Elyaf takviyeli Pps kompozitlerinin sürtünme ve aşınma karakterizasyonu
Friction and wear characterisation of fiber reinforced Pps composite materials
- Tez No: 496233
- Danışmanlar: YRD. DOÇ. DR. MEHMET İSKENDER ÖZSOY
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Polimer Bilim ve Teknolojisi, Mechanical Engineering, Polymer Science and Technology
- Anahtar Kelimeler: Aşınma, Sürtünme, Mühendislik plastikleri, Polifenilensülfid (PPS), Cam elyaf kompozitler, Plastik kompozitler, Polimer kompozitler, Tabakalı kompozitler, Wear, Friction, Engineering Polymers, Polyphenylene Sulfide, Glass fiber composites, Plastic composites, Polymer composites, Laminated composites
- Yıl: 2018
- Dil: Türkçe
- Üniversite: Sakarya Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Makine Tasarım ve İmalat Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada, Polifenilen sülfit polimer matriksli cam elyaf ve karbon fiber katkılı PPS mühendislik kompozitlerinin sürtünme ve aşınma özellikleri deneysel olarak incelenmiştir. Aşınma deneyleri pim-disk aşınma deney düzeneğinde gerçekleştirilmiştir. Mühendislik plastiklerinin aşınma deneylerinde üç farklı yük (50N, 100N ve 200N) ve üç farklı (1-2-3 m/s) kayma hızı kullanılmıştır. Deneylerde, karşı disk malzemesi olarak AISI 4140 çeliği kullanılmıştır. Farklı yük ve kayma hızlarında gerçekleştirilen aşınma deneylerinde PPS, %20, %30, %40 cam elyaf katkılı ve %30, %40, %50 karbon fiber katkılı mühendislik plastiklerinin sürtünme katsayıları ve aşınma oranları tespit edilmiş ve deney sonuçları birbirleriyle karşılaştırılmıştır. Elde edilen deneysel sonuçlara göre deneylerde kullanılan polimerler içinde en düşük sürtünme katsayısı ve en düşük aşınma oranı %50 karbon fiber katkılı PPS kompozitinde tespit edilmiştir. Sonuç olarak, bu çalışmalarda kayma hızının artışı ile aşınma oranlarının arttığı görülmüştür. PPS polimeri ve cam elyaf ve karbon fiber katkı maddeli PPS kompozitlerinde yükün artışı ile aşınma oranının arttığı görülürken, PPS polimeri ve cam elyaf ve karbon fiber katkı maddeli PPS kompozitlerinde yükün artışı ile sürtünme katsayısının azaldığı görülmüştür.
Özet (Çeviri)
In this study, friction and wear properties of carbon reinforced polyphenylene sulfide (PPSCF) and glass fiber reinforced polyphenylene sulfide (PPSGF) composite materials were investigated. Friction and wear tests were performed by pin-on-disc test configuration. Tests were carried out at room temperature and 50, 100, 200 N normal loads and 1, 2, 3 m/s sliding speeds were applied. The disc material is AISI 1040 steel. PPS composites filler content consisted of %20, %30 and %40 by weight ratio of glass fiber and %30, %40 and %50 by weight ratio of carbon fiber. The results showed that for carbon fiber filled composites, the friction coefficient and wear rate increased with the increase in applied load. The friction coefficient of glass fiber, reinforced composites, the friction coefficient value decreased with increase in applied load. Finally it is concluded that the lowest wear rate and friction coefficient was reached by 50% carbonfiber PPS composites.
Benzer Tezler
- Hava araçlarında kullanılmak üzere hibrit nanopartikül ve bazalt elyaf takviyeli poli (Fenilen sülfid) matrisli kompozit malzeme geliştirilmesi
Development of hybrid nanoparticle and basalt fiber reinforced poly (Phenylene sulfide) matrix composite materials for use in aircraft
ÇAĞRI ASLAN
Yüksek Lisans
Türkçe
2024
Sivil HavacılıkKocaeli ÜniversitesiHavacılık Bilimi ve Teknolojileri Ana Bilim Dalı
PROF. DR. NEVİN GAMZE KARSLI YILMAZ
- Development of polypropylene composite materials reinforced with reduced graphene oxide and talc for automotive applications
Otomotiv uygulamaları için indirgenmiş grafen oksit ve talk ile takviye edilmiş polipropilen kompozit malzemelerin geliştirilmesi
İREM DÜZENLİ
Yüksek Lisans
İngilizce
2026
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. FATMA SENİHA GÜNER
- Bir pamuk iplikhanesinde fiili çalışma metodlarının incelenmesi ve mevcut işlemlerin standart sürelerinin saptanması
Başlık çevirisi yok
MÜRŞİDE KESEROĞLU
Yüksek Lisans
Türkçe
1985
İşletmeEge ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
DOÇ. DR. MUSTAFA NAZMİ ERCAN
- Poli (etilen tereftalat) elyaf ve ipliklerin bazik ortamdaki davranışı
Başlık çevirisi yok
NURAY OLUKÇU
Yüksek Lisans
Türkçe
1987
Kimya MühendisliğiGazi ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. OYA ŞANLI
- Ankara keçilerinde serum tiroksin düzeyi ve tiftik kalitesi arasındaki ilişkiler
The Relatianship between serum thyroxine levels and the physical quality characteristic of the Angora goat mohair in Turkey
ZİŞAN EMRE