Atmosferik basınçlı plazma ve geleneksel yüzey modifikasyon yöntemleri uygulanan CAD/CAM zirkonya blokların farklı rezin simanlarla bağlantı dayanımlarının değerlendirilmesi
Evaluation of bond strength of CAD/CAM zirconia blocks with different resin cements, using atmospheric pressure plasma and conventional surface modification methods
- Tez No: 692246
- Danışmanlar: DR. ÖĞR. ÜYESİ BEKİR EŞER
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: bağlantı dayanımı, CAD/CAM, lazer, monolitik zirkonya, plazma, rezin siman, bond strength, CAD/CAM, laser, monolithic zirconia, plasma, resin cement
- Yıl: 2021
- Dil: Türkçe
- Üniversite: Fırat Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: 154
Özet
Monolitik zirkonya restorasyonlara olan ilgi, CAD-CAM sistemlerinin de geliştirilmesiyle giderek artmıştır. Zirkonya restorasyonların uzun dönem klinik başarısı zirkonya ile rezin siman arasındaki adezyona bağlıdır. Bu tez çalışmasının amacı, zirkonya ile rezin siman arasındaki bağlantı gücünün arttırılmasına yönelik uygulanan atmosferik basınçlı plazma ve farklı yüzey modifikasyon yöntemlerinin zirkonyanın yüzey özelliklerine ve adeziv rezin siman sistemlerine bağlanma dayanımına etkisinin değerlendirilmesidir. Vita YZ HT monolitik zirkonya diskinden elde edilen 180 adet zirkonya örneğin yüzeyine kontrol, kumlama, lazer, plazma, primer, kumlama+primer, lazer+primer, plazma+primer, lazer+plazma+primer olmak üzere 9 farklı yüzey işlemi uygulanmıştır. Her gruptan 10ar örneğin yüzey pürüzlülüğü ve temas açısı değerleri ölçülmüş, her gruptan birer örneğe SEM-EDS ve AFM analizleri yapılmıştır. Örneklerin yarısına Rely X Ultimate Clicker adeziv rezin siman, diğer yarısına Theracem self-adeziv rezin siman uygulanmıştır. Örnekler 37ºC sıcaklıktaki distile suda 24 saat boyunca bekletilmiş, ardından makaslama bağlantı testine tabi tutulmuşlardır. Başarısızlık tipleri stereomikroskop ile incelenmiş, SEM görüntülemeleri yapılmıştır. Kumlama, primer, kumlama+primer, plazma+primer ve lazer+plazma+primer yüzey işlemlerinin Ra değerleri kontrol grubuna göre anlamlı derecede yüksektir. Kumlama, plazma ve lazer gruplarının temas açısı değerleri kontrol grubuna göre anlamlı derecede düşüktür. Theracem siman grubunda en yüksek makaslama bağlanma değeri kumlama+primer grubunda gözlenirken bunu sırasıyla plazma+primer ve lazer+plazma+primer grupları izlemiştir. Rely X Ultimate Clicker siman grubunda en yüksek makaslama bağlanma değeri lazer+plazma+primer grubunda gözlenirken bunu sırasıyla kumlama+primer, plazma+primer ve lazer+primer grupları izlemiştir. Her iki siman grubunda da yüzey işlemi sonrası primer uygulaması makaslama bağlanma değerlerini anlamlı bir şekilde yükseltmiştir. Atmosferik basınçlı plazma tek başına uygulandığında zirkonyanın ıslanabilirliğini anlamlı olarak arttırmıştır ancak primer ile kombine kullanıldığında makaslama bağlanma değerlerini kontrol grubuna göre anlamlı olarak arttırabilmiştir. Plazma+primer uygulaması öncesinde lazer uygulamasının anlamlı bir etkisi olmamıştır. Zirkonya-rezin siman bağlantı dayanımının arttırılmasında kumlama+primer ve plazma+primer uygulamaları etkin prosedürlerdir.
