Katodik ark FBB tekniği ile seramik karo dekorasyonu için TiN kaplamaların üretilmesi ve karakterizasyonu

Production and characterization of TiN coatings for ceramic tile decoration by cathodic arc PVD technique

  1. Tez No: 561569
  2. Yazar: TUGAY TOSUN
  3. Danışmanlar: DR. ÖĞR. ÜYESİ BELGİN TANIŞAN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2019
  8. Dil: Türkçe
  9. Üniversite: Eskişehir Osmangazi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 62

Özet

Malzemeleri vakum altında fiziksel yöntemlerle buharlaştırmak, daha sonra bu buharı bir taban malzeme üzerinde biriktirmek esasına dayanan Fiziksel Buhar Biriktirme (FBB) yöntemleriyle üretilen sert ve aşınmaya dayanıklı kaplamalar parlak renk ve yüzey özellikleri ile dekoratif amaçlı olarak da kullanılmaktadır. Endüstride geleneksel yöntemlere göre daha ucuz ve aşınmaya dayanıklı dekoratif FBB kaplamaların başarılı uygulamaları bu tekniğin günümüzde seramik karo dekorasyonuna adaptasyonuna öncü olmuştur. Bu çalışmada Katodik Ark FBB tekniğinin seramik karoların metalik renklerde dekorasyonunda uygulanabilirliği araştırılmıştır. Kaplama ünitesinde titanyum hedef metali fiziksel olarak buharlaştırılarak, sır pişirimi yapılmış porselen karo yüzeyleri reaktif azot gazı atmosferlerinde TiN bileşiminde kaplanmıştır. Kaplama ünitesine beslenen reaktif gaz akışı, katod akımı ve kaplama süresi proses parametreleri olarak belirlenmiştir. Bu parametrelerin kaplamaların renk özelliklerine etkisi araştırılmış ve altın benzeri renklendirme için optimum proses parametreleri belirlenmeye çalışılmıştır. Deneysel sonuçların değerlendirilmesi için, CIE L*a*b* renk analizi, XRD ve SEM karakterizasyon teknikleri kullanılmıştır. 90 sn süreyle kaplama işlemi uygulanan K2 (550 sccm N2 gaz debisi-150 A akım) ve K6 (650 sccm N2 gaz debisi-200 A akım) kodlu numunelerin ticari TiN kaplamalara benzer L*a*b* renk değerlerine sahip oldukları görülmüştür. Bu numunelerin benzer şekilde ağırlıklı olarak TiN ve Ti2N fazları içerdiği ve TiN ince film kaplamaların karakteristik granül benzeri yüzey morfolojisini sergiledikleri tespit edilmiştir. Bu sonuçlardan K2 ve K6 numunelerinin N/Ti=1 stokiyometrisini karşıladığı ve endüstriyel kaplama işlemlerinde bu numunelere uygulanan kaplama parametrelerinin referans olarak alınabileceği düşünülmüştür. Ayrıca stokiyometrik olmayan kaplama parametreleri ile altın tonlarının yanı sıra; metalik efekte sahip mor, mavi-yeşil ve gri gibi farklı renklerde kaplamaların da üretilebileceği görülmüştür.

Özet (Çeviri)

Materials with physical method under vacuum evaporate, then this vapor to accumulate over a base material on the basis of Physical Vapor Deposition (PVD) method are produced hard and wear-resistant coatings with bright color and surface features also used as decorative purposes. In the successful application of decorative and wear resistant PVD coatings than conventional methods in the industry has been a pioneer adaptation of this technique on ceramic tile decoration. In this study, the applicability of the Cathodic Arc PVD technique of decoration of ceramic tiles in metallic colors were investigated. Titanium target metal evaporated with physically in reactive nitrogen gas atmosphere was covered fired glaze porcelain tile surfaces. Reactive gas flow rate to feed coating unit, cathode current and deposition time were selected as process parameters. The effect of these parameters were investigated on the coating colour properties and optimum process were tried to select for goldlike coloring. To evaluate experimental results, CIE L*a*b* colour analysis, XRD and SEM characterization techniques were used. It is seen that K2 and K6 coded samples which applied 90 sec coating process have same L*a*b* colour values with commercially TiN coatings. Similarly, these samples predominantly contained TiN and Ti2N phases and TiN thin film coatings exhibited characteristic granular-like surface morphology. From this results, K2 and K6 samples compensate N/Ti=1 stoichiometry and it is considered that the parameters which applied to these samples can be taken as reference in industrial coating process. Besides with nonstoinhiometric coating parameters, it is seen that diffirent colour coating can be produced such as purple with metallic effect, blue-green and grey.

Benzer Tezler

  1. Katodik ark FBB yöntemi ile dekoratif amaçlı Cr-O-N kaplamaların üretilmesi

    Production of Cr-O-N coatings by cathodic arc PVD, for decorative purposes

    SEMİH ÖNCEL

    Yüksek Lisans

    Türkçe

    Türkçe

    2002

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji Ana Bilim Dalı

    PROF. DR. MUSTAFA ÜRGEN

  2. Mo-N kaplamaların ark fiziksel buhar biriktirme yöntemiyle üretimi ve karakterizasyonu

    Production and characterisation of Mo-N coatings by arc physical vapour deposition technique

    M. KÜRŞAT KAZMANLI

    Doktora

    Türkçe

    Türkçe

    1999

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    PROF.DR. MUSTAFA ÜRGEN

  3. Surface modification of titanium hard tissue implants by magnesium doping

    Titanyum sert doku implant yüzeylerinin magnezyum katkılama ile modifikasyonu

    OKAN MAZMANOĞLU

    Yüksek Lisans

    İngilizce

    İngilizce

    2014

    Biyomühendislikİstanbul Teknik Üniversitesi

    Moleküler Biyoloji-Genetik ve Biyoteknoloji Ana Bilim Dalı

    DOÇ. DR. FATMA NEŞE KÖK

    DOÇ. DR. MUHAMMET KÜRŞAT KAZMANLI

  4. TiB2 coating on different substrates via dual process:CA-PDV and CRTD-Bor

    Farklı malzemeler üzerinde çift işlem (KA-FBB, KRTD-Bor) ile TiB2 kaplamasının elde edilmesi

    MEHRAN KARIMZADEHKHOEI

    Doktora

    İngilizce

    İngilizce

    2024

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    PROF. DR. GÜLDEM KARTAL ŞİRELİ

    PROF. DR. MUSTAFA KAMİL ÜRGEN

  5. 316L paslanmaz çelik üzerinde katodik ark FBB ve oxidasyon yöntemleriyle üretilen zirkonyum oksit kaplamaları özellikleri

    Properties of zirconium oxide coatings on 316-L stainless steels produced by cathodic arc PUD and oxidation techniques

    ERDEM ŞİRELİ

    Yüksek Lisans

    Türkçe

    Türkçe

    1999

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji Mühendisliği Ana Bilim Dalı

    PROF. DR. MUSTAFA ÜRGEN