Petrol tubing çeliğinin mikrobiyal korozyon davranışının incelenmesi

Investigation of microbial corrosion behavior of petroleum tubing steel

  1. Tez No: 600653
  2. Yazar: DUYGU ARSLAN
  3. Danışmanlar: PROF. DR. ESRA SUNGUR
  4. Tez Türü: Yüksek Lisans
  5. Konular: Mikrobiyoloji, Microbiology
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2019
  8. Dil: Türkçe
  9. Üniversite: İstanbul Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Biyoloji Ana Bilim Dalı
  12. Bilim Dalı: Temel ve Endüstriyel Mikrobiyoloji Bilim Dalı
  13. Sayfa Sayısı: 88

Özet

Petrol gerek yakıt olarak gerekse de mikroorganizmaların varlığını idame ettirebilmesi için iyi bir enerji kaynağıdır. Petrolün sahip olduğu fizikokimyasal koşullar ve mikroorganizmaların metabolik aktiviteleri bir araya geldiğinde, petrol üretiminde kullanılan metal aksamlarda ciddi korozyon problemleri ve dolayısı ile de büyük ekonomik kayıplar oluşabilmektedir. Petrol rezervuarlarında bulunan mikroorganizmalar, sulu ortamda lokalize değişiklikleri indükleyerek mikrobiyolojik olarak indüklenmiş korozyona (MIC) neden olabilirler. MIC'in, petrol boru hatları ve depolama tanklarında neden olduğu hasarlardan kaynaklı ciddi ekonomik kayıplara yol açtığı bilinmektedir. Petrol ve gaz endüstrisindeki tüm korozyon problemlerinin yaklaşık %20'sinin mikroorganizmalar tarafından oluşturulduğu bildirilmiştir. Bu çalışma kapsamında Adıyaman petrol sahasından alınan petrol su fazının, petrol üretiminde sıklıkla kullanılan N80 çeliğinin mikrobiyal korozyon davranışı üzerine etkisi hem gravimetrik hem de elektrokimyasal yöntemler ile 4 ay süresince incelenmiştir. Mikrobiyolojik korozyonun tespiti için biri test diğeri kontrol olmak üzere iki farklı laboratuvar ölçekli düzenekaynı koşullar altında çift tekrarlı olarak kurulmuştur. Deney ortamı olarak Adıyaman petrol sahasından alınan üretim suyu kulanılmıştır. Deneyler, petrol su fazı örneğinin alındığı bölgedeki sıcaklık olan 70°C'de gerçekleştirilmiştir. Gravimetrik analiz için, kuponlar belirli zaman aralıklarında(24, 48, 72, 96, 144, 168, 336, 720, 1080, 1440, 2160, 2880 sa) düzeneklerden çıkarılmış ve ağırlık kayıpları hesaplanmıştır.Eletrokimyasal deneylerde potansiyodinamik polarizasyon yöntemi esas alınmıştır. Ölçümler yukarıda belirtilen zamanlardagerçekleştirilmiştir. Ikor değerlerinden korozyon hızı hesaplanmıştır. Deney ve kontrol kurulmuştur. Metal yüzeyi, taramalı elektron mikroskobu (SEM) ile incelenmiştir. Deney ve kontrol kuponlarının ağırlık kayıplarının zamanla arttığı (sırasıyla, p

Özet (Çeviri)

Petroleum is a rich source of energy for both fuel and the maintenance of microorganisms. When the physicochemical conditions of the oil and the metabolic activities of the microorganisms come together, serious corrosion problems can occur in the metal parts used in oil productionleading to economic loses. Microorganisms present in petroleum reservoirs can cause microbiologically induced corrosion (MIC) by inducing localized changes in the aqueous medium. MIC is known to cause serious economic losses due to damage inoil pipelines and storage tanks. It has been reported that approximately 20% of corrosion problems in the oil and gas industry are caused by microorganisms. In this study, the effect of oil water phase taken from oil field in Adiyaman on microbial corrosion behavior of N80 steel using petroleum system was carried out for 4 months by both gravimetric and electrochemical methods.Two different laboratory scale devices, one as a test and one as acontrol for microbiological corrosion, were installed in duplicate under the same conditions. Potentiodynamic polarization method wasused in electrochemical experiments. Measurements were performed at the times indicated above. Corrosion rate was calculated from the Icorrvalues. Experiment and control have been established. Metal surface was examined by Scanning Electron Microscopy (SEM). The weight loss of the test and control coupons was found to increase with time (p

Benzer Tezler

  1. Effect of GTAW parameters on mechanical and microstructural properties of weld joints of low alloy AISI 4130 steel

    Gaz tungsten ark kaynak (GTAW) parametrelerinin kaynaklı düşük alaşımlı AISI 4130 çeliğinin mekanik ve mikroyapı özelliklerine etkileri

    ERKAN ATAMAN

    Yüksek Lisans

    İngilizce

    İngilizce

    2001

    Metalurji MühendisliğiOrta Doğu Teknik Üniversitesi

    Metalurji Mühendisliği Ana Bilim Dalı

    PROF. DR. ALPAY ANKARA

  2. Corrosion of N-80 type steel by CO2 / formation fluid mixtures

    N-80 tipi çeliğin CO2 / formasyon suyu karışımlarında korozyonu

    SAFİYE SEZA ÇİLİNGİROĞLU

    Yüksek Lisans

    İngilizce

    İngilizce

    1993

    Kimya MühendisliğiOrta Doğu Teknik Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. NEVİN SELÇUK

  3. Overview of solutions to prevent liquid loading problems in gas wells

    Gaz kuyularında sıvı dolumunun engellenmesi için çözüm yöntemlerine genel bakış

    ÖZMEN BİNLİ

    Yüksek Lisans

    İngilizce

    İngilizce

    2009

    Petrol ve Doğal Gaz MühendisliğiOrta Doğu Teknik Üniversitesi

    Petrol ve Doğal Gaz Mühendisliği Ana Bilim Dalı

    PROF. DR. EVREN ÖZBAYOĞLU

  4. Reservoir simulation modeling of a natural gas field for reservoir evaluation

    Bir doğal gaz sahasının rezervuar modellemesi ve değerlendirmesi

    SEDEF YILMAZ

    Yüksek Lisans

    İngilizce

    İngilizce

    2002

    Petrol ve Doğal Gaz MühendisliğiOrta Doğu Teknik Üniversitesi

    Petrol ve Doğal Gaz Mühendisliği Ana Bilim Dalı

    PROF. DR. MAHMUT PARLAKTUNA

  5. Investigating end user errors in oil and gas critical control systems

    Petrol ve gaz kritik sistemlerinde son kullanıcı hatalarının araştırılması

    LAYTH NABEEL ALRAWI

    Yüksek Lisans

    İngilizce

    İngilizce

    2019

    Bilgisayar Mühendisliği Bilimleri-Bilgisayar ve KontrolÇankaya Üniversitesi

    Bilgisayar Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ ÖZGÜR TOLGA PUSATLI