Son yıllarda geliştirilen 4 farklı endodontik biyomateryalin simüle edilmiş immatür dişlerin kırılma direncine etkisinin kalsiyum hidroksit ile karşılaştırmalı olarak değerlendirilmesi

Comparative evaluation of recently developed four endodontic biomaterials with calcium hydroxide regarding their effect on the fracture resistance of immature simulated teeth

PDF İndir

  1. Tez No: 480912
  2. Yazar: ASLI SOĞUKPINAR
  3. Danışmanlar: YRD. DOÇ. DR. VOLKAN ARIKAN
  4. Tez Türü: Diş Hekimliği Uzmanlık
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2017
  8. Dil: Türkçe
  9. Üniversite: Kırıkkale Üniversitesi
  10. Enstitü: Diş Hekimliği Fakültesi
  11. Ana Bilim Dalı: Pedodonti Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 155

Özet

Bu tez çalışmasında; geleneksel MTA ve son yıllarda üretilen MTA türevi kalsiyum silikat içerikli materyaller olan Biodentine, Micro-Mega MTA ve NeoMTA Plus'ın in-vitro şartlarda simüle edilmiş immatür dişlerde kanal dolgusu olarak kullanımları sonrası, dişlerin kısa ve uzun dönem kırılganlıklarına etkilerinin kalsiyum hidroksit [Ca(OH)2] uygulanmış ve hiçbir uygulama yapılmamış sağlam dişlerle karşılaştırmalı olarak değerlendirilmesi amaçlanmıştır. Araştırmamızda 270 adet çürüksüz daimi üst keser dişi rastgele 4 adet çalışma, 1 negatif ve 1 pozitif kontrol olmak üzere 6 gruba (n=45), ayrıca her grup kendi içinde 2 hafta, 2 ay ve 1 yıl olmak üzere 3 alt gruba (n=15) ayrılmıştır. Örneklerin immatür dişleri simüle edecek şekilde prepare edilmesinin ardından çalışma grubundaki dişler; ProRoot MTA (MTA-PR), Biodentine (BD), Micro-Mega MTA (MM-MTA) ve NeoMTA Plus (NEO) ile Pozitif Kontrol grubundaki dişler ise kalsiyum hidroksit [Ca(OH)2] ile doldurulmuştur. Negatif Kontrol Grubunu oluşturan sağlam dişlere hiçbir işlem uygulanmamıştır. Her bir grubun 2 hafta, 2 ay ve 1 yıl olan 3 alt grubu (n=15) salin solüsyonunda 37 °C'de tutulmuştur. Bekleme sürelerinin ardından örnekler akril bloklar içine mine-sement sınırı ile akrilik rezin arasında 2mm mesafe olacak şekilde gömülmüştür. Daha sonra Instron cihazına yerleştirilerek kronların uzun aksına 45° açı ile 1mm/dk. hızla kuvvet uygulanmış ve kırılma anındaki pik makaslama kuvvetleri kaydedilmiştir. Sonuçlar istatistiksel olarak hem materyal hem de bekleme süreleri açısından karşılaştırılmıştır. Kırılma direnci ölçümlerine ait dağılımın normale yakın olup olmadığı Kolmogorov-Smirnov testiyle, varyansların homojenliği ise Levene testiyle araştırılmıştır. Tanımlayıcı istatistikler medyan (çeyrekler arası genişlik) biçiminde ifade edilmiştir. Gruplar arasında kırılma direnci düzeyleri yönünden farkın önemliliği Kruskal Wallis testiyle araştırılmıştır. Kruskal Wallis test istatistiği sonuçlarının önemli bulunması halinde Conover'in çoklu karşılaştırma testi kullanılarak farka neden olan durum(lar) tespit edilmiştir. Aksi belirtilmedikçe p

Özet (Çeviri)

