Demir-çelik endüstrisinde kullanılan karbon bağlı alümina-zirkon-silikat (AZS) sürgü plakalarının geliştirilmesi
Developing of carbon bonded alumina-zircon-silicate slide gate plates used in iron-steel industry
- Tez No: 447020
- Danışmanlar: DOÇ. TİJEN ENNİL KÖSE, PROF. DR. ALPAGUT KARA
- Tez Türü: Yüksek Lisans
- Konular: Kimya Mühendisliği, Metalurji Mühendisliği, Mühendislik Bilimleri, Chemical Engineering, Metallurgical Engineering, Engineering Sciences
- Anahtar Kelimeler: Akış Kontrol Sistemi, Sürgü Plakası, Karbon Bağlı Refrakterler, Flow Control System, Slide Gate Plate, Carbon Bonded Refractories
- Yıl: 2016
- Dil: Türkçe
- Üniversite: Eskişehir Osmangazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Kimyasal Teknolojiler Bilim Dalı
- Sayfa Sayısı: 106
Özet
Refrakter tüketiminin en fazla olduğu sanayi kuruluşu olan demir-çelik endüstrisinde çelik üretimindeki teknolojik gelişmelere paralel olarak daha uzun ömürlü ve dayanımı yüksek refrakter malzeme talebi de artmaktadır. Çelik üretim prosesi boyunca refrakter malzeme tüketiminin en fazla olduğu proseslerden biri de sıvı akış kontrol sistemleridir. Burada refrakterden beklenen özellikler üretilen çelik kalitesinden bağımsız olarak yüksek erozyon, korozyon direnci, ısıl şoka dayanım, mekanik aşınmaya dayanıklı plakalar olmasıdır. Üstün ısıl şok direnci ve kimyasal korozyona karşı dayanımı açısından karbon bağlı sürgü plakaları kullanımda geleneksel seramik bağlı sürgü plakalarına göre daha çok tercih edilmektedir. Bu tez kapsamında, endüstriyel ürünün elde edilmesi için yapılan literatür araştırmasının ardından uygun hammaddeler seçilerek deneysel çalışmalar başlatılmıştır. Daha sonra, uygun ürün eldesi için farklı parametrelerde reçete tasarımları yapılmıştır. Tüm parametreler için şekillendirme basıncı 1000 kg/cm2, 1200°C'de tünel fırında anti-oksidatif atmosferde pişirim uygulanmıştır. Belirlenen ana parametreler ise; harman içerisinde kullanılacak zirkon miktarı, anti-oksidant çeşidi ve miktarı son olarak yapıda karbon bağını oluşturacak karbon çeşidi ve miktarıdır. Burada belirlenen parametreler ile varılması hedeflenen amaç şu şekildedir: Parametre 1; zirkon miktarı ile ısıl genleşmesi ölçülerek ısıl şoka dayanımının yorumlanmasıdır. Parametre 2; kullanılacak anti-oksidantların hem karbonun oksidasyonunun engellenmesi hem de yapıda oluşan viskırların daha yüksek dayanım sağlaması yönünde incelenmesidir. Parametre 3; kullanılan karbon kaynağının çeşidi ve miktarı ile yapıda oluşan karbon bağının ve viskır oluşumunun gözlenmesidir. Optimum özelliklerin elde edildiği nihai ürün reçetesi ile üretilen sürgü plakasının üç farklı demir-çelik fabrikasında endüstri denemeleri yapılmıştır. Denemeler sonucunda hedeflenen döküm ömürleri karşılanmıştır.
Özet (Çeviri)
Heavy metal industry is one of the biggest consumer of refractory materials among other industries. The industry require more durable and long-lived refractory material in consequence of developing technology increasingly. One of the most consumable system of the refractory is flow control mechanisms such as slide gate plate throughout the steel manufacturing process. Beside of steel manufacturing quality, high corrosion resistance, thermal shock resistance and chemical corrosion resistance are required characters of slide gate plate. Carbon based slide gate plates are more preferable than ceramic based gate plates due to having superior thermal shock resistance and chemical corrosion. In order to obtain equivalent characteristic of material, experimental studies were initiated right after researching articles. Due to obtaining proper product, designed different recipes using tunnel type furnace under 1000 kg/cm2 forming pressure at 1200°C in antioxidant environment. Determined main parameters are; rate of zirconia in blend, rate and type of antioxidant, rate and type of carbon that making carbon bonds in the structure. Aims of the project are; 1) Interpreting of thermal shock resistance of material, measuring thermal expansion trying different zirconia rate. 2) Investigating effects of antioxidant that prevent carbon oxidation and also,“whisker”occurs in material structure that increasing high resistance. 3) Observing carbon bond and“whisker”using different rate and type of carbon. Slide gate plates were tried in 3 different iron and steel plants to validate optimum properties of refractory material.
Benzer Tezler
- Tavas manganez cevherlerinden laboratuvar tipi ark fırınında ferromanganez/ferrosilikomanganez üretim koşullarının belirlenmesi
Başlık çevirisi yok
MEHMET EMİN ARI
- Sıcak haddelenmiş çelikleri işleyen tesislerde biriken demir esaslı yağlı çamurdan demirli hammadde üretilmesi
Production of ferrous raw materials from iron based oily mill sludge released in the facilities processing hot rolled steels
SAMET BALLI
Yüksek Lisans
Türkçe
2019
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA KELAMİ ŞEŞEN
- Gümrük Birliği sürecinde Türkiye'nin demir çelik ticareti performansı: 1996 - 2014
Iron and steel trade performance of Turkey in the Customs Union process: 1996 - 2014
YASİN BIYIK
Doktora
Türkçe
2019
Ekonometriİstanbul Teknik Üniversitesiİşletme Mühendisliği Ana Bilim Dalı
PROF. DR. NEDİME LERZAN ÖZKALE
- Yüksek fırın baca tozlarının ferromanganez üretiminde kullanılması
Utilization of blast furnace flue dust in ferromanganese production
İBRAHİM ÖZDEMİR
Yüksek Lisans
Türkçe
2015
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA KELAMİ ŞEŞEN
- Understanding the unusual passive behaviour of high strength hybrid steel in corrosive environments
Yüksek mukavemetli hibrit çeliğin korozif ortamlarda olağandışı pasif davranışının anlaşılması
BESTE PAYAM
Yüksek Lisans
İngilizce
2022
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ CEM ÖRNEK