Poliolefin kaplanarak süperhidrofobik hale getirilen polyester kumaşların sentezi ve karakterize edilmesi

Synthesis and characterization of superhydrophobic polyester fabrics coated by polyolefins

  1. Tez No: 647109
  2. Yazar: BAHAR ŞENGÜL
  3. Danışmanlar: PROF. DR. HÜSNÜ YILDIRIM ERBİL
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya Mühendisliği, Chemical Engineering
  6. Anahtar Kelimeler: Süperhidrofob, Polipropilen, Polietilen, Polipropilen-Polietilen Kopolimer, Siklik Olefin Kopolimer, Polyester kumaş, Superhydrophobic, Polypropylene, Polyethylene, Polypropylene-Polyethylene Copolymer, Cyclic Olefin Copolymer, Polyester fabric
  7. Yıl: 2020
  8. Dil: Türkçe
  9. Üniversite: Gebze Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 134

Özet

Yüzeyinde 150º'den büyük su temas açıları veren süperhidrofobik kumaşlar, yağmurda ıslanmayan askeri ve sivil pardesüler, filtrasyonda kullanılan membranlar, metal levha depolamada korozyon önleyici, askeri örtüler, hastanelerde tıbbi önlükler, itfaiye kıyafetleri, fonksiyonel spor giyim ve korozyon önleyici brandalar gibi birçok alanda uygulanma potansiyeline sahiptir. Ayrıca, kendi kendini temizleme performansı sayesinde bazı tekstil ürünlerinin yıkama sayısını azaltabilir. Bu tez çalışmasında, polipropilen (PP) ve polietilen (LDPE), polipropilen-polietilen kopolimer (PP-PE), siklo-olefin kopolimer (COC) çözeltileriyle, 79 gr/m² ve 149 gr/m² ağırlıklarında 2 farklı %100 polyester kumaş kaplanmıştır. Değişik miktarlardaki polimerleri çözmek için ksilen solventi kullanılmış, sonra bu çözeltilere değişik miktarlarda 1:1 oranında çözücü olmayan metil etil keton ve siklohekzanon non-solventleri eklenmiş ve çözeltide bulutlanma başlamadan şeffaf halde iken daldırma ile kaplamalar yapılmış ve karakterize edilmiştir. Kumaşlar kaplanmadan önce bir çerçeve ile gerdirilmiş sonra da sabit bir hızda daldırılıp, çıkarılıp, kurutulmuştur. Kaplama esnasında farklı sıcaklıklar (polimer tipine bağlı olarak 40-120 °C arasında) ve solvent/non-solvent oranları (10:90-40:60 arasında) uygulanmıştır. Ayrıca PP/PP-PE ve PP/COC polimer karışımlarının beraber kullanımlarının da su temas açısı üzerine etkisi incelenmiştir. Her bir polimer kaplama malzemesi için farklı optimum kaplama sıcaklığının mevcut olduğu saptanmıştır. Çalışmalar esnasında kullanılan polimer tipinin, kaplandıktan sonra kumaş yüzeyinde ölçülen temas açısını önemli derecede etkilediği sonucuna varılmıştır. Optimum kaplama çözelti konsantrasyonu 30 mg/ml olarak bulunmuştur, ancak optimum kaplama sıcaklığı her polimer için farklıdır: PP-PE kopolimeri için 63°C; PP polimeri için 90 °C; siklo-olefin kopolimeri için 60 °C ve LDPE polimeri için 72 °C'dir. En yüksek temas açısı 79 gr/m²'lik kumaş için 152° ± 2 olarak PP polimeri ve 1:1 oranlı PP/PP-PE bileşimi ile elde edilmiştir. 149 gr/m²'lik kumaşı için elde edilen maksimum temas açısı PP-PE kopolimeri ile 150° olarak elde edilmiştir.