In this thesis study; it was aimed that comparative assessment of traditional MTA and recently developed MTA-derived calcium silicate containing materials such as Biodentine, Micro-Mega MTA and NeoMTA on the short-term and long term fragility of calcium hydroxide [Ca(OH)2] treated and healthy teeth, after using as a root filling material in-vitro simulated immature teeth. Two hundred and seventy extracted sound maxillary incisors were divided into 6 groups (n=45) such as randomly chosen 4 experimental groups, 1 negative control and 1 positive control and each groups were divided into 3 subgroups (n=15) as 2 weeks, 2 months and 1 year. After preparation of the specimens to simulate the immature teeth, teeth in study experimental groups were filled with ProRoot MTA (MTA-PR), Biodentine (BD), Micro-Mega MTA (MM-MTA) and NeoMTA Plus (NEO), and positive control group [Ca(OH)2] was filled with Ca(OH)2. There was no treatment applied to negative control group (healthy teeth). The waiting intervals were 2 weeks, 2 months and 1 year for each group of 3 subgroups (n = 15), and the samples were held in saline at 37 °C. According to the storage period, specimens were embedded in acrylic resin leaving a 2mm gap between cementoenamel junction. Then, the specimens were loaded at a crosshead speed of 1mm/min to the long axis of the crowns at an angle 45° in an Instron testing machine and the peak loads up to fracture were recorded. The results were compared statistically in terms of both materials and storage times. The Kolmogorov-Smirnov test was used to understand if the dispersion related to the fracturing resistance measurements are normal or not, and Levene test is used for the homogeneity of variations. Descriptive statistics were expressed in median (width between quarters). Kruskal Wallis test was used to investigate the significance of differences between groups in terms of fracture resistance levels. When results of Kruskal Wallis test statistic became significant, Conover's multiple comparison tests was used for identifying the situations causing the difference. Results for p

Benzer Tezler

  1. Tez No

    443758

    Farklı güncel nikel titanyum döner alet sistemleri ile şekillendirilmiş kök kanallarındaki smear tabakasının uzaklaştırılmasında Er,CR:YSGG ve Er:YAG lazerlerin etkinliklerinin karşılaştırılması

    Comparison of the smear layer removal efficiency of Er,CR:YSGG and Er:YAG laser irridation in root canals prepared with different novel nickel titanium rotary systems

    FATİH AKSOY

    Doktora

    Türkçe

    Türkçe

    2016

    Diş HekimliğiGaziantep Üniversitesi

    Endodonti Ana Bilim Dalı

    PROF. DR. TAYFUN ALAÇAM

    YRD. DOÇ. UĞUR AYDIN

  2. Tez No

    79682

    Basınçlı teknikle uygulanan dökülebilir seramikle yapılan pivolu kronların invivo ve invitro olarak incelenmesi

    Research on crowns with pivot: Applied with castable pressurized ceramic as invivo and invitro

    BURCU GÜNDOĞAR

    Doktora

    Türkçe

    Türkçe

    1999

    Diş HekimliğiGazi Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. LEVENT NALBANT

  3. Tez No

    448889

    Kök kanal şekillendirmesi esnasında oluşan streslerin sonlu elemanlar analizi yöntemi ile değerlendirilmesi

    Evaluate the stresses generated during root canal shaping by finite element analysis method

    HAZAL EDA ÖZDİLER

    Doktora

    Türkçe

    Türkçe

    2016

    Diş Hekimliğiİstanbul Üniversitesi

    Endodonti Ana Bilim Dalı

    PROF. DR. FEHMİ RAİF ERİŞEN

  4. Tez No

    462378

    Yeni jenerasyon restoratif materyaller kullanılarak bilgisayar yardımıyla tasarlanan ve üretilen kron restorasyonların, 3 boyutlu görüntü hizalama yöntemiyle klinik aşınma miktarlarının incelenmesi

    Examining clinically surface wear amount of crown restorations produced by CAD&CAM method using new jeneration restorative material with 3 dimensional image aligning

    DİDEM OĞUZ

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2017

    Diş HekimliğiEge Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. AKIN ALADAĞ

  5. Tez No

    618417

    Evaluating the performance of different continous vector representation methods for turkish words

    Türkçe sözcükler için farklı sürekli vektör temsilyöntemlerinin başarım değerlendirmesi

    GÖKHAN GÜLER

    Yüksek Lisans

    İngilizce

    İngilizce

    2020

    Bilgisayar Mühendisliği Bilimleri-Bilgisayar ve Kontrolİstanbul Teknik Üniversitesi

    Bilgisayar Mühendisliği Ana Bilim Dalı

    DOÇ. DR. AHMET CÜNEYD TANTUĞ

Geri Dön