Evaltuation of shear bond strength of TWO highly translucent monolithic zirconia CAD/CAM materials to self adhesive resin cement after different surface pretreatment
Farkli yüzey işlemlerinin iki yüksek translusent monolitik zirkonya CAD/CAM malzemesinin self adeziv simanlarla bağlanma mukavemetine olan etkisinin değerlendirilmesi
- Tez No: 713607
- Danışmanlar: PROF. DR. NURAY ÇAPA YILDIRIM
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: kesme bağlanma dayanımı, CAD/CAM, monolitik zirkonya, self adeziv rezin siman, yüzey işlemi, Dental bonding, Dental çimentolar, Yüzey işleme tekniği, Yüzey pürüzlülüğü, Zirkonyum, Shear bond strength, CAD/CAM, monolithic zirconia, self-adhesive resin cement, surface treatment, fiber laser, Dental bonding, Dental cements, Surface handling technique, Surface roughness, Zirconium
- Yıl: 2022
- Dil: İngilizce
- Üniversite: Yeditepe Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Farklı yüzey işlemlerinin iki yüksek translusent monolitik zirkonya CAD/CAM malzemesinin self adeziv simanlarla bağlanma mukavemetine olan etkisinin değerlendirilmesi. Bu in vitro çalışmanın amacı; farklı yüzey işlemlerinin, self adeziv rezin simanın iki yüksek translüsent monolitik zirkonya CAD/CAM malzemesinin kesme mukavemeti üzerindeki etkisini değerlendirmektir. İki yüksek translusent monolitik CAD/CAM zirkonya markası değerlendirilmiştir: Zenostar Zr translusent (Wieland Dental; Pforzheim, Almanya) ve Ceramill zolid fx pre-shade (Amann Girrbach AG, Koblach, Avusturya). 152 adet disk şeklinde iki markanın monolitik zirkonya örnekleri, 5 eksenli CAD/CAM sistemi (VHF K5 Almanya) kullanılarak ön sinterlenmiş bloklarla hazırlanmıştır, daha sonra özel fırında gerekli nihai boyuta (10 mm çapında ve 3 mm yüksekliğinde) gelecek şekilde sinterlenmiştir. 140 örnek Yüzey işlemlerine göre yedi gruba ayrılmıştır: yüzey işlemi yok (kontrol), %9.5 HF asit ile aşındırma, 50 μm Al2O3 ile kumlama, 50 μm Al2O3 ile kumlama +Z Prime Plus, Cojet, Siljet ve fiber lazer. Üreticilerin önerilerine göre, kompozit rezin silindirleri, RelyX U200 self adeziv rezin siman ile zirkonya disklere yapıştırılmıştır. Bütün örnekler termosiklusa (5C/55C'de 5000 siklus) maruz bırakılmıştır. 12 örneğin yüzey pürüzlülüğü SEM kullanılarak değerlendirilmiştir. Üniversal test makinesi kullanılarak kesme bağlanma mukavemeti test edilmiştir. Bağlanmadaki kopma tipleri SEM ve Steromikroskop kullanılarak incelenmiştir. Veriler, iki yönlü ANOVA ve post hoc Tukey çoklu karşılaştırma testi kullanılarak istatistiksel olarak analiz edilmiştir. Bağlanma dayanımı, iki farklı yüksek translusent zirkonya CAD/CAM materyali arasında istatistiksel olarak anlamlı bir farklılık göstermemiştir (p:0.055; p>0.05). Bağlanma dayanımı, yüzey işleminden önemli ölçüde etkilenmiştir (p:0.000; p<0.05). Zenostar için en yüksek kesme bağlanma kuvveti fiber lazerde bildirilmiştir (17,81±2MPa). Ceramill için en yüksek kesme bağlanma kuvveti fiber lazerde bildirilmiştir (21,7±3,55 MPa). Her iki monolitik zirkonya grubu için tribokimyasal silika kaplamanın (Cojet, Siljet) ve 50 μm Al2O3 ile kumlama + Z Prime Plus uygulamasının bağlanma gücüne etkisinde istatistiksel olarak anlamlı bir fark bulunmamıştır. En baskın kopma tipi, fiber lazer gruplarında kohezivdi ve Cojet, Siljet ve kumlama+Z Prime Plus gruplarında ise karışık (adeziv ve koheziv) tip oldu. HF asit yüzey işlemi 1 saat uygulandığında monolitik zirkonyanın bağlanması için etkili bir yüzey işlemi olmamıştır. Kumlama+Z Prime Plus, Cojet ve Siljet monolitik zirkonya için mevcut en iyi simantasyon protokolüdür. İki monolitik zirkonya CAD/CAM bloğu için fiber lazerle yapılan yüzey işlemi bağlanma dayanımını artırmıştır ancak zirkonyanın renk değiştirmesine neden olmuştur. Fiber laserin yüksek taranlusent monolilik zirkonyada zarar vermeden bağlanmayı artırmak için daha fazla araştırmaya ihtiyaç vardır.