Özet (Çeviri)

Superhydrophobic fabrics that allow water contact angles higher than 150º have a big potential to be applied in many areas such as non-wetting military and civilian topcoats in the rain, filtration membranes, anti-corrosion in metal sheet storage, military drapes, medical gowns in hospitals, firefighting clothing, functional sportswear and anti-corrosion tarpaulins. In addition, it can reduce the number of washing some textile products due to its self-cleaning performance. In this thesis, two different 100% polyester fabrics which has 79 g/m² and 149 g/m² weight types were coated by using solutions of polypropylene, polyethylene, polypropylene-polyethylene copolymer and cyclic-olefin copolymer. Xylene was used to dissolve different amounts of polymers, then different amounts of MEK and cyclohexanone by ratio of 1:1 as a non-solvent couple and fabrics were dipped before clouding point and finally coated fabrics characterized. The fabrics were stretched with a frame and then dipped at a constant speed, removed and dried. In the coating process different temperatures (between 40-120 ° C depend on the polymer type) and solvent/non-solvent ratios (between 10:90-40:60) were applied. In addition, the effects of PP/PP-PE and PP/COC polymer mixtures were investigated on water contact angle. It has been found that There are different optimum coating temperatures for each polymer coating material. It was concluded that the type of polymer used during the studies significantly affected the contact angle measured on the fabric surface after coating. The optimum coating concentration of the solution was determined as 30 mg/ml, but the optimum coating temperature was different for each polymer: these are 63 °C for the PP-PE copolymer; 90 °C for PP polymer; 60 °C for cyclic-olefin copolymer; and 72 °C for PE polymer. In addition, It is 90 °C for 1:1 ratio PP-PE/PP solution and COC/PP solutions. The highest contact angles were obtained with a PP polymer of 152 ° ± 2 and a PP/PP-PE composition in a ratio of 1:1 for the fabric of 79 g/m². The maximum contact angle for the 149 g/m² fabric was 150 ° with the PP-PE copolymer solition.

Benzer Tezler

  1. Farklı poliolefin / kil nanokompozit malzemeler ile üretilen ambalajların diyet bisküvilerin kalitesine etkisinin belirlenmesi

    Determining effect of films produced with different polyolefin/clay nanocomposites on the quality of sugar-free bran biscuits

    TOLGA KANKAYA

    Yüksek Lisans

    Türkçe

    Türkçe

    2011

    Gıda MühendisliğiSüleyman Demirel Üniversitesi

    Gıda Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ATIF CAN SEYDİM

  2. Synthesis of pyrrole-imine schiff base ligands and their complexes with group IVB metal (Ti, Zr, Hf)

    Pirol-imin schiff bazı ligandlarının sentezi ve grup IV metalleri ile kompleksleri (Ti, Zr, Hf)

    CAHİT CAN ÇANAKÇI

    Yüksek Lisans

    İngilizce

    İngilizce

    2021

    Kimyaİstanbul Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. OZAN SANLI ŞENTÜRK

  3. Tek kullanımlık iş güvenliği donanımlarının beton içerisinde değerlendirilerek, oluşturulan beton numunenin termal ve dayanım özelliklerinin incelenmesi

    Investigation of thermal values and strength properties of concrete sample created by evaluating disposable safety equipment in concrete

    ASLIHAN YILMAZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    Makine MühendisliğiMunzur Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. GÖKHAN KAHRAMAN

  4. Grafting copolymerization of itaconic acid and its derivatives onto polyolefines

    İtakonik asit ve türevlerinin poliolefinler üzerine aşı koplolimerizasyonu

    GÜLNUR BAŞER

    Yüksek Lisans

    İngilizce

    İngilizce

    2005

    Polimer Bilim ve Teknolojisiİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    PROF.DR. CANDAN ERBİL

    PROF.DR. NURSELİ UYANIK

  5. Farklı poliolefinlerin termoplastik vulkanizat karışımlarının bazı mekanik özelliklerine etkisi

    Effect of polyolefin type on some mechanical properties of thermoplastic vulcanizate compound

    SAADET ÇINARBAŞI

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Kimya Mühendisliğiİstanbul Üniversitesi-Cerrahpaşa

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. AHMET KAŞGÖZ