Epoksi bazlı çar kompozitlerinin özelliklerine poli(etilen tereftalat) atığının farklı piroliz sıcaklığının etkisi

Effect of different pyrolysis temperature of the poly(ethylene terephthalate) waste on the properties of epoxy based char composites

  1. Tez No: 489379
  2. Yazar: ALİZE YÜCEL
  3. Danışmanlar: PROF. DR. GÜLNARE AHMETLİ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya Mühendisliği, Chemical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2018
  8. Dil: Türkçe
  9. Üniversite: Selçuk Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 88

Özet

Bu çalışmada önemli bir katı atık problemi olan termoplastik atıklardanyıkanmamış ve yıkanmış poli(etilen tereftalat) türü plastik, atıklar epoksi kompozit malzemelerin hazırlanması için 300-700 ºC aralığında piroliz edilerek ham madde olarak geri dönüştürülmüştür. Yapılan piroliz deneyleri sonucunda, piroliz katı ürünü olan çar verimi yıkanmamış ve yıkanmış grup için sırasıyla %18.32-20.15 ve %17.13-37.89 değerlerini alarak piroliz sıcaklığına bağlı olarak azalmıştır. Çarların karakterizasyonu için FTIR, TGA ve SEM analizleri kullanılmıştır. Piroliz sıcaklığı arttıkça çarın aromatik yapısı ve buna bağlı olarak termal dayanımı artmıştır. Çarlarla elde edilen kompozitlerin mekanik, termal, su sorpsiyonu ve elektriksel iletkenlik özelliklerine atıkplastik yıkama işleminin ve çar oranının etkisi incelenmiştir. Kompozitlerin morfolojik yapıları SEM ile incelenmiştir. Çekme dayanımı, tüm piroliz sıcaklıklarında elde edilen çar oranına bağlı olarak artmış ve tüm piroliz sıcaklıklarında PETyıkanmamış çarı kompozitleri için en uygun oran %30 iken PETyıkanmış çarı kompozitleri için %50'lik oran en uygun oran olarak belirlenmiştir. Bu oranlardaki çekme dayanımı değerleri yıkanmamış ve yıkanmış PET çarları için sırasıyla 97-136 MPa ve 94-124 MPa aralığında değişmiştir. Kompozitlerin TGA analizi, PET çarlarının termal dayanıklılığının önemli ölçüde arttığını göstermiştir. Tüm kompozitler yarıiletken bulunup iletkenlikleri 10-8-10-3 S cm-1aralığında değişmiş ve piroliz sıcaklığının artması ile elektriksel iletkenliğin de arttığı tespit edilmiştir. Plastiğin piroliz sıcaklığı kompozitlerin su sorpsiyonunda genelde etkili olmamış ve %0,2-1 aralığında değişmiştir. Kompozitlerin çekme dayanımı ile su sorpsiyonunun bir yıl oda şartlarında bekleme süresince fazla değişmediği görülmüş, fakat donma-çözme işlemine tabi tutulmuş her 2 tür kompozitin çekme uzaması ve çekme dayanımı değerlerinde çok az bir azalma olmuştur.

Özet (Çeviri)

In this study, plastic wastes such as untreated and washed poly (ethylene terephthalate) were pyrolyzed at 300-700 ºC for the preparation of epoxy composite materials from thermoplastic wastes, which is an important solid waste problem, and recycled as raw material. As a result of the pyrolysis experiments, pyrolysis solid product char yield decreased by pyrolysis temperature by taking values of 18.32-20.15% and 17.13-37.89% for the unwashed and washed group, respectively. FTIR, TGA and SEM analyzes were used for the characterization of the chars. As the pyrolysis temperature increases, the aromatic structure of the char and thus its thermal resistance increases. The effect of waste plastics washing process and char ratio on mechanical, thermal, water sorption and electrical conductivity properties of char based composites were investigated. Morphological structures of the composites were examined by SEM. The tensile strength increased with the char ratio obtained at all pyrolysis temperatures and the optimal ratio for PETunwashed char composites was determined as 30% while for all PETwashed pyrolysis char composites 50% was the optimal ratio. The tensile strength values at these ratios varied between 97-136 MPa and 94-124 MPa for unwashed and washed PET chars, respectively. TGA analysis of composites has shown that PET chars is significantly increased that the thermal stability. All composites were found to be semiconductors, their conductivities varied between 10-8-10-3 S cm-1, and the electrical conductivity increased with increasing pyrolysis temperature. The pyrolysis temperature of plastics was not generally effective in the water sorption of composites and ranged from 0.2 to 1%. The tensile strength of the composites showed that the water sorption did not change much during the one-year waiting period in the room conditions, but the tensile strength and tensile strength values of the two types of composites subjected to freeze-thawing were slightly reduced.

Benzer Tezler

  1. PECVD yöntemi ile polimerle kaplanmış grafen bazlı epoksi kompozit özelliklerinin incelenmesi

    Investigation of epoxy composite properties based on graphene coated with polymer by PECVD method

    DUYGU YANARDAĞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    Kimya MühendisliğiSelçuk Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. GÜLNARE AHMETLİ

    DOÇ. DR. MUSTAFA KARAMAN

  2. Karbon – e cam / epoksi hibrit kompozitlerin çekme basma ve darbe özelliklerinin sayısal analizi

    Numarical analysis of tensile compression and impact properties of carbon – e glass / epoxy hybrid komposite's

    KHALED NIMER MOHAMMAD AL-NIMER

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Makine Mühendisliğiİstanbul Aydın Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ LÜTFİYE DAHİL

  3. Al6061 T6 alaşımlarının yapıştırılmasında farklı yüzey hazırlığı işlemlerinin mekanik dayanıma etkisinin incelenmesi

    Investigation of the effect of different surface preparations on mechanical strength of bonding Al6061 T6 alloys

    TİMUÇİN ÖĞRENİR

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Makine MühendisliğiSakarya Uygulamalı Bilimler Üniversitesi

    İmalat Mühendisliği Ana Bilim Dalı

    PROF. DR. SALİM ASLANLAR

  4. Dual-curable textile adhesives for cord/rubber applications

    Çift-kürlenebilen tekstil yapıştırıcılarının kord kumaş/kauçuk uygulamaları

    ZEHRA YILDIZ

    Doktora

    İngilizce

    İngilizce

    2017

    Polimer Bilim ve Teknolojisiİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    PROF. DR. HACER AYŞEN ÖNEN