Bakır yüzeyinde üretilen bakır karbür yüzey kompozitlerinin fiziksel, mekanik ve korozyon özelliklerinin araştırılması

Investigation of physical, mechanical and corrosion properties of copper carbide surface composites produced on copper surface

  1. Tez No: 538268
  2. Yazar: CİHAN ÖZORAK
  3. Danışmanlar: DOÇ. DR. SERKAN ISLAK
  4. Tez Türü: Doktora
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2019
  8. Dil: Türkçe
  9. Üniversite: Kastamonu Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 120

Özet

Bu tez çalışmasında, bakırın aşınma özelliklerinin geliştirilmesi ve elektriksel özelliklerinin ise minimum etkilenmesi hedeflenmiştir. Bu sebeple elektrolitik bakır üzerine bakır matriksli karbür takviyeli yüzey kompozitleri plazma sprey kaplama yöntemiyle kaplanmıştır. Karbür olarak SiC, B4C ve WC-Co kullanılmıştır. Bu karbürlerin miktarının tribolojik, korozyon ve fiziksel özellikler üzerine etkisini araştırmak amacıyla her biri için ağırlıkça %5, %10 ve %20 olarak ilave edilmiştir. Aşınma özelliklerin belirlenmesi için ileri-geri hareketli aşınma, korozyon özelliklerinin belirlenmesi için ise potansiyodinamik yöntem kullanılmıştır. Üretilen kaplamaların mikroyapı özellikleri ve faz dağılımının tespiti amacıyla optik mikroskop, SEM-EDS ve XRD analizleri yapılmıştır. Kaplama tabakalarının elektriksel iletkenlikleri girdap akımları prensibine göre gerçekleştirilmiştir. Silisyum karbür ve bor karbürün dekompoze olduğu XRD analizlerinden ve SEM-EDS, Mapping analizlerinden anlaşılmaktadır. Tungsten karbür kobaltta metalik ve intermetalik bileşikler oluşmuştur. Tüm kaplamaların sertlik değerleri alt malzemenin sertlik değerinden yüksektir. Her bir kaplamada katkı oranının artmasıyla sertlikler artış göstermiştir. En yüksek sertlik değerinin tungsten karbür kobalt katkısında olduğu ve yaklaşık olarak ana malzemenin sertlik değerinin 1.8 katı olduğu belirlenmiştir. Aşınma özellikleri incelendiğinde bakır altlık ve kaplama tabakalarında hem abrasif hem de adhesif aşınma türleri gözlenmiştir. Tüm numunelerde yükün artmasıyla malzeme kaybı da artmaktadır. Korozyon sonuçları irdelendiğinde tüm numuneler arasında en düşük akım yoğunluğunun kaplamasız altlık malzemede olduğu görülmektedir. Numunelerin kaplanmasıyla birlikte akım yoğunluğunun artmasıyla birlikte korozyon hızlarıda artmaktadır. Tüm numunelerin elektriksel iletkenlik sonuçları karşılaştırıldığında kaplamadaki karbür oranının artmasıyla elektriksel iletkenlik azalmaktadır. Aynı zamanda kaplamadaki katkı miktarının artması da gözenekliliğin artmasına neden olmuştur.

Özet (Çeviri)

This thesis aims to improve the tribological properties of copper and to minimize its alteration of electrical properties. For this reason, copper carbide surface composites on electrolytic copper are coated with plasma spray coating method. SiC, B4C and WC-Co were used as carbide. These carbides have been added 5%, 10% and 20% by weight to investigate the effect on tribological, corrosion and physical properties. For the tribological properties, Ball-on-Flat Sliding wear method is used. Potentiodynamic method was used for corrosion. For the microstructure properties and phase composition of the produced coatings, optical microscope, SEM-EDS and XRD analyzes were used. The electrical conductivity of the coating layers is based on the eddy currents principle. It can be observed that silicon carbide and boron carbide are decomposed in the result of XRD analyses, SEM-EDS, and Mapping analyses. Also, at tungsten carbide-cobalt Co6W6C, W2C and WC phases were detected through XRD analyses. The hardness values of all coatings are higher than the hardness of the substrate. Hardness values increased with increasing rate of additive in each coating. The highest hardness value is tungsten carbide-cobalt. Also, it can be seen that the hardness value of tungsten carbide-cobalt is approximately 1.8 times of the hardness value of the substrate material. Both abrasive and adhesive wear types were observed in the copper substrate and coating layers. The increase of the load in all samples cause a rise of the loss of material. Through the examinations of corrosion results of all samples, it is observed that the lowest current density is in the uncoated substrate material. Coating the samples increased the current density. The results of electrical conductivity tests decrease with the increase in carbide ratio in the coating. At the same time, the increase in the amount of additive in the coating also caused the increase in porosity.

Benzer Tezler

  1. Metal infiltre edilmiş mikro poroz karbon kompozitlerin aşınma ve sürtünme davranışının karakterizasyonu

    Başlık çevirisi yok

    GÜLTEKİN GÖLLER

    Doktora

    Türkçe

    Türkçe

    1997

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji Mühendisliği Ana Bilim Dalı

    PROF. DR. ADNAN TEKİN

  2. Copper - diamond composite fabrication by electroforming process for thermal management applications

    Elektroşekillendirme ile üretilen ısıl yönetim amaçlı bakır - elmas kompozit kaplamalar

    GÖKÇE EVREN

    Yüksek Lisans

    İngilizce

    İngilizce

    2020

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MUSTAFA KAMİL ÜRGEN

  3. Development of porous ceramics for wastewater purification

    Atık su filtrelenmesi için gözenekli seramiklerin geliştirilmesi

    DAMLA ZEYDANLI

    Doktora

    İngilizce

    İngilizce

    2019

    Kimyaİstanbul Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. SÜLEYMAN AKMAN

    DOÇ. DR. ÇEKDAR VAKIF AHMETOĞLU

  4. Investigation of the cutting performances of the diamond tools used in the natural stone industry

    Doğal taş sanayisinde kullanılan elmaslı kesicilerin kesim performansının incelenmesi

    BERRAK BULUT

    Doktora

    İngilizce

    İngilizce

    2021

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MURAT BAYDOĞAN

  5. Production of copper - silicon carbide composites for thermal management applications by electroforming process

    Termal yönetim uygulamalarında kullanılmak üzere bakır - silisyum karbür kompozitinin elektroşekillendirme yöntemi ile üretimi

    BURAK EVREN

    Yüksek Lisans

    İngilizce

    İngilizce

    2019

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    PROF. DR. MUSTAFA KAMİL ÜRGEN