Özet (Çeviri)
Interest in monolithic zirconia restorations has increased with the development of CAD-CAM systems. The long-term clinical success of zirconia restorations depends on the adhesion between the zirconia and the resin cement. The aim of this thesis is to evaluate the effects of atmospheric pressure plasma and different surface modification methods applied to increase the bond strength between zirconia and resin cement on the surface properties of zirconia and bond strength to adhesive resin cement systems. 9 different surface treatments including control, sandblasting, laser, plasma, primer, sandblasting+primer, laser+primer, plasma+primer, laser+plasma+primer on the surface of 180 zirconia samples obtained from Vita YZ HT monolithic zirconia disc has been applied. Surface roughness and contact angle values of 10 samples from each group were measured, SEM-EDS and AFM analyzes were performed on one sample from each group. Rely X Ultimate Clicker adhesive resin cement was applied to half of the samples and Theracem self-adhesive resin cement was applied to the other half. The specimens were kept in distilled water at 37ºC for 24 hours and then subjected to the shear test. Failure types were examined with a stereomicroscope and SEM images were made. Ra values of sandblasting, primer, sandblasting+primer, plasma+primer and laser+plasma+primer surface treatments were significantly higher than the control group. The contact angle values of the sandblasting, plasma and laser groups were significantly lower than the control group. The highest shear bonding value was observed in the sandblasting+primer group in the Theracem cement group, followed by plasma+primer and laser+plasma+primer groups, respectively. In the Rely X Ultimate Clicker cement group, the highest shear bond value was observed in the laser+plasma+primer group, followed by the sandblasting+primer, plasma+primer and laser+primer groups, respectively. Primer application after surface treatment significantly increased the shear bond values in both cement groups. Atmospheric pressure plasma significantly increased the wettability of zirconia when applied alone, but when used in combination with primer, it could significantly increase the shear bond strength values compared to the control group. There was no significant effect of laser application before plasma+primer application. Sandblasting+primer and plasma+primer applications are effective procedures in increasing the zirconia-resin cement bond strength.
Benzer Tezler
- Plazma yüzey işleminin epoksi film yapıştırıcılı CFRP kompozit bağlantılarının performansına etkisinin incelenmesi
Investigation of the effect of plasma surface treatment on the performance of CFRP composite connections with epoxy film adhesive
AHMETCAN ALKOÇ
Doktora
Türkçe
2024
Metalurji MühendisliğiYıldız Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. AFİFE BİNNAZ HAZAR
- Investigation of gasification characteristics of Soma lignite by high pressure TGA
Soma linyitinin gazlaştırma özelliklerinin yüksek basınçlı TGA ile incelenmesi
GÖZDE KARDEŞ
Yüksek Lisans
İngilizce
2020
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. AHMET ALPER AYDIN
- Nanogözenekli zeolit malzemeye dayalı yeni gaz boşalma elektronik cihazının özellikleri
Pecularities of novel gas discharge electronic device based on nanoporous zeolite material
KIVILCIM KÖSEOĞLU
Doktora
Türkçe
2013
Fizik ve Fizik MühendisliğiGazi ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. BAHTİYAR SALAMOV
PROF. DR. SELİM ACAR
- Synthesis and characterization of hafnium boride-based ceramic powders
Hafniyum borür-esaslı seramik tozlarının sentezlenmesi ve karakterizasyonu
NAZLI AKÇAMLI
Doktora
İngilizce
2016
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. İSMAİL DUMAN
- Effects of dielectric barrier discharge cold plasma on the quality of dandelion root infusions
Dielektrik bariyer boşaltım soğuk plazmanın karahindiba kökü infüzyonlarının kalitesi üzerine etkisi
BERFİN EDA ELÇİK
Yüksek Lisans
İngilizce
2023
Gıda Mühendisliğiİstanbul Teknik ÜniversitesiGıda Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ CELALE KIRKIN GÖZÜKIRMIZI