Siirt yöresinde farklı santrallerde üretilen betonların mekanik ve fiziksel özelliklerinin incelenmesi
Mechanical and physical analysis of concrete produced in different facilities of Siirt region
- Tez No: 432840
- Danışmanlar: PROF. DR. SERVET YILDIZ
- Tez Türü: Yüksek Lisans
- Konular: Teknik Eğitim, Technical Education
- Anahtar Kelimeler: Hazır Beton, Siirt Bölgesi, Katkı, ready mixed concrete, Siirt, Supplement
- Yıl: 2016
- Dil: Türkçe
- Üniversite: Fırat Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Yapı Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 108
Özet
Bu çalışmada Siirt Yöresinde farklı santrallerde üretilen hazır betonların mekanik ve fiziksel özellikleri incelenmiştir. Yörede faaliyet gösteren beton santralleri A Beton Santrali, B Beton Santrali ve C Beton Santrali olarak adlandırılmıştır. Bu santrallerde üretilen betonlardan C25 beton sınıfı üzerinde; basınç, porozite, yüksek sıcaklık, donma-çözülme ve eğilmede çekme deneyleri uygulanmıştır. Bu deneyler için 28 günlük numuneler kullanılmış ve numunelerin 28 günlük dayanım değerleri dikkate alınarak gerekli karşılaştırma işlemleri gerçekleştirilmiştir. Her üç santralde üretilen betonların 28 günlük basınç dayanımlarını sağladıkları görülmüştür. C Beton santralinde üretilen betonun porozite değerinin %8,46 olduğu ve diğer santrallerde üretilen betonların porozite değerlerinden daha düşük olduğu tespit edilmiştir. Donma-çözülme deneyinde A Beton santralinde üretilen betonların ortalama basınç dayanım değerlerinde %11,73, B Beton Santralinde üretilen betonların ortalama basınç dayanım değerlerinde %7,33, C beton Santralinde ise %5,52 oranında bir basınç dayanım kaybı tespiti yapılmıştır. Donma-çözülme olayının beton numuneler üzerinde bozulmalara neden olduğu görülmüş, ancak; üretilen betonların donma-çözülmeden fazla etkilenmediği tespit edilmiştir. Yüksek sıcaklık deneyinde numuneler 300-400-500-600-800°C sıcaklıklara maruz bırakılmışlardır. Sıcaklık derecesinin artması ile birlikte basınç dayanım kaybının her üç santralin ürettiği betonda da arttığı görülmüş, fakat dayanım kaybının en fazla 600-800°C'de gerçekleştiği ve dayanım kaybının %70,4 seviyesine kadar ilerlediği görülmüştür. Elde edilen verilere göre üretilen betonların çevresel faktörlerin zararlı etkilerinin azaltılabilmesi için su/çimento oranının iyi ayarlanması, uygun katkı maddelerinin ve agregaların iyi seçilmesi gerektiği tespiti yapılmıştır. Tesiste üretilen beton her ne kadar standartlar ve talep edilen sınıfta üretilse dahi, laboratuvar şartlarında bırakılan numune sonuçları ile yetinilmemeli ve asıl olan beton dökümü ve sonrasında yapılması gereken bakım işlemlerinin son derece önemsenmesi gerektiği kanaatine varılmıştır.
Özet (Çeviri)
This study investigated the physical and mechanical properties of ready mixed concrete produced in different batch plants in Siirt city. The batch plants were named as A, B, and C. C25 concrete that was produced in these batch plants were tested under pressure, porosity, high temperature, freezing/thawing and bending. Samples of 28 days were used for these experiments and the endurance values of 28 days were compared under necessary attention. İt was seen that the produced concrete at every three hours covered 28-days pressure resistance. Also, it was detected that the concrete produced in C batch plant had a porosity value of 8.46%, which is lower than the porosity values belonging other batch plants. İn the experiment of freezing/thawing, it was recorded that average pressure strength of concrete produced in plant A is 11.73% while it was 7.33% in plant B and 5.52% in plant C. It was discovered that freezing/thawing led to deterioration on concrete samples, but the deterioration was not significant. In high temperature experiments, the samples were exposed to 300-400-500-600-800°C. Together with temperature increase, pressure strength-loss on concrete produced at all plants also increased, but the top loss was seen at the degree of 600-800 with a rate of 70.4% strength-loss. According to the acquired data, in order to decrease deterioration effect of environment on concrete, it was concluded that water/cement ratio should be adjusted carefully, and suitable supplemental additives and aggregates should be selected meticulously. No matter how quality had the concrete produced in the plants, only laboratory results of the samples would not be sufficient. Therefore, it was concluded that necessary curing process after concrete placing is highly crucial and shall be cared.
Benzer Tezler
- Siirt yöresinde yetiştirilen bazı üzüm çeşitlerinin göz verimliliklerinin belirlenmesi ve farklı göz şarjı uygulamalarının verim ve kaliteye etkisi
Determination of bud efficiency and effects of crop loading on yield and quality factors of some grape varieties grown in Siirt province
TAYFUN DÖLEK
Yüksek Lisans
Türkçe
2017
ZiraatSiirt ÜniversitesiBahçe Bitkileri Ana Bilim Dalı
YRD. DOÇ. DR. HALİT SEYFETTİN ATLI
YRD. DOÇ. DR. NURHAN KESKİN
- Siirt yöresinde halk tarafından şalgam olarak tüketilen turp bitkisinin metal içeriği ve biyolojik aktivitelerinin belirlenmesi
Determination of the metal content and biological activities of the radish plant consumed as a turnip by the public in Siirt region
HASAN ÖZDEN
- Siirt yöresinde yetiştirilen incir (Ficus carica L.) genotiplerinin trnL-F bölgesine bağlı genetik karakterizasyonu
Genetic characterization of linked to trnL-F region of figs (Ficus carica L.) genotypes that grown in the Siirt geography
BAHAR ÖZDEMİR
Yüksek Lisans
Türkçe
2019
ZiraatSiirt ÜniversitesiBahçe Bitkileri Ana Bilim Dalı
PROF. DR. KORAY ÖZRENK
PROF. DR. FERİT ÇELİK
- Siirt yöresinde doğal olarak yetişen Cynara syriaca B. tipleriile Cynara scolymus L. türü enginarlarında etken madde tespiti
Determination of active ingredient in the Cynara scolymus L. artichoke species with Cynara syriaca B. species growing naturally in Siirt region
YUNUS AKTAR
Yüksek Lisans
Türkçe
2019
ZiraatSiirt ÜniversitesiBahçe Bitkileri Ana Bilim Dalı
DR. ÖĞR. ÜYESİ MUHEMET ZEKİ KARİPÇİN
PROF. DR. SUAT ŞENSOY
- Siirt yöresinde yetişen sert kabuklu meyve türlerinin pazarlama ve tüketim olanaklarının araştırılması
Investi̇gati̇on of the marketi̇ng and use opportuni̇ti̇es growi̇ng nuts speci̇es i̇n si̇i̇rt regi̇on
MERVE KARDEŞ
Yüksek Lisans
Türkçe
2017
ZiraatSiirt ÜniversitesiBahçe Bitkileri Ana Bilim Dalı
DOÇ. DR. KORAY ÖZRENK
DOÇ. DR. FERİT ÇELİK