The deformation rate sensitivities of additively and conventionally fabricated 316L alloys
Eklemeli ve geleneksel yöntemle üretilen 316L alaşımlarının deformasyon hızı hassasiyetleri
- Tez No: 705062
- Danışmanlar: PROF. DR. MUSTAFA GÜDEN
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Mühendislik Bilimleri, Savunma ve Savunma Teknolojileri, Mechanical Engineering, Engineering Sciences, Defense and Defense Technologies
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2021
- Dil: İngilizce
- Üniversite: İzmir Yüksek Teknoloji Enstitüsü
- Enstitü: Mühendislik ve Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 92
Özet
Seçici Lazer Ergitme yöntemi ile eklemeli olarak üretilmiş 316L (SLM-316L) ve ekstrüde edilmiş-tavlanmış ticari 316L (C-316L) alaşımlarının basma testi altındaki gerilim-gerinim davranışı, statik (1x10-3 s-1) ve dinamik (2500-3150 s-1) hızlar arasında belirlendi. SLM-316L, ikizlenme ve kayma yoluyla deforme olurken, C-316L martenzitik dönüşümle deforme olmuştur ve her iki alaşım da yaklaşık 0,51 gerinim değerine kadar kırılma olmadan deforme olmuşlardır. SLM-316L'nin C-316L'den daha yüksek akma dayanımı, SLM-316L'nin daha yüksek dislokasyon yoğunluğuna atfedilmiştir. C-316L alaşımının daha yüksek pekleşme (iş sertleşmesi) hızı, martenzit plakalarının, dislokasyon hareketine karşı, ikiz sınırlarına kıyasla, daha yüksek direnç göstermesine atfedilmiştir. Gerinim hızı arttıkça, her iki alaşımın akış gerilmelerinde artış görülmüştür. Ancak, yüksek gerinim hızlarında, gerinim arttıkça artan adyabatik ısınma nedeniyle gerinim hızı hassasiyetleri düşmüştür. Her iki alaşımın Johnson-Cook malzeme model parametreleri, adyabatik ve izotermal koşullar için ayrıca belirlenmiştir. C-316L numunelerindeki martenzit oluşumu ve SLM-316L numunelerindeki ikiz oluşumu statik gerinim hızlarına kıyasla yüksek gerinim hızlarında azalmıştır. C-316L'nin XRD spektrumları da yüksek gerinim hızlarında martenzit oluşumunun azaldığını doğrulamıştır. Yüksek gerinim hızlarında azalan ikizlenme ve martenzit oluşumu, test numunelerinin adyabatik ısınması nedeniyle artan istif bozukluğu enerjisine bağlanmıştır. Yüksek gerinim oranlarında istif bozukluğu enerjisinin artması, kayma ile deformasyonu teşvik etmiştir. Son olarak, yeniden yükleme testleri, SLM-316L'de bir gerinim hızı geçmişi etkisi ortaya koyarken C-316L'de bu etkinin olmadığını ortaya çıkarmıştır.
Özet (Çeviri)
The compression stress-strain behavior of a Scanning Laser Melt 316L (SLM-316L) and an annealed and extruded commercial 316L (C-316L) were determined between 1x10-3 s-1 and 2500-3150 s-1. SLM-316L deformed by twinning and slip, while C-316L by martensitic transformation and slip with no fracture until about 0.51 strain. The higher yield strength of SLM-316L than C-316L was attributed to the higher dislocation density of SLM-316L. The higher work hardening rate of C-316L alloy was proved due to the higher resistance of martensite plate than twin boundary to the dislocation motion. As the strain rate increased, both alloys showed increased flow stresses. However, the rate sensitivities declined as the strain increased due to the adiabatic heating at high strain rates. The Johnson and Cook flow stress material models of both alloys were further determined for the adiabatic and isothermal conditions. The martensite formation in C-316L specimens and twinning formation in SLM-316L alloys decreased at high strain rates compared to quasi-static strain rates. The XRD spectra of C-316L also confirmed the reduced martensite formation at high strain rates. The reduced twin and martensite formation at high strain rates were attributed to the increased stacking fault energy due to the adiabatic heating of the test specimens. The increase of stacking fault energy at high strain rates promoted a higher fraction of the deformation by slip. Lastly, the reloading tests revealed a strain-rate history effect in SLM-316L and no strain-rate history effect in C-316L.
Benzer Tezler
- The effect of strain rate on the deformation behavior of additively manufactured short carbon fiber reinforced polyamide composites
Gerinme hızının eklemeli imalat yöntemi ile üretilen kısa karbon fiber takviyeli polyamid kompozitlerin deformasyon davranışına etkisi
MEHMET KAAN ZEYBEK
Yüksek Lisans
İngilizce
2022
Makine Mühendisliğiİzmir Yüksek Teknoloji EnstitüsüMakine Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA GÜDEN
- AA5754 alüminyum alaşımının farklı sıcaklık ve gerinim hızlarının deformasyon davranışına olan etkilerinin incelenmesi
Investigation of the effect of various temperatures and strain rates on the deformation behaviour of AA5754 aluminum alloy
ÖMER İLHAN
Yüksek Lisans
Türkçe
2023
Makine MühendisliğiDüzce ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. NURİ ŞEN
- Mechanical behavior of nanotwinned materials-experimental and computational approaches
Başlık çevirisi yok
HAKAN YAVAŞ
- Yüksek devirli gemi diesel motorlarının analitik ve deneysel incelenmesi
An Analytical and exeperimental investigation of high speed marine diesel engines
OSMAN AZMİ ÖZSOYSAL
- Experimental investigation of convective drying of green bricks in a laboratory scale tunnel dryer
Laboratuvar ölçekli tünel kurutucuda yaş tuğlaların konveksiyonla kurutulmasının deneysel olarak incelenmesi
SELİN ÖZEN
Yüksek Lisans
İngilizce
2014
Kimya MühendisliğiMarmara ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. PERVİZ SAYAN
PROF. DR. SİBEL TİTİZ SARGUT