Co-B içeren katazlizör sentezi, karakterizasyonu ve araştırılması
Synthesis, characterization and investigation of catalysts containing Co-B
- Tez No: 619848
- Danışmanlar: PROF. DR. NURAN AY
- Tez Türü: Doktora
- Konular: Kimya Mühendisliği, Chemical Engineering
- Anahtar Kelimeler: Kobalt bileşikleri, Reaksiyon sıcaklığı, Co:B oranı, Karakterizasyon, Cobalt compounds, Reaction temperature, Co:B rates, Characterization
- Yıl: 2020
- Dil: Türkçe
- Üniversite: Eskişehir Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Temel İşlemler ve Termodinamik Bilim Dalı
- Sayfa Sayısı: 131
Özet
Bu çalışmada, kobalt klorür hekzahidrat, kobalt nitrat hekzahidrat ve kobalt sülfat heptahidrat ile sodyum boraks pentahidrat reaksiyona sokularak kobalt borat eldesi incelenmiştir. Co:B mol oranları 1:2, 1:3, 1:4, 1:5, 1:7 ve 1:10, reaksiyon sıcaklığı 25˚C, 35˚C, 40˚C ve 45˚C olarak seçilmiştir. Reaksiyon sonucunda katı süzülüp, yıkanarak kurutulmuştur. 700, 850, 950 ve 1000˚C'de, 1, 2, 3, 7 saat ısıl işlem uygulanmıştır. Numunelerin karakterizasyonu TG-DTA, XRD, FTIR, SEM, ICP-OES, BET ve Rietveld analizleriyle gerçekleştirilmiştir. Reaksiyon sıcaklığı ve Co:B oranları değiştiğinde farklı miktarda kobalt piroborat ve kobalt tetraborattan oluşan iki faz elde edilmiştir. Numunelerde BO3 ve BO4 grupları mevcuttur. Tek fazdan oluşan numunelerde ise BO4 gruplarına ait piklerin şiddetleri çok küçüktür. %90'nın üzerinde kobalt piroborat içerdiği belirlenen numunelerin XRD grafiklerinde kobalt tetraborat fazlarının varlığı bulunamamıştır. Farklı kobalt bileşikleriyle hazırlanan numunelerin mikroyapılarında önemli bir değişikliğe rastlanmamıştır. Çoğunlukla levha ve çubuğumsu morfolojiden oluşmuş bir mikroyapı birlikte görülmektedir. Numunelerin elementel analizleri sonucunda %Co miktarları 23,08-34,84, %B miktarları 9,68-14,76 arasında değişmektedir.
Özet (Çeviri)
In this study cobalt borate synthesis was investigated using the reaction between cobalt chloride hexahdyrate, cobalt nitrate hexahydrate, cobalt sulphate heptahydrate and borax. The Co:B rates were chosen as 1:2, 1:3, 1:4, 1:5, 1:7, 1:10 and reaction temperatures 25, 35, 40, 45˚C. Suspension arised after reaction was filtered, washed and dried. The heat treatment carried out at 700, 850, 900 and 1000˚C during 1, 2, 3, 5, 7 hours. The samples were characterized by TG-DTA, XRD, FTIR, SEM, ICP-OES, BET and Rietveld analysis techniques. As reaction temperature and Co:B rates changed, two phases were obtained containing different amounts of cobalt tetraborate (CoB4O7) and cobalt pyroborate (Co2B2O5). It's seen that there are BO3 ve BO4 vibrations peaks. The samples which composed of one phase have small intensities of BO4 groups peaks. The presence of cobalt tetraborate phases was not found in XRD patterns of the samples that containing more than 90% cobalt pyroborate. There is no significant changes in microstructure among samples which were synthesized with different cobalt compounds. Mainly, microstructures of samples contains plates and rod-like forms together. The samples elemental analysis results were changed for Co amounts %23,08-34,84 and for B amounts %9,68-14,76.
Benzer Tezler
- Bor içeren yeni bir poliokzometalat bileşiğinin sentezi yapısının karakterizasyonu ve katalitik aktivitesinin belirlenmesi
Synthesis of a new polyoxometalate compound containing boron and determination of its structure and catalytic activities
EBRU KANAR
- Polihıpe ve polimıpe nanokompozitlerinin sentezi, karakterizasyonu ve mekanik özelliklerinin geliştirilmesi
Synthesis, characterization and improving mechanical properties of polyhipe and polymipe nanocomposites
ELİF BERBER
Yüksek Lisans
Türkçe
2013
Polimer Bilim ve TeknolojisiYalova ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
YRD. DOÇ. DR. EMİNE HİLAL MERT
- Grafen-heteroatom temelli katalizörlerin sentezi, karakterizasyonu ve hidrojen üretiminde kullanımı
Graphene-heteroatom based catalysts and their application for hydrogen production
DUYGU AKYÜZ
Doktora
Türkçe
2019
EnerjiMarmara ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. ATIF KOCA
PROF. DR. ALİ RIZA ÖZKAYA
- Tiyo ve okso grubu içeren polimerik ftalosiyaninlerin mikrodalga yardımlı sentezi ve karakterizasyonu
Synthesis and characterization of phthalocyanines polymeric containing thio and oxa group
RAMAZAN ÖZKAN
- Yeni tip tetrakis-[4-(1-(piridin-4-IL) etoksil)] sübstitüsyonlu ftalosiyanin komplekslerinin sentezi ve spektrofotometrik karakterizasyonu
Novel tetrakis- [4- (1- (pyridin-4-IL) ethoxyl)] substituted phthalocyanines : Synthesis and spectrophotometric characterization
BETÜL ÖZDEMİR