Comparing Bacterial Colonization Of Laser Etched And Acid Etched Enamel In Bonding Orthodontic Ceramic Brackets
Lazerle aşındırma ve Asitle aşındırma yöntemleri ile mine yüzeyine diş teli yapıştılması,kopma kuvvetlerinin değerlendirilmesi ve bakteri kolonizayonunun gözlenmesi
- Tez No: 583488
- Danışmanlar: PROF. DR. MURAT GÜLSOY
- Tez Türü: Yüksek Lisans
- Konular: Mühendislik Bilimleri, Engineering Sciences
- Anahtar Kelimeler: Asit ile asındırma, Lazer, Seramik Braketlerin Çıkarılması, Bakteri, Acid Etching, Laser, Debonding, Ceramic Brackets, Bacteria
- Yıl: 2019
- Dil: İngilizce
- Üniversite: Boğaziçi Üniversitesi
- Enstitü: Biyomedikal Mühendislik Enstitüsü
- Ana Bilim Dalı: Biyomedikal Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu projenin amacı, ortodontik seramik braketlerin yapıstırılmasında lazerle pürüzlendirilmis ve asitle asındırılmıs emaye bakteriyel kolonizasyonunu karsılastırmak ve ayrıca asitle asınmadan kaynaklanan emaye demineralizasyon ve dis çürümesi riskini azaltan bir yöntem gelistirmektir. Seramik braket yapıstırılması, asitle asındırma ve lazerle asındırma gibi farklı yollarla yapıldı. Bu projede, sıgır dislerini temizledikten sonra, gömülü alçı blogundan önce, dislerin labiyal yüzeyinde 10 x 10 mm alan olusturuldu. Daha sonra, mine yüzeyinin labiyal yüzeyi, blogun yatay eksenine mümkün oldugu kadar paralel konumlandırıldı ve alçı bloguna gömüldü. Alçı blokta sadece 10 * 10 mm alan belirmistir. Daha sonra ilk adım, seramik asındırıcıların asitle asındırma yöntemi kullanıldı ve lazerle asındırma teknigi uygulandı, daha sonra kopma kuvvetini ölçmek için universal test makinesiyle seramik braketler mine yüzeyinden çıkartıldı. Ikinci adım, lazerle asındırma ve asitle asındırma tekniklerinden sonra bakterilerin dislerdeki kolonizasyonunu ölçmek için bakteri asılama olmustur.Sonuçlar, kopma kuvvetleri arasında anlamlı bir fark vardır ( islem uygulanmayan ve asit, lazer grupları karsılastırıldıgında). Ayrıca, lazerle asındırılmıs ve asitle asındırılmıs grupların CFU degerleri arasında anlamlı bir fark oldugu göstermistir. Ancak lazerle oyulmus gruplar için ortalama deger ve ortalama CFU degerleri asitle asındırılmıs gruplardan daha düsüktü.
Özet (Çeviri)
COMPARING BACTERIAL COLONIZATION OF LASER ETCHED AND ACID ETCHED ENAMEL IN BONDING ORTHODONTIC CERAMIC BRACKETS The aim of this project comparing bacterial colonization of laser etched and acid etched enamel in bonding orthodontic ceramic brackets and also to develop a method which reduces the risk of enamel demineralization and tooth decay caused by acid etching. In this project, after cleaning bovine teeth, before the embedding gypsum block, 10*10 mm area was created a labial surface of teeth. Then, they were buried in gypsum block as the labial surface. They were put in the gypsum block as parallel as possible. Then, the first step is the bonding of ceramic brackets by using acid etching (for acid etching group phosphoric acid solution is used within the ratio of 37% to the bonding surfaces. Then laser etching method was applied. Universal testing machine was used to debond the brackets. The second step was inoculation of bacteria to measure colonization of bacteria on the teeth after laser etching and acid etching techniques. There were 4 different experimental groups: Acid etched group, Laser etched group, Non-etched group, and Gypsum group. Each group was composed of 12 samples. After the inoculation part, S. Mutants colonies were counted on a counting aid manually and the colony-forming units (CFUs) were examined. Results show that there was a significant difference between debonding forces (nonetched vs acid etched, laser etched) and there was a significant difference between CFU values of laser etched and acid etched groups. Mean value and average CFU values for laser etched groups were lower than acid etched groups.
Benzer Tezler
- Bazı esterlerin kinetik incelenmesi ve termodinamik parametrelerin belirlenmesi
Kinetic study and detesmination of thermodnamic parameters of some esters
İBRAHİM TAŞ
Yüksek Lisans
Türkçe
1986
Kimya MühendisliğiUludağ ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. MUSTAFA CEBE
- Helisel yayların statik karakteristiklerini ölçme ve kontrol etme cihazının tasarımı ve imalatı
Design and manufacture of a device measuringand controlling the static characteristics of helical springs
MUAMMER MUSULLUOĞLU
Yüksek Lisans
Türkçe
1987
Makine MühendisliğiGazi ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. FEVZİ ERCAN
- Fonon dispersiyon eğrilerinin simulasyonu ve hallerin yoğunluğu
Simulation of phonon dispersion curves and density of states
MUSTAFA ÖZCAN
Yüksek Lisans
Türkçe
1987
Fizik ve Fizik MühendisliğiGazi ÜniversitesiFizik Ana Bilim Dalı
DOÇ. DR. KEMAL ÇOLAKOĞLU
- Saksılı arçek olarak pazarlama olanağı bulunan bazı ilkbahar ve yaz arçeklerinin morfolojik özellikleri
Başlık çevirisi yok
DEFNE YARAR(ERGEN)
Yüksek Lisans
Türkçe
1986
BotanikEge ÜniversitesiPeyzaj Mimarlığı Ana Bilim Dalı
PROF. DR. AYSEL BAYRAKTAR
- İncir işletmelerinde açığa çıkan hurda incirlerin tek hücre proteini üretiminde substrat olarak kullanımı
Başlık çevirisi yok
HÜLYA OKER
Yüksek Lisans
Türkçe
1987
Gıda MühendisliğiEge ÜniversitesiGıda Bilimi ve Teknolojisi Ana Bilim Dalı
DOÇ. DR. MEHMET KARAPINAR
- 8 çeltik çeşidinde çimlenme devresinde farklı su derinliklerinin çıkışa etkisi üzerine bir araştırma
Effect of different water depth on germination of 8 rica cultivors
FERİDE AŞICI