    Türkçe

    2020

    Şehircilik ve Bölge PlanlamaMimar Sinan Güzel Sanatlar Üniversitesi

    Şehir ve Bölge Planlama Ana Bilim Dalı

    DOÇ. DR. ADEM ERDEM ERBAŞ

  2. Cumhuriyet dönemi kâğıt sanayi (1923-1973)

    Turkey's paper industry in the Republican era (1923-1973)

    MEHMET TUĞTİGİN ŞEN

    Doktora

    Türkçe

    Türkçe

    2022

    TarihAnkara Üniversitesi

    Atatürk İlkeleri ve İnkılap Tarihi Ana Bilim Dalı

    PROF. DR. NECDET AYSAL

  3. Türkiye selüloz ve kâğıt fabrikaları işletmelerinin (SEKA) Türkiye ekonomisine katkıları (1970-1990)

    Contributions of Turkish cellulose and paper factories (SEKA) to Turkish economy (1970-1990)

    YAVUZ USTA

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    EkonomiKocaeli Üniversitesi

    İktisat Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ MEHMET EMİN YARDIMCI

  4. Seka I. Kağıt Fabrikası'nın mimari analizi ve çağdaş hayata adaptasyonu için öneriler

    Architectural analysis of Seka I. Paper Factory and suggestions for adaptation to modern life

    REYHAN ÇÖMLEKÇİOĞLU KARTAL

    Yüksek Lisans

    Türkçe

    Türkçe

    2009

    MimarlıkGebze Yüksek Teknoloji Enstitüsü

    Mimarlık Ana Bilim Dalı

    YRD. DOÇ. DR. ELİF ÖZLEM AYDIN

  5. Responding the challenges of preserving an industrial network as heritage: Turkey Cellulose and Paper Factories (SEKA)

    Bir endüstri ağını miras olarak korumak: Türkiye Selüloz ve Kağıt Fabrikaları (SEKA)

    BİLGE KÖSE

    Doktora

    İngilizce

    İngilizce

    2018

    MimarlıkOrta Doğu Teknik Üniversitesi

    Mimarlık Ana Bilim Dalı

    DOÇ. DR. AYŞE GÜLİZ BİLGİN ALTINÖZ