Geri Dön

Mechanical performance of lightweight fiber reinforced geopolymer mortar incorporating expanded clay at elevated temperatures

Yüksek sıcaklıklarda genişletilmiş kil içeren hafif elyaf takviyeli geopolimer harcının mekanik performansı

PDF İndir

  1. Tez No: 676286
  2. Yazar: MAYSAM ALI AMOORI ALJANABI
  3. Danışmanlar: PROF. DR. ABDULKADİR ÇEVİK, DOÇ. DR. DERYA BAKBAK
  4. Tez Türü: Yüksek Lisans
  5. Konular: İnşaat Mühendisliği, Civil Engineering
  6. Anahtar Kelimeler: Hafif Jeopolimer Harcın (HJH), Hafif Genleşmiş Kil Agrega (HGKA), PVA Lifler, Yüksek Sıcaklık, Mekanik Özellikler, Lightweight Geopolymer Mortar (LWGM), Lightweight Expanded Clay Aggregate (LECA), PVA Fibers, Elevated Temperatures, Mechanical Properties
  7. Yıl: 2021
  8. Dil: İngilizce
  9. Üniversite: Gaziantep Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 93

Özet

Bu çalışma, hafif genleşmiş kil agrega (HGKA) ve polivinil alkol (PVA) liflerinin hafif jeopolimer harcın (HJH) özellikleri üzerindeki etkisini incelemektedir. Sıcaklık seviyesinin (oda sıcaklığı, 250°C ve 500°C), lifli ve lifsiz JHJ'nin mekanik özellikleri üzerindeki etkisi araştırılmıştır. HGKA, %60 ve %80 oranları ile nehir kumunun kısmi ikamesi için kullanılmıştır. HGKA için kullanılan ana malzeme, sodyum silikat ve sodyum hidroksit çözeltilerinin bir karışımı ile aktive edilen cüruftur. Üç farklı karışım yapılmış ve normal oda koşullarında kürlenmiştir. İşlenebilirlik ve taze haldeki yoğunluk özellikleri ölçülmüştür. HGKA'nın lifli ve lifsiz mekanik özelliklerini değerlendirmek için basınç, eğilme ve tek eksenli çekme testleri gibi bir dizi deney yapılmıştır. Çalışmada, HGKA oranının arttırılmasının, HGKA'nın yoğunluğunda ve basınç dayanımında bir azalmaya yol açtığını bulunumuştur. Ayrıca, %1'lik bir PVA fiber oranının, HGKA'nın eğilme ve çekme davranışını önemli ölçüde iyileştirdiği görülmüştür. Deneysel sonuçlar, 500°C'lik yüksek sıcaklıklara maruz kalan numunelerin mekanik özelliklerinin belirgin şekilde değiştiğini göstermiştir.

Özet (Çeviri)

This study examines the impact of using lightweight expanded clay aggregate (LECA) and polyvinyle alcohol (PVA) fibers on the properties of lightweight geopolymer mortar. The effect of temperature level (room temperature, 250°C, and 500°C) on the mechanical properties of LWGM with and without fibers is also explored. LECA is used as a partial replacement to river sand with 60% and 80%. The base material utilized for LWGM is slag which was activated by a mixture of sodium silicate and sodium hydroxide solutions. Three different mixtures were prepared and cured at ambient temperature. The fresh properties in terms of workability and density were performed. A series of experiments, such as compression, flexural and uniaxial tensile tests were carried out to assess the mechanical properties of LWGM with and without fibers. The study found that increasing the level of LECA replacement leads to a decrease in the density and compressive strength of the LWGM. Furthermore, incorporating a 1% PVA fiber volume fraction improved the flexural, and tensile behavior of LWGM significantly. The experimental results indicated that the mechanical properties of tested samples subjected to the elevated temperatures of 500°C changed noticeably.

Benzer Tezler

  1. Tez No

    708700

    Mechanical performance of fiber-reinforced slag-based lightweight geopolymer mortar incorporating with expanded glass lightweight aggregate at elevated temperatures

    Genleştirilmiş cam hafif agrega ile üretilmiş elyaf takviyeli curuf esaslı hafif geopolimer harcının yüksek sıcaklık altındaki mekanik performansı

    AHMAD MOTEE AL MOHAMMAD

    Yüksek Lisans

    İngilizce

    İngilizce

    2021

    İnşaat MühendisliğiGaziantep Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. ABDULKADİR ÇEVİK

  2. Tez No

    802890

    Mechanical properties of normal and steel fibre-reinforced lightweight geopolymer concrete under chemical attack

    Kimyasal saldırı altında normal ve çelik fiber takviyeli hafif jeopolimer betonun mekanik özellikleri

    NIZAR BUSTANI

    Yüksek Lisans

    İngilizce

    İngilizce

    2023

    İnşaat MühendisliğiGaziantep Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. NİHAT ATMACA

  3. Tez No

    389271

    Hafif agrega içeren yalın ve PVA lif ile güçlendirilmiş yapısal betonların mekanik özelliklerinin incelenmesi

    Investigation of mechanical properties of conventional and structural semi-lightweight concretes reinforced with PVA fibers

    MURAT EMRE DİLLİ

    Yüksek Lisans

    Türkçe

    Türkçe

    2015

    İnşaat Mühendisliğiİstanbul Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. HAKAN NURİ ATAHAN

  4. Tez No

    610391

    Thermal and mechanical performance of cementitious PCM composites

    Çimentolu FDM kompozitlerinin ısıl ve mekanik performansları

    ERMAN YİĞİT TUNCEL

    Doktora

    İngilizce

    İngilizce

    2020

    İnşaat Mühendisliğiİstanbul Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. BEKİR YILMAZ PEKMEZCİ

  5. Tez No

    694950

    Mechanical behavior of additively manufactured polymer composite structures and interfaces

    Eklemeli imalat ile üretilen polimer kompozit yapıların ve arayüzeylerin mekanik özellikleri

    MEHMET KEPENEKCİ

    Yüksek Lisans

    İngilizce

    İngilizce

    2021

    Makine MühendisliğiOrta Doğu Teknik Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. SEZER ÖZERİNÇ

Geri Dön