Özet (Çeviri)
Evaluation of shear bond strength of two highly translucent monolithic zirconia CAD/CAM materials to self-adhesive resin cement after different surface pretreatment In-vitro study aimed to assess the effect of different surface treatments on the shear bond strength of self-adhesive resin cement to highly translucent monolithic zirconia-based CAD/CAM materials. 2 brands of highly translucent monolithic CAD/CAM zirconia were evaluated: Zenostar Zr translucent (Wieland Dental; Pforzheim, Germany) and Ceramill zolid fx preshade (Amann Girrbach AG, Koblach, Austria). 152 disc shaped monolithic zirconia sample of two brands were used and prepared from pre-sintered blocks using 5 axis CAD/CAM system (VHF K5 Germany) and then sintered to the final required dimension (10 mm in diameter and 3 mm in height) in a special high-temperature furnace. After those 140 discs were divided into seven groups according to the surface treatment received: no treatment (control), 9.5% HF acid etching, airblasting with 50 μm Al2O3, airblasting with 50 μm Al2O3 + Z Prime Plus, Cojet, Siljet, fiber laser. Composite resin cylinders were bonded to zirconia disc with RelyX U200 self-adhesive resin cement according to manufacturer's instructions. All specimens were thermocycled (5000 cycles at 5oC/55oC). 12 samples were used for surface roughness evaluation using SEM. A shear bond test was performed using the universal testing machine. Failure modes were examined using stereomicroscope and SEM. Data were analyzed statistically by using two-way ANOVA and post hoc Tukey's multiple comparison test. The bond strength was not statistically significantly different between two highly translucent zirconia CAD/CAM materials (p:0.055; p>0.05). The bond strength was significantly affected by the surface treatment (p:0.000; p<0.05). The highest shear bond strength for Zenostar was reported as fiber laser (17,81±2 MPa). The highest shear bond strength for Ceramill was reported as fiber laser (21,7±3,55 MPa). There was no statistically significant difference between bond strength of Tribochemical silica coating (Cojet, Siljet) and air blasting plus Z Prime Plus for both monolithic zirconia groups. The predominant failure mode was cohesive failure for fiber laser groups and mixed failure for Cojet, Siljet, and blasting+ Z Prime Plus groups. HF acid surface treatment for one hour is not effective for bond of monolithic zirconia. Cojet, Siljet, and alumina blasting with Z Prime Plus is the best available cementation protocol for highly translucent monolithic zirconia. Fiber laser enhanced shear bond strength of two highly translucent monolithic zirconia CAD/CAM blocks, however it led to discoloration of zirconia. Fiber laser as surface treatment needs more research for optimization their effect to increase bond strength without damage to highly translucent monolithic zirconia.
Benzer Tezler
- Farklı fiberlerle güçlendirilmiş kompozit rezinin mine ve dentine bağlanma dayanımının makaslama testi metoduyla değerlendirilmesi ve taramalı elektron mikroskobu (SEM) ile incelenmesi
Evaluation of bond strengths of different fiber reinforced composites to enamel and dentine with shear bond test method and scannig electron microscopy (SEM) observations
NURCAN ÖZAKAR İLDAY
Doktora
Türkçe
2010
Diş HekimliğiAtatürk ÜniversitesiDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
PROF. DR. NİLGÜN SEVEN
- Farklı yüzey işlemleri uygulanan 3 tip rezin matriks seramiğin bir rezin simana bağlanma dayanımının incelenmesi
Evaluation of bond strength of a resin cement to 3 types of resin-matrix ceramics with different surface treatments
MEHMET EFE KONUKOĞLU
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiAnkara Yıldırım Beyazıt ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. FİLİZ AYKENT
- A new approach in studying the engineering behavior and mechanical properties of artificial bonded soils in the laboratory
Bağlı yapay zeminlerin mühendislik ve mekanik özelliklerinin laboratuvarda incelenmesine yönelik yeni bir yaklaşım
RICHARD VALL NGANGU RICARDO
Doktora
İngilizce
2022
İnşaat Mühendisliğiİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. MUSAFFA AYŞEN LAV
- Seramik birleştirme teknolojisi ve yapısal seramiklerin lehimlenmesi
Ceramic foining technology and brazing of structural ceramics
OSMAN AKKOCA
- Evaluation of shear bond strength and adhesive remnant index of two orthodontic color change adhesives systems on bonding of metal brackets
Metal braketlerin yapıştırılmasında iki ortodontik renk değiştiren adeziv sisteminin kesme bağlanma kuvveti ve artık adeziv endeksinin değerlendirilmesi
MUAYAD MUQDAD GHAIDAN ALBAYATI
Yüksek Lisans
İngilizce
2021
Diş HekimliğiAltınbaş ÜniversitesiOrtodonti Ana Bilim Dalı
PROF. DR. SABRİ İLHAN RAMOĞLU