Çevre sıcaklığı ve kaynak ön tav ısıl işleminin polietilen doğalgaz borularının elektrofüzyon kaynağına etkisi
An effect of environment temperature and preheat treatment on the electrofusion welding of polyethylen natural gas pipes
- Tez No: 405852
- Danışmanlar: PROF. DR. RAMAZAN KAÇAR
- Tez Türü: Yüksek Lisans
- Konular: Enerji, Polimer Bilim ve Teknolojisi, Petrol ve Doğal Gaz Mühendisliği, Energy, Polymer Science and Technology, Petroleum and Natural Gas Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2015
- Dil: Türkçe
- Üniversite: Karabük Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İmalat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Doğal gaz ve su dağıtım hatlarında kullanılan polietilen boruların elektrofüzyon kaynağıyla birleştirmeleri, standartlarda -5 ºC ile +30 ºC sıcaklık aralığında yapılması önerilmektedir. Bu çalışmada çevre sıcaklığının birleştirme özellikleri üzerindeki etkisi araştırılmıştır. Bu amaçla yüksek yoğunluklu (PE100) ve orta yoğunluklu (PE80) borular elektrofüzyon kaynak yöntemi ile farklı çevre sıcaklıklarında (oda sıcaklığı, 0, -10, -20 ve -30 ºC) ve ön tav işlemi (60 ve 80 ºC) uygulanarak birleştirilmiştir. Birleştirmelere standartlarına göre sızdırmazlık ve ezme testi yanısıra bağlantının dayanımını belirlemek için tekli ve çiftli soyma-ayırma testi uygulanmıştır. Böylece birleştirmelerin ayrılma tokluğu, K, ve ayrılmak için normal enerji, EN, hesaplanmıştır. İlaveten kaynak numunelerimizin ani yüklere karşı dayanımını ölçmek için izod darbe dayanım testi gerçekleştirilmiştir. Sonuç olarak artan çevre sıcaklığına bağlı olarak kaynak bölgesindeki daha fazla oluşan kristal yapı miktarının dayanımı arttırdığı ancak şekillendirilebilirliği azalttığı tespit edilmiştir. Ön tav ısıl işlemi düşük çevre sıcaklıklarında elde edilen birleştirmelerin özelliklerine olumlu katkıda bulunurken, yüksek çevre sıcaklıklarında elde edilen bağlantının dayanımını olumsuz etkilediği belirlenmiştir.
Özet (Çeviri)
The standard used in electrofusion welding of polyethylene natural gas and water transportation network pipes, recommends that welds need to be carried out at the temperature range between -5 ºC and +30 ºC. In this study, an effect of the environment temperature on the properties of weldment is investigated. For this purpose, high density (PE100) and medium density (PE80) pipes were joined with electrofusion welding method at the various environment temperatures (room temperature, 0, -10, -20 and -30 ºC) and by using preheat temperatures (60 and 80 ºC). According to standard, leaking and crush decohesion test have been carried out and the peel decohesion and double peel decohesion tests have been also applied for determining the strength of weldment. Thus, decohesion toughness, K, and nominal energy, EN, for the decohesion of weldment was calculated. Impact resistance of weldments were also investigated by Izod impact test. Conclusively, the strength of the weldment increased while the ductility was decreased by increasing amount of crystalline in weld region associated with increasing environment temperature. It was determined that the preheat treatment process affected positively the features of weldment which was joined at low environment temperature however the strength of weldments joined at room temperature was affected negatively.
Benzer Tezler
- Yeni Cami'nin akustik açıdan performans değerlendirmesi
Evaluation of the acoustical performance of the New Mosque
EVREN YILDIRIM
Yüksek Lisans
Türkçe
2003
Mimarlıkİstanbul Teknik ÜniversitesiMimarlık Ana Bilim Dalı
PROF. DR. SEVTAP YILMAZ DEMİRKALE
- Discovery of novel enzymes using proteomic approaches
Proteomik yaklaşımlar kullanılarak yeni enzimlerin keşfi
MERVE ÖZTUĞ KILINÇ
Doktora
İngilizce
2021
Biyokimyaİstanbul Teknik ÜniversitesiMoleküler Biyoloji-Genetik ve Biyoteknoloji Ana Bilim Dalı (disiplinlerarası)
PROF. DR. NEVİN GÜL KARAGÜLER
DOÇ. DR. MÜSLÜM AKGÖZ
- Burdur ili mermer sektörünün kurumsal ve ekonomik yapısı
İnstitutional and economic structure of marble sector in burdur
AHMET SARITAŞ
- Isıl dönüştürücülerin değişken kaynak ve çevre sağlığı şartlarında termodinamik analizi
Başlık çevirisi yok
H.ALİ ÖZEN
- AISI P11 VE AISI P91 kalite dikişsiz boru çeliklerinin mekanik özelliklerine gerilme giderme tavlaması sıcaklığının etkisi
Effect of stress relief annealing temperature on mechanical properties of AISI P11 VE AISI P91 grade seamless pipe steels
CANER KIRBAŞ
Yüksek Lisans
Türkçe
2014
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. MURAT BAYDOĞAN