Otomotiv cam uygulamaları için kobalt katkılı nikel oksit ince filmlerin üretimi, karakterizasyonu ve optiksel özelliklerinin belirlenmesi

Production characterization and determination of optical properties of cobalt doped nickel oxide thin films for automotive glass application

  1. Tez No: 654574
  2. Yazar: MEHMET KOPAR
  3. Danışmanlar: PROF. DR. CENGİZ ÖNER, DR. TURAN GÜRGENÇ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Mühendislik Bilimleri, Engineering Sciences
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2020
  8. Dil: Türkçe
  9. Üniversite: Fırat Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Otomotiv Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 70

Özet

Bu çalışmada, ITO camlarının yüzeyleri farklı oranlarda kobalt (Co) katkılı nikel oksit (NiO) ince filmleri ile sol-jel döndürerek kaplama yöntemi kullanılarak kaplandı. ITO camlar ilk olarak 15*15 mm ölçülerinde kesildi. Kesilen camlar sırasıyla ethanol ve methanol banyosunda ultrasonik temizleyicide temizlendi. Daha sonra saf su ile durulama işlemi yapıldıktan sonra azot gazıyla kurutuldu. Camlar temizlendikten sonra saf ve Co katkılı NiO sol-jel solüsyonları ile döndürerek kaplama cihazıyla kaplandı. Kaplama işlemi 1000 d/dk da 30 saniye süreyle gerçekleştirildi. Kaplama işlemi bittikten sonra manyetik ısıtıcıda 15 dk süreyle 150 °C de buharlaştırma işlemi yapıldı. Yapılan bu işlemler her katman için ayrı ayrı uygulanarak ITO cam yüzeyleri 3 kat kaplandı. Kaplanan cam yüzeyler 600 °C de 2 saat süreyle tavlandı. Elde edilen numunelerin kaplanmış yüzey tabakalarının yapısal özelikleri X-ışını kırınımı (XRD), alan emisyonlu taramalı elektron mikroskobu (FE-SEM) ve enerji dağılımlı X-ışınları (EDX) ile analiz edildi. Optiksel özellikleri ultraviyole spektrometresi (UV-vis) yöntemi ile belirlendi. Yapılan deneysel çalışmalar sonucunda, Co katkı oranının artmasıyla X-ışını kırınım zirvelerinde değişimler gözlemlendi ve Co katkısına bağlı olarak ilave zirve noktaları gözlemlenmedi. Buna bağlı olarak Co katkısının NiO' in yapısına uygun olarak yerleştiği sonucuna varıldı. FE-SEM analizleri sonucunda tüm numunelerin kaplama tabakalarının nano boyutlu yapılardan oluştuğu tespit edilmiştir. UV-vis spektrometresi analizleri sonuçlarına göre Co katkı oranının artmasıyla soğurma, yansıtma ve geçirgenlik değerleri değişmiştir.

Özet (Çeviri)

In this study, the surfaces of ITO glasses were coated with different proportions of cobalt (Co) doped nickel oxide (NiO) thin films using sol-gel spin coating method. ITO glasses were first cut to the size of 15 * 15 mm. The cut glasses were cleaned with ethanol and methanol bath in an ultrasonic cleaner, respectively. Then, after rinsing with distilled water, it was dried with nitrogen gas. After the glasses were cleaned, they were coated with a spin coating device with pure and Co-doped NiO sol-gel solutions. The coatinsg was carried out at 1000 rpm for 30 seconds. After the coating process was finished, evaporation was carried out in a magnetic heater at 150 ° C for 15 minutes. These processes were applied separately for each layer and ITO glass surfaces were coated in 3 layers. The coated glass surfaces were annealed at 600 ° C for 2 hours. The structural properties of the coated surface layers of the obtained samples were analyzed by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM) and energy dispersive X-rays (EDX). Optical properties were determined by ultraviolet spectrometry (UV-vis) method. As a result of the experimental studies, changes in the X-ray diffraction peaks were observed with the increase in the Co doping ratio, and no additional peaks were observed due to the Co dopant. Accordingly, it was concluded that the Co contribution was placed in accordance with the structure of NiO. As a result of the FE-SEM analysis, it was determined that the coating layers of all samples consist of nano-sized structures. According to the results of UV-vis spectrometer analysis, the absorption, reflection and transmittance values changed with the increase of the Co doping ratio.

Benzer Tezler

  1. Thin film coatings with various materials and techniques for smart glass applications

    Akıllı cam uygulamaları için farklı malzemeler ve tekniklerle ince film kaplamalar

    AYŞE DİCEL

    Yüksek Lisans

    İngilizce

    İngilizce

    2021

    Bilim ve Teknolojiİstanbul Teknik Üniversitesi

    Nanobilim ve Nanomühendislik Ana Bilim Dalı

    PROF. DR. ESRA ZAYİM

  2. Development of intrinsic connection elements to join composite and metals components for automotive applications

    Otomotiv uygulamaları için kompozit-metal yapılarda intrinsik bağlantı arayüzü geliştirilmesi

    CAN ADALI

    Yüksek Lisans

    İngilizce

    İngilizce

    2018

    Makine MühendisliğiTürk-Alman Üniversitesi

    Malzeme Bilimi ve Makine Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. SELİM COŞKUN

    PROF. DR. MARKUS STOMMEL

  3. Machine learning based anomaly detection technique for in-vehicle networks

    Araç içi ağlar için makine öğrenmesi tabanlı anomali tespit tekniği

    ARİF AKAR

    Yüksek Lisans

    İngilizce

    İngilizce

    2017

    Bilgisayar Mühendisliği Bilimleri-Bilgisayar ve KontrolÇankaya Üniversitesi

    Elektronik ve Haberleşme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. KLAUS WERNER SCHMIDT

  4. Çeşitli sektörler uygulamaları için doğal kaynaklı malzemelerle ekonomik ve işlevsel kompozitlerin geliştirilmesi

    Development of economical and functional composites with naturally sourced materials for various industry applications

    NİLDA ÖZSOY

    Doktora

    Türkçe

    Türkçe

    2023

    Tekstil ve Tekstil MühendisliğiMarmara Üniversitesi

    Tekstil Mühendisliği Ana Bilim Dalı

    PROF. DR. ERHAN SANCAK

  5. The production of chopped glass fiber reinforced PPS composite via extrusion and injection moulding and characterization studies

    Kırpık cam elyaf takviyeli PPS matrisli kompozitin extrüzyon ve enjeksiyon ile üretimi ve karakterizasyon çalışmaları

    FEYZA ZENGİN

    Yüksek Lisans

    İngilizce

    İngilizce

    2020

    Polimer Bilim ve TeknolojisiMarmara Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. ARİF NİHAT GÜLLÜOĞLU

    DR. MEHMET MASUM TÜNÇAY