Duvar karosu üretiminde perlit kullanımı

Using perlit in wall tile body

  1. Tez No: 58201
  2. Yazar: BEYHAN TAŞPINAR
  3. Danışmanlar: DOÇ. DR. NURAN AY
  4. Tez Türü: Yüksek Lisans
  5. Konular: Seramik Mühendisliği, Ceramic Engineering
  6. Anahtar Kelimeler: Perlit, Monoporous
  7. Yıl: 1997
  8. Dil: Türkçe
  9. Üniversite: Anadolu Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Seramik Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 110

Özet

ÖZET Yüksek Lisans Tezi DUVAR KAROSU ÜRETİMDE PERLİT KULLANIMI BEYHAN TAŞPINAR Anadolu Üniversitesi Fen Bilimleri Enstitüsü Seramik Mühendisliği Anabilim Dalı Danışman: Doç. Dr. Nuran AY 1997,98 Hızlı tek pişirim yöntemi ile üretilen duvar karosuna“monoporoz”denilmektedir. Monoporoz üretimi başlıca hammaddelerin öğütülmesi, granül yapma, presleme, sırlama, kurutma ve pişirme süreçlerini içerir. Perlit %90-97 cam, %3-10 kristalleşmiş mineraller içeren volkanik kayaçtır. Dünyadaki 6 milyar tonluk perlit rezervinin 4 milyar tonu ülkemizde bulunmaktadır. Günümüzde perlit genleştirilerek inşaat, metalürji, tanım ve filtre endüstrisinde kullanılmakta ve bir kısmı da ihraç edilmektedir. Rezervlerin çok büyük bir kısmı ise değerlendirilememektedir. Bu çalışmada ham perlit % 5, % 10, % 15 ve % 20 oranlarında monoporoz bünyesine ilave edilmiş ve bu bünyeler perlit içermeyen bünye ile karşılaştırarak mekanik, fiziksel ve ısıl özellikleri incelenmiştir. Hazırlanan numunelerin kuruma ve pişme küçülmeleri, ham, kuru ve pişmiş mukavemetleri, su emmeleri, yığınsal yoğunluk ve görünür yoğunluklar yapılan deneylerle tesbit edilmiştir. Ayrıca ham ve pişmiş dilatometre ve X-ışınları difraktometresi analizleri yapılmıştır. Çalışma sonucunda perlit miktarına bağlı olarak, mukavemet ve su emme değerleri değişmediği halde karoların kütlelerinin %1-2,7 ve hammaddelerin öğünme sürelerinin %30 oranlarında azaldığı görülmüştür. Bunların yanında hammadde maliyetinin de %10-20 oranında azaldığı tesbit edilmiştir. Pişme küçümelerinde ise bir miktar artma gözlenmiştir. Isıl genleşme katsayıları değişmezken X-ışınları difraktometresi sonuçlarına göre toplam kristal faz miktarında azalma olmuştur. Anahtar Kelimeler : Perlit, Monoporoz,

Özet (Çeviri)

ABSTRACT Master of Science Thesis USING PERLİT IN WALL TILE BODY BEYHAN TAŞPINAR Anadolu University Graduate School of Natural and Applied Sciences Ceramic Engineering Supervisor: Doç. Dr. Nuran AY 1997,98 The wall tile that is produced with single firing method called is monoporous. The monoporous production includes mainly proceses such as grinding of raw materials, granulation, presing, glazing, drying and firing. Perlit is volcanic rock that includes %90-97 amorf phase and %3-10 cristalized minerals. Perlit exists about 4 000 millon ton in our country. İn the bulding, metallurgy, agriculture, filter sectors expanded perlit is used and raw perlit which is not expanded is exported. But most amount of the perlit isn't consumed. In this study raw perlit was added with %5, %10, %15 and %20 portions to the monoporous body and by comparing these bodies with non perlit included bodies their mecanic, physcal and thermal characteristics were examined. Firing shrinkage, modulus of rupture raw, dry and fired samples, water absorption, bulk density, appereant density were measured with the experiments. Raw and fired thermal expansion coefficiency and X-ray analyses were made. Finally, decreasing was seen depending on perlit amount mass of fired tiles about %1-2,7and grinding time of raw materials about %30 whereas in modulus of ruptures and water absorptions change was not noted. In addition cost of raw materials was reduced %30 portions. However the firing shrinkage was increased a little. Total cristalline phase was reduced according to X-ray diffraction results while thermal expansion coefficent was not changed.

Benzer Tezler

  1. Tez No

    627642

    Ergitici olarak kullanılan farklı alkali kaynaklarının seramik duvar karosu bünyesindeki teknolojik özelliklere etkisinin incelenmesi

    Investigation of the effects of different resources used as flux on the technological properties of ceramic wall tile bodies

    MERİH ANIL EMİR

    Yüksek Lisans

    Türkçe

    Türkçe

    2020

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. CÜNEYT ARSLAN

  2. Tez No

    150618

    Yer ve duvar karosu üretiminde ortak bünye kullanımı

    Employment of a multipurpose tile body for both wall and floor tile production

    MUSTAFA FAHRİ ÖZER

    Yüksek Lisans

    Türkçe

    Türkçe

    2004

    Seramik MühendisliğiAnadolu Üniversitesi

    Seramik Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. ALPAGUT KARA

  3. Tez No

    119770

    Söğüt Çöplük feldspatının duvar karosu üretiminde kullanımı

    Use of Söğüt Çöplük feldspar in wall tile bodies

    ZUHAL GÜVEN

    Yüksek Lisans

    Türkçe

    Türkçe

    2002

    Seramik MühendisliğiAnadolu Üniversitesi

    Seramik Mühendisliği Ana Bilim Dalı

    PROF. DR. NURAN AY

  4. Tez No

    720260

    Yer ve duvar karosu üretiminde deformasyon ve su emme kriterlerine etki eden parametrelerin incelenmesi

    Investigation of parameters affecting deformation and water absorption criteria in floor and wall tile production

    FEVZİ HAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    Makine MühendisliğiYozgat Bozok Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. HAMZA KEMAL AKYILDIZ

  5. Tez No

    153021

    Bor endüstrisi katı atıklarından borun katı-sıvı özütleme ile geri kazanılması ve katı atıkların seramik üretiminde kullanılması

    Recovery of boron from solid wastes of boron industry by solid-liquid extraction and utilization of the solid wastes in ceramic industry

    İLKER KIPÇAK

    Doktora

    Türkçe

    Türkçe

    2004

    Kimya MühendisliğiEskişehir Osmangazi Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    Y.DOÇ.DR. MİNE ÖZDEMİR